Search

Warhead power assessment of the anti-ship missile plays a vital role in determining the optimal design of missile, thus having important strategic research significance. However, in the assessment process, expert’s judgement will directly affect the assessment accuracy. In addition, there are many criteria involved in the missile design alternatives. Some criteria with poor performance may be compensated by other criteria with excellent performance, and then it is impossible to find the truly optimal alternative. Aimed at solving these problems, this paper proposes a synthetical assessment process based on fuzzy hesitant linguistic term set and the Gained and Lost Dominance Score (GLDS) method. In order to improve the assessment accuracy of experts and solve the problem that experts generate different opinions, combined with the advantages of fuzzy hesitant sets and linguistic term sets, the double hierarchy hesitant fuzzy linguistic term sets are used in this paper to improve the accuracy of expert’s judgement. In order to effectively combine expert’s experience with the data of criteria, the evidence theory and entropy weight method are used to transfer the expert’s judgement to the weight. In order to avoid selecting defective alternative of missile design, the GLDS is used to fuse expert information and criteria information. Sensitivity analysis shows that the assessment process has sensitivity to some extent. However, when the fluctuation of expert’s assessment makes the fluctuation of θ in the range of −5% to 5%, the impact on the results is not quite conspicuous. The analysis of calculation result and comparative analysis show that the assessment process proposed in this paper is accurate enough, has great advantage in selecting the current and potential optimal alternative of missile design, and avoids the alternatives with low criteria performance that cannot be compensated by other criteria being selected.

The atomic scale local structures affect the initiation performance of ultra-fine explosives according to the stimulation results of hot spot formation. However, the experimental characterization of local structures in ultra-fine explosives has been rarely reported, due to the difficulty in application of characterization methods having both high resolution in and small damage to unstable organic explosive materials. In this work, X-ray total scattering was explored to investigate the atomic scale local distortion of two widely applicable ultra-fine explosives, LLM-105 and HNS. The experimental spectra of atomic pair distribution function (PDF) derived from scattering results were fitted by assuming rigid ring structures in molecules. The effects of grain refinement and thermal aging on the atomic scale local structure were investigated, and the changes in both the length of covalent bonds have been identified. Results indicate that by decreasing the particle size of LLM-105 and HNS from hundreds of microns to hundreds of nanometers, the crystal structures remain, whereas the molecular configuration slightly changes and the degree of structural disorder increases. For example, the average length of covalent bonds in LLM-105 reduces from 1.25 Å to 1.15 Å, whereas that in HNS increases from 1.25 Å to 1.30 Å, which is possibly related to the incomplete crystallization process and internal stress. After thermal aging of ultra-fine LLM-105 and HNS, the degree of structural disorder decreases, and the distortion in molecules formed in the synthesis process gradually healed. The average length of covalent bonds in LLM-105 increases from 1.15 Å to 1.27 Å, whereas that in HNS reduces from 1.30 Å to 1.20 Å. The possible reason is that the atomic vibration in the molecule intensifies during the heat aging treatment, and the internal stress was released through changes in molecular configuration, and thus the atomic scale distortion gradually heals. The characterization method and findings in local structures obtained in this work may pave the path to deeply understand the relationship between the defects and performance of ultra-fine explosives.

In order to improve the safety of hexanitrohexaazaisowurtzitane (CL-20), submicron CL-20 particles were prepared by a siphon ultrasonic-assisted spray refining experimental device. The samples were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD), and differential scanning calorimetry (DSC), and the impact sensitivity of the samples was tested. The results show that the particle size of siphon-refined CL-20 is about 800 nm~1 μm, which is more smooth, mellow, and dense than that of CL-20 prepared by a traditional pressure-refined method. The peak diffraction angle of pressure- and siphon-refined CL-20 is basically the same as that of raw CL-20, and their crystal forms are ε type. The peak strength of pressure- and siphon-refined CL-20 decreased obviously. The apparent activation energy of pressure-refined CL-20 and siphon-refined CL-20 is 13.3 kJ/mol and 11.95 kJ/mol higher than that of raw CL-20, respectively. The thermal stability of CL-20 is improved. The activation enthalpy (ΔH#) is significantly higher than that of raw CL-20, and the characteristic drop is 70.4% and 82.7% higher than that of raw CL-20. The impact sensitivity of siphon-refined CL-20 is lower than that of pressure-refined CL-20, so the safety performance of an explosive is improved obviously.