Search

This study addresses the durability and complications of zirconia dental implants through a prospective clinical investigation. Zirconia implants are increasingly utilized in dental implantation, and a comprehensive understanding of their long-term performance is essential. Background: Zirconia dental implants have gained attention due to their biocompatibility and aesthetics. However, research on their extended success and complication rates is limited. Materials and Methods: A prospective clinical study involved the placement of 30 zirconia dental implants in patients requiring tooth replacement. The implants were followed up for five years. Success was defined as the implant remaining stable and functional. Complications, including peri-implant mucositis and peri-implantitis, were monitored. Statistical analysis included descriptive statistics, Chi-square test, and P-values were set at P < 0.05. Results: The long-term success rate of zirconia dental implants was found to be 93.3%. Among the 30 implants, only 2 exhibited failure. The most common complication was peri-implant mucositis, occurring in 16.7% of implants. Notably, the incidence of peri-implantitis was limited, observed in 6.7% of implants. Statistical analysis showed significant associations between implant failure and smoking (P = 0.021). Conclusion: Zirconia dental implants demonstrated a high long-term success rate of 93.3% over five years. Peri-implant mucositis was the predominant complication, with a relatively low occurrence of peri-implantitis. The findings underscore the potential of zirconia implants for reliable dental implantation. Addressing modifiable risk factors, such as smoking, could further enhance implant success. Continued research is recommended to validate and expand upon these outcomes. [ABSTRACT FROM AUTHOR]

Aphthous ulcers, also known as canker sores, are a common oral condition characterized by recurrent, painful, small ulcers that typically arise on the non-keratinized mucous membranes within the mouth. Although the pathogenesis of aphthous ulcers is not completely understood; it is believed to be involved in a combination of genetic predisposition, local trauma, stress, hormonal changes, and certain environmental factors. Thus, management of aphthous ulcer revolves around reducing pain, promoting healing and preventing recurrence., (© 2024 Biomedical Informatics.)

Aim: Evaluation and comparison of flexural strength and hardness of heat-cured polymethylmethacrylate (PMMA) denture base with polyetheretherketone (PEEK)., Material and Methods: A total of 80 samples of PEEK and PMMA were prepared and divided into two groups: group A and group B, of 40 each. Both the groups were further divided into subgroups consisting of 20 samples of PMMA and PEEK. The group A specimens were tested for flexural strength by universal testing machine (UTM), and group B samples were subjected to hardness test using Vickers microhardness tester. The values obtained were subjected to statistical analysis. The readings were subjected to an unpaired t -test for comparison of flexural strength and hardness of PEEK and PMMA., Result: The flexural strength of PEEK was 183 MPa, while that of PMMA was 84 MPa. The hardness of PEEK and PMMA was 24 VHN and 19.4 VHN, respectively., Conclusion: It was observed that PEEK can be a potential denture base material with superior properties as compared to PMMA. Further researches are needed to be carried out., Clinical Significance: PEEK as a denture base exhibits adequate flexural strength prolonging its clinical longevity and overcoming the most common reason for the failure of PMMA denture base that results in fracture.