Search

The thesis is divided in three chapters, each one covering one topic. Initially, the thermo-mechanical and impact properties of materials used for back protectors have been analysed. Dynamical mechanical analysis (DMTA) has shown that materials used for soft-shell protectors present frequency-sensitive properties. Furthermore, through impact tests, the shock absorbing characteristics of the materials have been investigated proving the differences between soft and hard-shell protectors; moreover it has been demonstrated that the materials used for soft-shell protectors maintain their protective properties after multi-impacts. The second chapter covers the effect of the visco-elastic properties of the thermoplastic polymers on the flexural and rebound behaviours of ski boots. DMTA analysis on the materials and flexural and rebound testing on the boots have been performed. A comparison of the results highlighted a correlation between the visco-elastic properties and the flexural and rebound behaviour of ski boots. The same experimental methods have been used to investigate the influence of the design on the flexural and rebound behaviours. Finally in the third chapter the thermoplastic materials employed for the construction of ski boots soles have been characterized in terms of chemical composition, hardness, crystallinity, surface roughness and coefficient of friction (COF). The results showed a relation between material hardness and grip, in particular softer materials provide more grip with respect to harder materials. On the contrary, the surface roughness has a negative effect on friction because of the decrease in contact area. The measure of grip on inclined wet surfaces showed again a relation between hardness and grip. The performance ranking of the different materials has been the same for the COF and for the slip angle tests, indicating that COF can be used as a parameter for the choice of the optimal material to be used for the soles of ski boots.

Environmental decay in porous masonry materials, such as brick and mortar, is a widespread problem concerning both new and historic masonry structures. The decay mechanisms are quite complex dependng upon several interconnected parameters and from the interaction with the specific micro-climate. Materials undergo aesthetical and substantial changes in character but while many studies have been carried out, the mechanical aspect has been largely understudied while it bears true importance from the structural viewpoint. A quantitative assessment of the masonry material degradation and how it affects the load-bearing capacity of masonry structures appears missing. The research work carried out, limiting the attention to brick masonry addresses this issue through an experimental laboratory approach via different integrated testing procedures, both non-destructive and mechanical, together with monitoring methods. Attention was focused on transport of moisture and salts and on the damaging effects caused by the crystallization of two different salts, sodium chloride and sodium sulphate. Many series of masonry specimens, very different in size and purposes were used to track the damage process since its beginning and to monitor its evolution over a number of years Athe same time suitable testing techniques, non-destructive, mini-invasive, analytical, of monitoring, were validated for these purposes. The specimens were exposed to different aggressive agents (in terms of type of salt, of brine concentration, of artificial vs. open-air natural ageing, …), tested by different means (qualitative vs. quantitative, non destructive vs. mechanical testing, punctual vs. wide areas, …), and had different size (1-, 2-, 3-header thick walls, full-scale walls vs. small size specimens, brick columns and triplets vs. small walls, masonry specimens vs. single units of brick and mortar prisms, …). Different advanced testing methods and novel monitoring techniques were applied in an integrat

Scopo dello studio: valutare i cambiamenti indotti da diversi trattamenti di mordenzatura sulla morfologia superficiale e sulla microstruttura di due vetro-ceramiche a base disilicato di litio (IPS e.max® Press e IPS e.max® CAD) ed esaminarne gli effetti sia sull’adesione con un cemento resinoso che sulla resistenza alla flessione. Materiali e metodi: Settanta dischetti (12 mm di diametro, 2 mm di spessore) di ogni ceramica sono stati preparati e divisi in 5 gruppi: nessun trattamento (G1), HF 5% 20s (G2), HF 5% 60s (G3), HF 9.6% 20s (G4), HF 9.6% 60s (G5). Un campione per ogni gruppo è stato analizzato mediante profilometro ottico e osservato al SEM. Per gli altri campioni è stato determinato lo shear bond strength (SBS) con un cemento resinoso. Dopo l’SBS test, i campioni sono stati caricati fino a frattura utilizzando il piston-on-three-ball test per determinarne la resistenza biassiale alla flessione. Risultati: L’analisi morfologica e microstrutturale dei campioni ha rivelato come diversi trattamenti di mordenzatura producano delle modifiche nella rugosità superficiale che non sono direttamente collegate ad un aumento dei valori di adesione e dei cambiamenti microstrutturali che sono più rilevanti con l’aumento del tempo di mordenzatura e di concentrazione dell’acido. I valori medi di adesione (MPa) per IPS e.max® CAD sono significativamente più alti in G2 e G3 (21,28 +/- 4,9 e 19,55 +/- 5,41 rispettivamente); per IPS e.max® Press, i valori più elevati sono in G3 (16,80 +/- 3,96). La resistenza biassiale alla flessione media (MPa) è più alta in IPS e.max® CAD (695 +/- 161) che in IPS e.max® Press (588 +/- 117), ma non è non influenzata dalla mordenzatura con HF. Conclusioni: il disilicato di litio va mordenzato preferibilmente con HF al 5%. La mordenzatura produce alcuni cambiamenti superficiali e microstrutturali nel materiale, ma tali cambiamenti non ne influenzano la resistenza in flessione., Purpose: The aim of this study was to evaluate the changes induced by different etching treatments on the surface morphology and microstructure of two lithium disilicate-based glass ceramic (IPS e.max® Press and IPS e.max® CAD) and examine the effects on the bond strength between ceramic and composite resin and on the biaxial flexural strength. Materials and methods: Seventy discs (12 mm diameter, 2 mm thickness) of each ceramic were prepared and divided in 5 groups: no treatment (G1), HF 5% 20s (G2), HF 5% 60s (G3), HF 9.6% 20s (G4), HF 9.6% 60s (G5). One specimen for each group was examined by optical profilometer and observed under scanning electron microscopy. On the other specimens was determined the shear bond strength (SBS) with a resin cement. After SBS test, specimens were loaded to failure using a piston-on-three-ball test to determine the biaxial flexural strength. Results: morphological analysis of treated specimens showed that different etching treatments produces changes in surface roughness but this changes are not directly related to an increasing adhesion value. The SEM analysis revealed that etching causes microstructural changes in lithium disilicate which are more relevant with the increasing of etching time and acid concentration. The mean bond strength values (MPa) for IPS e.max® CAD are statistically higher in G2 and G3 (21,28 +/- 4,9 and 19,55 +/- 5,41 respectively); for IPS e.max® Press, G3 has significant higher adhesion value (16,80 +/- 3,96). The mean biaxial flexural strength values (MPa) are significantly higher in IPS e.max® CAD (695 +/- 161) than in IPS e.max® Press (588 +/- 117). Etching with HF does not affect the flexural strength of the material. Conclusions: lithium disilicate has to be etched preferably with 5% HF. Etching produces several changes in surface and microstructure of the material, but does not compromise the flexural strength.

The above factors emphasize the scope of this thesis for further investigations on zirconia, the improvement of all-ceramic zirconia restorations, and especially the interaction of zirconia and veneering and its influence on the performance of the whole restoration. The introduction, chapter 1, gave a literature overview on zirconia ceramics. In chapter 2, the objective of the study was to evaluate the effect of abrading before and after sintering using alumina-based abrasives on the surface of yttria-tetragonal zirconia polycrystals. Particular attention was paid to the amount of surface stress–assisted phase transformation (tetragonal→monoclinic) and the presence of microcracks. Chapter 3 is based on the idea that the conventional sintering techniques for zirconia based materials, which are commonly used in dental reconstruction, may not provide a uniform heating, with consequent generation of microstructural flaws in the final component. As a consequence of the sintering system, using microwave heating, may represent a viable alternative. The purpose of the study was to compare the dimensional variations and physical and microstructural characteristics of commercial zirconia (Y-TZP), used as a dental restoration material, sintered in conventional and microwave furnaces. Chapter 4 described the effect of sandblasting before and after sintering on the surface roughness of zirconia and the microtensile bond strength of a pressable veneering ceramic to zirconia.

This thesis wad aimed at the study and application of titanium dioxide photocatalytic activity on ceramic materials. As a matter of fact, photocatalysis is a very promising method to face most of the problems connected with the increasing environmental pollution. Furthermore, titanium dioxide, in its anatase crystallographic phase, is one of the most investigated photocatalytic material and results to be perfectly compatible with silicate body mixes. That goal was pursued by two different strategies: 1. the addition to a body mix used for heavy clay products of several titania powders, with different mean crystallite size, surface area, morphology and anatase/rutile ratio and a titania nanosuspension as well. The titania addition followed two procedures: bulk and spray addition over the ceramic samples surface. Titania was added in two different percentages: 2.5 and 7.5 wt.% in both of the methods. The ceramic samples were then fired at three maximum temperatures: 900, 950 and 1000 °C. Afterwards, the photocatalytic activity of the prepared ceramic samples was evaluated by following the degradation of an organic compound in aqueous medium, under UV radiation. The influence of titania morphological characteristics on the photoactivity of the fired materials was studied by means of XRD and SEM observations. The ceramic samples, sprayed with a slip containing 7.5 wt.% of titania powder and fired at 900 °C, have the best photoactivity, with a complete photo-decomposition of the organic compound. At 1000 °C no sample acted as a photocatalyst due to the anatase-to-rutile phase transformation and to the reaction between titania and calcium and iron oxides in the raw materials. 2. The second one foresaw the synthesis of TiO2-SiO2 solid solutions, using the following stoichiometry: Ti1-xSixO2 where x = 0, 0.1, 0.3 and 0.5 atoms per formula unit (apfu). The mixtures were then fired following two thermal cycles, each with three maximum temperatures. The effect of SiO2 addition

This research, carried out during the PhD in Materials Engineering, deals with the creation of layers, with different functionality, deposited on a ceramic substrate, to obtain photovoltaic cells for electricity production. The research activities are included in the project PRRIITT, Measure 4 (Development of Networks), Action A (Research and Technology Transfer Laboratories), Thematic reference 3 (Advanced materials applications development), co-financed by the Emilia Romagna Region, for the creation of CECERBENCH laboratory, which aims to develop "Tiles with a functionalised surface”. The innovation lies in the study of materials and in the development of technologies to achieve a "photovoltaic surface", directly in the tiles production process. The goal is to preserve the technical characteristics, and to make available new surfaces, exploiting renewable energy sources. The realization of Building Integrated PhotoVoltaic (BIPV) is nowadays a more and more spread tendency. The aims of the research are essentially linked to the need to diversify the actual ceramic tile production (which is strongly present in the Emilia Romagna Region ), and to provide a higher added value to the tiles. Solar energy production is the primary objective of the functionalization, and has a relevant ecological impact, taking into account the overwhelming global energy demand. The specific activities of the PhD were carried out according to the achievement of scientific and technological objectives of CECERBENCH laboratory, and involved the collaboration in design solutions, to obtain the cells directly on the tiles surface. The author has managed personally a part of the research project. Layers with different features were made: - Electrically conductive layers, directly on the ceramic tiles surface; - Layers to obtain the photovoltaic functionality; - Electrically insulating, protective layers (double function). For each layer, the most suitable materials have been selected. Among th