Calcium sulfate powder materials containing terbium ions at 0, 1.0, or 2.0 mol.% were obtained. They are characterized by the presence of a CaSO4 × 0.5H2O phase, while Tb3+ is incorporated into the lattice at ≤1.0 mol.%. Specific surface area enlarged from 2.1 to 22.5 m2/g as crystallite size decreased from 68 to 31 nm. Thermal analysis showed that terbium slightly raises the temperature of CaSO4 × 2H2O-to-CaSO4 transition. Studies of solubility in SBF solution showed the presence of a calcium phosphate layer in terbium-containing cements on the 7th day. Luminescent properties were studied by excitation at 266 nm and 489 nm corresponding to absorption bands of the host and Tb3+ (7F6 - 5D4 absorption band). The recorded emission peaks of the materials showed that the luminescence of the samples was green, with the luminescence intensity increasing when Tb3+ was introduced. The developed materials can find applications in medicine as bioimplants with a possibility of noninvasive visualization of the bone restoration process.

Mesoporous hydroxyapatite (HA) materials demonstrate advantages as catalysts and as support systems for catalysis, as adsorbent materials for removing contamination from soil and water, and as nanocarriers of functional agents for bone-related therapies. The present research demonstrates the possibility of the enlargement of the Brunauer–Emmett–Teller specific surface area (SSA), pore volume, and average pore diameter via changing the synthesis medium and ripening the material in the mother solution after the precipitation processes have been completed. HA powders were investigated via chemical analysis, X-ray diffraction analysis, Fourier-transform IR spectroscopy, transmission electron microscopy (TEM), and scanning (SEM) electron microscopy. Their SSA, pore volume, and pore-size distributions were determined via low-temperature nitrogen adsorption measurements, the zeta potential was established, and electron paramagnetic resonance (EPR) spectroscopy was performed. When the materials were synthesized in water–ethanol and water–acetone media, the SSA and total pore volume were 52.1 m2g−1 and 116.4 m2g−1, and 0.231 and 0.286 cm3g−1, respectively. After ripening for 21 days, the particle morphology changed, the length/width aspect ratio decreased, and looser and smaller powder agglomerates were obtained. These changes in their characteristics led to an increase in SSA for the water and water–ethanol samples, while pore volume demonstrated a multiplied increase for all samples, reaching 0.593 cm3g−1 for the water–acetone sample.