An approach to detecting discontinuities in carbon fiber-reinforced polymers, caused by impact loading followed by compression testing, was developed. An X-ray sensor-based installation was used, while some algorithms were developed to improve the quality of the obtained low-contrast radiographic images with negligible signal-to-noise ratios. For epoxy/AF (#1) composite subjected to a "high-velocity" steel-ball impact with subsequent compression loading, it was not possible to detect discontinuities since the orientation of the extended zone of interlayer delamination was perpendicular to the irradiation axis. After drop-weight impacts with subsequent compression loading of epoxy/CF (#2) and PEEK/CF (#3) composites, the main cracks were formed in their central parts. This area was reliably detected through the improved radiographic images being more contrasted compared to that for composite #3, for which the damaged area was similar in shape but smaller. The phase variation and congruency methods were employed to highlight low-contrast objects in the radiographic images. The phase variation procedure showed higher efficiency in detecting small objects, while phase congruency is preferable for highlighting large objects. To assess the degree of image improvement, several metrics were implemented. In the analysis of the model images, the most indicative was the PSNR parameter (with a S-N ratio greater than the unit), confirming an increase in image contrast and a decrease in noise level. The NIQE and PIQE parameters enabled the correct assessment of image quality even with the S-N ratio being less than a unit. [ABSTRACT FROM AUTHOR]

The aim of this study was to optimize a set of technological parameters (travel speed, extruder temperature, and extrusion rate) for 3D printing with a PEEK-based composite reinforced with 30 wt.% glass fibers (GFs). For this purpose, both Taguchi and finite element methods (FEM) were utilized. The artificial neural networks (ANNs) were implemented for computer simulation of full-scale experiments. Computed tomography of the additively manufactured (AM) samples showed that the optimal 3D printing parameters were the extruder temperature of 460 °C, the travel speed of 20 mm/min, and the extrusion rate of 4 rpm (the microextruder screw rotation speed). These values correlated well with those obtained by computer simulation using the ANNs. In such cases, the homogeneous micro- and macro-structures were formed with minimal sample distortions and porosity levels within 10 vol.% of both structures. The most likely reason for porosity was the expansion of the molten polymer when it had been squeezed out from the microextruder nozzle. It was concluded that the mechanical properties of such samples can be improved both by changing the 3D printing strategy to ensure the preferential orientation of GFs along the building direction and by reducing porosity via post-printing treatment or ultrasonic compaction. [ABSTRACT FROM AUTHOR]