Search

The obtaining technology of nanocomposites based on polyamide-6 and organomodified montmorillonite is developed. The technological parameters of extrusion and injection molding, and their influence on the formation of nanoscale inorganic phase of the polyamide are investigated. Morphology and thermal behavior of polyamide-6, composites based on polyamide-6 and modified montmorillonite are studied by WAXS, XRD, DTA and DSC data. Morphology and thermal behavior of polyamide-6 and composites based on polyamide-6 and modified montmorillonite are shown to be in a strong juxtaposition. New γ-phase formation is revealed in composite polyamide-6 – 1–2 % of modified montmorillonite in contrast with polyamide-6 and mechanical mixtures of polyamide-6 and montmorillonite. Optimal concentrations of modified montmorillonite in the composites stated as 1 – 2 % are shown to correspond with composites improved properties as compared to initial polyamide-6. It is explained by increasing crystallinity degree, which resulted from acting of modified montmorillonite particles as nucleation heterogenetic agents., Розроблено технологію отримання нанокомпозитів на основі поліаміду-6 та органомодифікованого монтморилоніту. Досліджено технологічні параметри екструзії та лиття під тиском та їх вплив на формування нанодисперсної неорганічної фази поліаміду. Морфологія та термічна поведінка поліаміду-6, композитів на основі поліаміду-6 та модифікованого монтмориллоніту, вивчені за допомогою WAXS, XRD, DTA та DSC. Показана якісна відмінність морфології та термічної поведінки поліаміду-6 та композитів на основі поліаміду-6 і модифікованого монтмориллоніту перебувають у сильному зіставленні. При складі поліаміду-6 – 1–2% модифікованого монтморіллоніту в порівнянні з поліамідом-6 та механічними сумішами поліаміду-6 та монтморилоніту виявлено нове утворення γ-фази. Показано, що оптимальні концентрації модифікованого монтмориллоніту в композитах, які вказані як 1–2%, відповідають поліпшеним властивостям композицитів у порівнянні з вихідним поліамідом-6. Це пояснюється збільшенням ступеня кристалинності, що виникає внаслідок дії модифікованих монтморилонітних частинок як зародкових гетерогенних агентів., Разработана технология получения нанокомпозитов на основе полиамида-6 и органомодификованого монтмориллонита. Исследованы технологические параметры экструзии и литья под давлением и их влияние на формирование нанодисперсных неорганической фазы полиамида. Морфология и термическое поведение полиамида-6, композитов на основе полиамида-6 и модифицированного монтмориллониту, изучены с помощью WAXS, XRD, DTA и DSC. Показано качественное различие морфологии и термической поведения полиамида-6 и композитов на основе полиамида-6 и модифицированного монтмориллониту находятся в сильном сопоставлении. При составе полиамида-6 – 1–2% модифицированного монтмориллонита по сравнению с полиамидом-6 и механическими смесями полиамида-6 и монтмориллонита обнаружено новое образование γ-фазы. Показано, что оптимальные концентрации модифицированного монтмориллонита в композитах, которые составляют 1–2%, соответствуют улучшенным свойствам композицитив по сравнению с исходным полиамида-6. Это объясняется увеличением степени кристаличности, возникающем вследствие действия модифицированных частиц монтмориллонита как зародышевых гетерогенных агентов.

Technology of obtaining montmorillonite modified by polyionenes is developed. Macromolecular polymer intercalation of a quaternary ammonium salt of montmorillonite intercrystalline space is shown to be accompanied with increased interlayer distances from 1.08 nm to 1.67 nm. The technique of synthesis of montmorillonite modified by polyionenes is suggested. Optimal conditions for sorption of polyionenes molecules with montmorillonite are found to be: the concentration of aqueous dispersion of montmorillonite is 1 %, the temperature of the reaction medium is 40 °C, the montmorillonite-polyionene ratio is 3 : 1, the processing time is 24 hours. The mechanism of montmorillonite modification is suggested to involve the next steps: connection of organic cations to montmorillonite surface determined by attachment of organic cations to exchange position during ion-exchange adsorption and adsorption of organic cations with acid sylanol groups, i.e. torn bonds on crystal faces. These processes are shown to result in more perfect structure by organic cations adsorption with acid sylanol groups (torn bonds on crystal faces)., Разработана технология получения монтмориллонита, модифицированного полионенами. Показано, что интеркаляция макромолекулярного полимера четвертичной аммониевой соли межмолекулярного пространства монтмориллонита сопровождается увеличением межслоевых расстояний от 1.08 нм до 1.67 нм. Предложена методика синтеза монтмориллонита, модифицированного полионинами. Найдены оптимальные условия для сорбции молекул полионенов с монтмориллонитом: концентрация водной дисперсии монтмориллонита составляет 1 %, температура реакционной среды – 40 °C, отношение монтмориллонит-полиионен составляет 3 : 1, время обработки 24 ч. Предполагается, что механизм модификации монтмориллонита включает следующие стадии: подключение органических катионов к поверхности монтмориллонита, определяемое присоединением органических катионов к обменному положению при ионообменной адсорбции и адсорбции органических катионов кислотными силановыми группами, тобто розорванными связями на поверхностях кристаллов. Показано, что эти процессы приводят к более совершенной структуре путем адсорбции органических катионов кислотными группами силанола (разрывы связей на поверхностях кристаллов)., Розроблено технологію отримання монтмориллоніту, модифікованого полііоненами. Показано, що інтеркаляція високомолекулярних полімерів четвертинної амонієвої солі монтморіллонітного міжкристалічного простору супроводжується збільшенням міжшарової відстані від 1.08 нм до 1.67 нм. Запропоновано методику синтезу монтмориллоніту, модифікованого полііоніенами. Виявлено оптимальні умови для сорбції молекул полііонінів з монтмориллонітом: концентрація водної дисперсії монтмориллоніту становить 1 %, температура реакційного середовища 40 °С, співвідношення монтмориллоніту-полііонену 3 : 1, час обробки 24 годин Запропонований механізм модифікації монтморіллоніту включає наступні стадії: з'єднання органічних катіонів з поверхнею монтмориллоніту, що визначається приєднанням органічних катіонів до обмінної позиції при адсорбції та адсорбцію органічних катіонів з кислотними синанольними групами, тобто розірваними зв'язками на поверхнях кристалів. Показано, що ці процеси призводять до більш досконалої структури за рахунок адсорбції органічних катіонів кислотними синанольними групами (розірваними зв'язками на поверхнях кристалів).