Copyright of Journal of Natural Fibers is the property of Taylor & Francis Ltd and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)

In this work, thermal stability, flame retardance and smoke suppression characteristic of kenaf (KF) and oil palm empty fruit bunch (EFB) filled composites were studied. Polylactic acid (PLA), polystyrene (PS) and liquid epoxy were used as the matrices. Aluminum trihydrate (ATH) flame retardant (FR) ranging from 5 - 15% was incorporated into the composites to investigate the effects of ATH concentration on flammability and smoke intensity. The thermoplastic composites were prepared through solvent dissolution followed by compression molding. The thermoset composite was produced using a vacuum press machine. Vertical Bunsen burner test, Ringelmann smoke chart, thermogravimetric analysis (TGA), scanning electron microscopy (SEM) and tensile test were performed to investigate the flame retardancy, smoke suppression properties, thermal stability, morphology and mechanical properties of the composites. The results show that incorporation of ATH can greatly increase the flame retardance and smoke suppression of the materials. Their mechanisms were discussed. SEM micrographs of post combustion ATH incorporated samples revealed that the morphology of char residue consisted of numerous pores in the polymer bulk. These porous-like structures have shown to be beneficial in retarding flame. [ABSTRACT FROM AUTHOR]

Cellulose nanocrystals (CNCs) from kenaf core were prepared using acid hydrolysis method while graphene oxide (GO) were synthesized from modified Hummer's method. Low filler content composites films of CNC (0.1 - 0.4 wt.%) and GO (0.1 - 0.6 wt.%) in PLA films were prepared separately using solution casting method. From tensile test, it was found that optimum modulus increment were obtained for 0.2 wt.% CNCs and 0.4 wt.% GO in PLA which gave an increment of 125% and 40%, respectively. Only a small amount of CNCs are needed to improve the tensile properties of PLA. From microscopic observation of fractured surface at higher filler contents, CNC agglomerates tend to form which serves as void nucleating agent during plastic deformation due to poor interfacial properties while GO agglomerates cannot be observed in composites. Improved mechanical properties were not due to increment of crystallinity in PLA but reinforcement from fillers. [ABSTRACT FROM AUTHOR]