The sensitivity of zinc (Zn(II)) detection using fast-scan cyclic voltammetry (FSCV) with carbon fiber microelectrodes (CFMEs) is low compared to other neurochemicals. We have shown previously that Zn(II) plates to the surface of CFME's and we speculate that it is because of the abundance of oxide functionality on the surface. Plating reduces sensitivity over time and causes significant disruption to detection stability. This limited sensitivity and stability hinders Zn(II) detection, especially in complex matrices like the brain. To address this, we developed plasma-treated gold fiber microelectrodes (AuMEs) which enable sensitive and stable Zn(II) detection with FSCV. Typically, gold fibers are treated using corrosive acids to clean the surface and this step is important for preparing the surface for electrochemistry. Likewise, because FSCV is an adsorption-based technique, it is also important for Zn(II) to adsorb and desorb to prevent irreversible plating. Because of these requirements, careful optimization of the electrode surface was necessary to render the surface for Zn(II) adsorption yet strike a balance between attraction to the surface vs. irreversible interactions. In this study, we employed oxygen plasma treatment to activate the gold fiber surface without inducing significant morphological changes. This treatment effectively removes the organic layer while functionalizing the surface with oxygen, enabling Zn(II) detection that is not possible on untreated gold surfaces. Our results demonstrate significantly improved Zn(II) detection sensitivity and stability on AuME compared to CFME's. Overall, this work provides an advance in our understanding of Zn(II) electrochemistry and a new tool for improved metallotransmitter detection in the brain. [ABSTRACT FROM AUTHOR]

The effect of cations on the corrosion of galvanized steel (GS) is scarcely reported. In this study, a wet–dry cyclic test was conducted to study NH4+, Na+, and Mg2+ cation effect on the corrosion behavior of GS available in Nepal. Fourteen wet–dry cycles (18 h wet and 6 h dry) were performed by exposing samples at 298 K with a relative humidity of 90% in a wet cycle and 50% in a dry cycle for 14 days. The cations strongly affect the corrosion rate of the GS sample estimated by weight loss and potentiodynamic polarization. The potentiodynamic polarization curves showed the inhibition of cathodic and anodic reactions by Mg2+ ion, while the NH4+ ion only changed the cathodic reaction. Mg2+ ion was found to shift the corrosion potential to noble values compared with NH4+ and Na+ ions. A compact and thin corrosion products layer was developed in Mg2+ salt solution in contrast to a thick and porous corrosion products layer in NH4+ and Na+ salt solutions. Red rust due to corrosion of underlying steel appeared in the presence of NH4+ and Na+ salt solutions. Finally, the weight loss data revealed that the corrosivity of cations for GS decreased in the order Na+ > NH4+ > Mg2+. [ABSTRACT FROM AUTHOR]