We considered the possibility of reducing industrial waste by fabricating and reusing dental models prepared using a fused deposition modeling (FDM) 3D printer and polylactic acid (PLA) filaments. The purpose of this study was to verify the accuracy of models fabricated using FDM and PLA.The same provisional crown was used to check the marginal fit on PLA models prepared using an intraoral scanner (IOS) and FDM, plaster models made with silicone impression material and plaster, and resin models prepared using an IOS and stereolithography apparatus (SLA) 3D printer. The marginal fit was measured using micro-computed tomography at four points on the tooth: the buccal center (B), palatal center (P), mesial center (M), and distal center (D) points.At point B, the marginal gaps were 118 ± 21.7, 62 ± 16.4, and 50 ± 26.5 μm for the PLA, resin, and plaster models, respectively, with a significant difference between the PLA model and the other two. However, the marginal gap at all other measurement points was not significantly different between the models (P0.05).We compared the accuracy of the models fabricated using the FDM, SLA, and conventional methods. The combination of FDM and PLA filaments showed no significant differences from the other models, except at point B, indicating its usefulness. Therefore, FDM and PLA may become necessary materials for dental treatment in the future.

In this study, we evaluated the characteristics of five commercial resin composites used for provisional restorations. The inorganic filler contents of the resins were measured, and three-point bending, wear, surface hardness, water absorption, and staining tests were performed. The specimens underwent additional three-point bending tests after water storage and undergoing thermal stresses at 5°C and 55°C (10,000 cycles). Data were analyzed using one- or two-way analysis of variance and Bonferroni post-hoc tests. Pearson's correlation coefficient was used for pairwise comparisons. Each resin composite presented with different mechanical properties, based on variations in the inorganic filler content. The flexural strength of each resin composite was significantly decreased after water storage. There has a positive correlation between flexural strength and dynamic hardness but a negative correlation between flexural strength and maximum wear depth. The types and contents of the inorganic fillers, the composition of the monomer in the resin matrix, and the addition of plasticizers can affect the properties of the material.

Computer-aided design and manufacturing (CAD/CAM) resin-produced restorations were approved by a health insurance system in Japan from the year 2014. In this study, we investigated the use of CAD/CAM resin blocks in Japan since 2014, and the clinical use of adhesive systems for CAD/CAM resin-produced restorations in dentistry. Our findings indicated a rise in the clinical application of these products; however, some studies have reported instances of debonding and fracture of the restorations. CAD/CAM resin blocks were implemented in the health insurance system in Japan as an alternative for alloys due to the continuous rise in the prices of gold and palladium. Thus, in order to reduce the number of failures in CAD/CAM resin-produced restorations due to debonding and fracture, the integration of these restorations with the tooth structures is of utmost importance.

This study aimed to investigate how different compositions of experimental silane-based primers in a methyl methacrylate solution containing 3-(trimethoxysilyl)propyl methacrylate (3-TMSPMA) or 3-(4-methacryloyloxyphenyl)propyl trimethoxysilane (3-MPPTS) might act as silicon dioxide bonding agents. With or without post-silanization heat treatment, primer-treated quartz discs were bonded using the MMA-TBB resin and their bond strengths were evaluated. The disks were primed with one of the following materials: 1 mol% 3-TMSPMA, 2 mol% 3-TMSPMA, 1 mol% 3-MPPTS, and 2 mol% 3-MPPTS. Shear bond strength was determined both before and after thermocycling. Statistical analyses were performed with non-parametric procedure (Kruskal-Wallis, Mann-Whitney U, and Steel-Dwass tests). Both primers were effective with heat treatment to enhance bonding between quartz and the MMA-TBB, and the bonding durability of the 1 and 2 mol% 3-MPPTS (16.8 and 24.9 MPa) with heat groups was significantly higher than in the 1 and 2 mol% 3-TMSPMA (5.4 and 9.8 MPa) with heat groups.

The resin-coating technique is one of the successful bonding techniques used for the indirect restorations. The dentin surfaces exposed after cavity preparation are coated with a thin film of a coating material or a dentin bonding system combined with a flowable composite resin. Resin coating can minimize pulp irritation and improve the bond strength between a resin cement and tooth structures. The technique can also be applied to endodontically treated teeth, resulting in prevention of coronal leakage of the restorations. Application of a resin coating to root surface provides the additional benefit of preventing root caries in elderly patients. Therefore, the coating materials have the potential to reinforce sound tooth ("Super Tooth" formation), leading to preservation of maximum tooth structures.

We used a polymicrobial (PM) biofilm model to examine associations of bacterial adhesiveness with surface characteristics of various dental materials. Four types of dental materials (apatite pellet, zirconia, ceramic, and composite resin) with rough and mirror surfaces were used. Surface roughness, surface free energy, zeta potential, and colony-forming units (CFUs) of the biofilm formations were measured. Biofilms were cultured for 24 h under anaerobic conditions, plated onto blood agar medium, and anaerobically cultured for 4 days. After culturing, CFU per mm2 was calculated, and samples were observed under a scanning electron microscope. Means and standard deviations of the experimental data were estimated, and one-way ANOVA and Tukey multiple comparison assays were performed. Pearson correlation coefficients were obtained for the CFU and surface characteristics. Surface roughness and surface free energy appeared to affect generation of PM biofilms on oral materials, and zeta potential was involved in generation of PM biofilms on mirror-ground oral materials.

The demand for titanium and titanium alloys in dentistry is high. A surveillance survey regarding the clinical and laboratory uses of titanium/titanium alloys in Japan was conducted in this study. The alloys used for casting demonstrated a decreasing tendency in quantity, whereas the use of non-casting titanium alloys increase in the market. This increasing trend is reflected the popularity of CAD/CAM devices. In Japan, the processing technologies of titanium alloys have been improved; therefore, the application of titanium and titanium alloys to dental procedures covered by the insurance is clearly worth considering.

This study investigated the in vitro anti-demineralization effects of resin-based temporary filling materials containing surface prereacted glass-ionomer (S-PRG) filler on dentin. Bovine root dentin specimens with a 3×3 mm experimental surface were divided into four treatment groups: DuraSeal (DU) as a control, S-PRG filler-free temporary material (S0), material containing 10% (S10) and 20% (S20) S-PRG filler. Each material was applied to 3×2 mm of the experimental surface, and the specimens were immersed in 8% methylcellulose gel demineralization system for one week at 37˚C. Mineral profiles and integrated mineral loss (IML) of lesions induced on the surface (3×1 mm) adjacent to the materials were computed by transversal microradiography. S10 and S20 yielded thick surface layers and shallow lesion bodies, with significantly lower IML than DU and S0 (p

This study aimed to investigate how different compositions of experimental silane-based primers in a methyl methacrylate solution containing 3-(trimethoxysilyl)propyl methacrylate (3-TMSPMA) or 3-(4-methacryloyloxyphenyl)propyl trimethoxysilane (3-MPPTS) might act as silicon dioxide bonding agents. With or without post-silanization heat treatment, primer-treated quartz discs were bonded using the MMA-TBB resin and their bond strengths were evaluated. The disks were primed with one of the following materials: 1 mol% 3-TMSPMA, 2 mol% 3-TMSPMA, 1 mol% 3-MPPTS, and 2 mol% 3-MPPTS. Shear bond strength was determined both before and after thermocycling. Statistical analyses were performed with non-parametric procedure (Kruskal-Wallis, Mann-Whitney U, and Steel-Dwass tests). Both primers were effective with heat treatment to enhance bonding between quartz and the MMA-TBB, and the bonding durability of the 1 and 2 mol% 3-MPPTS (16.8 and 24.9 MPa) with heat groups was significantly higher than in the 1 and 2 mol% 3-TMSPMA (5.4 and 9.8 MPa) with heat groups.

Silane coupling agents alter the properties of material surfaces, which are modified by means of an organic functional group of specific silanes. This review describes the use of hydrophobic silane compounds for surface modification of silica-based and other materials. (J Oral Sci 58, 151-155, 2016).

The aims of this study were to evaluate a new restorative method using a carbon dioxide laser (CO(2)-laser) and to evaluate the acid resistance of teeth. Experimental calcium phosphate glass (CPG) powder and two low melting point ceramics (Finesse and zirconium silicate) were fused to enamel surfaces using a CO(2)-laser at an irradiation intensity of 1.0 watt for 30 seconds with a beam size of 0.49 mm at the focal point. The treated teeth were observed with a scanning electron microscope, and the acid resistance of the treated enamel surfaces was evaluated. The CPG fused successfully to the enamel surface, and the treated enamel surface showed high acid resistance compared with the low melting point ceramics and the non-irradiated surfaces. This system may lead to the development of new restorative methods that do not require the use of bonding agents.

This paper evaluated the wear resistance of resin composite materials with fillers which were modified with a novel hydrophobic silane coupling agent. The novel silane coupling agent containing hydrophobic phenyl group 3-(3-methoxy-4-methacryloyloxyphenyl)propyltrimethoxysilane (p-MBS) was synthesized. The experimental light-cure hybrid composites containing 85wt% of filler modified with this silane were formulated. Twelve specimens were prepared for the three-body-wear test with the ACTA machine and the collected data were analyzed statistically using a one-way ANOVA and Tukey's multiple comparison test as the post hoc test. The wear of the composites containing fillers treated with p-MBS was significantly lower compared with the composite materials containing fillers pretreated with 3-methacryloyloxypropyltrimethoxysilane or the commercially composites (AP-X and ELS extra low shrinkage) after a wear test for 200,000 cycles (p

The purpose of this study was to evaluate the antibacterial activity against polymicrobial (PM) biofilms of a condensed tannin extracted from astringent persimmon (PS-M), which is contained in refreshing beverages commercially available in Japan. Salivary PM biofilms were formed anaerobically on glass coverslips for 24 and 72 h and were treated for 5 min with sterilized deionized water (DW), 0.05 and 0.2 wt% chlorhexidine digluconate (CHX), and 0.5–4.0 wt% PS-M solution. The colony forming units (CFU/mL) were determined and morphological changes of the biofilms were observed by scanning electron microscopy (SEM). The CFUs were lower in all PS-M and CHX groups compared to the DW group. PS-M exerted a dose-dependent effect. PS-M (1.53 × 107) at a dose of 4.0 wt% had the same effect as 0.2 wt% CHX (2.03 × 107), regardless of the culture period. SEM revealed the biofilm structures were considerably destroyed in the 4.0 wt% PS-M and 0.2 wt% CHX. These findings indicate that the antibacterial effects of PS-M, a naturally derived substance, are comparable to those of CHX. PS-M may keep the oral cavity clean and prevent dental caries and periodontal disease related to dental plaque, as well as systemic disease such as aspiration pneumonitis.

A fluoride-releasing coating material containing surface pre-reacted glass-ionomer (S-PRG) filler has become commercially available. However, there has been no detailed investigation of its remineralization effects at various tooth surface regions. The remineralization effects of S-PRG filler-containing coating material at different sites of demineralized dentin surfaces in vitro were evaluated.Baseline lesions were prepared on bovine root dentin surfaces by immersion in demineralization buffer and divided into four groups: (B)--baseline lesion; (P)--S-PRG filler-containing material; (V)--S-PRG filler-free coating material as negative control; and (X)--resin-modified glass- ionomer as positive control. Material was applied to half the lesion surface, then P, V and X were remineralized in a gel system. Mineral profiles, integrated mineral loss (IML) and lesion depth (LD) at four regions, i.e. 1--exposed dentin surface adjacent to the material; 2--at a distance from the material; 3--beneath the material near to the edge; and 4--at a distance from the edge, were analyzed by transversal microradiography. Data were analyzed using ANOVA and Games-Howell test with α = 0.05.B showed typical artificial demineralized lesion. The IMLs of V, P and X at regions 1 and 2, and P and X at region 3 were significantly lower than that of B, however, those of V at region 3 and the other three groups at region 4 were not significantly different from that of B. At region 1, P and X showed significantly lower IMLs than V. At region 2, the IML of X showed significantly lower IML than V. There was no significant difference between P and X. The LD values of V, P and X at all regions were not significantly different from that of B. Fluoride, strontium and silicate ions released from the S-PRG filler would provide a favorable environment for remineralization of the demineralized dentin in P.

The hydrolytic stability of a group of experimental composite materials was evaluated. Seven distinct composites were formed by the mixing of a resin monomer mixture with silica filler that had been pre-treated with one of 7 different ethanol solutions. In one case, the filler was treated with an ethanol solution that contained only 3-methacryloyloxypropyltrimethoxysilane. In 5 cases, it was treated with solution containing a mixture of 3-methacryloyloxypropyltrimethoxysilane and one of the following hydrophobic fluoroalkyltrimethoxysilanes: trifluoropropyl-, nonafluorohexyl-, tridecafluorooctyl-, heptadecafluorodecyl-, and henicosafluorododecyl-trimethoxysilane. The tensile strength, after being immersed in water for 1800 days, of 2 of the experimental composites, whose pre-treatment regimen had included a fluoroalkyltrimethoxysilane, was significantly higher than that of the composite whose pre-treatment regimen had not included a fluoroalkyltrimethoxysilane. Moreover, there was no significant difference between the tensile strength of fresh samples of these 2 composites and the tensile strength of identically produced samples that had remained under water for 1800 days or that had been subjected to 30,000 cycles of thermal stress.

Three novel aqueous fluoride surfactants (F4, F6, and F8) and a positive control (10F2S-3I) were applied to bovine enamel and the surface free energy was calculated by measuring the surface contact angles of three liquids: distilled water, α-bromonaphthalene and diiodomethane. The specimens were stored in water for 90 days, and then immersed in acetic acid/sodium acetate. The modified specimens recorded higher contact angles and lower surface free energy immediately after treatment than the control (p

Six silane coupling agents having amide group (biosilanes) were synthesized with the aim to construct the material surface that allows cells to be compatible with it without their destruction. These agents were expected to make a soft landing to cytoplasm through the hydrogen bonding between their amide groups and cells. Evaluations of cell affinity using glass substrates modified with the synthesized biosilanes revealed that many cells remain on the modified glass plate. In addition, the implantation into the body of immunodeficient mouse of a composite material composed of porous hydroxyapatite and osteoblast showed the formation of a bone-like structure.