Search

The relation between the cellulose nanocrystals (CNC) dynamic properties and the centrifugation G force applied on their purification process was investigated using the depolarized dynamic light scattering technic. Samples containing CNC were prepared using sulfuric acid hydrolysis and centrifugated on the following G forces: 1840, 4140, 7370, 11510 e 16580. The translational and rotational diffusion coefficients were determined for the different samples, from these values, the CNC widths (d) and lengths (L) were calculated. The values for the d and L lied from 213 ± 10 nm to 294 ± 14 nm and 4,4 ± 1,2 nm to 9,5 ± 2,0nm, respectively. The results agree with the the literature, confirming the applicability of the technic on the study of NCC dynamic properties in aqueous suspensions. There was no significant variation on the values of L by the increment on the G force within the studied interval. On the other hand, d reduced with the G force increase for values above 7370. Investigou-se, utilizando a técnica de espalhamento dinâmico de luz depolarizado, a relação das propriedades dinâmicas de suspensões de nanocristais de celulose (NCC) com a força G de centrifugação aplicada no processo de purificação das mesmas. Amostras contendo NCC foram preparadas por meio de hidrólise com ácido sulfúrico e centrifugadas nas intensidades de 1840, 4140, 7370, 11510 e 16580 de força G. Determinou-se os coeficientes de difusão translacionais e rotacionais e, a partir destes, calculou-se as larguras (d) e os comprimentos (L) dos NCC. Os valores de L e de d encontraram-se nas faixas de 213 ± 10 a 294 ± 14nm e de 4,4 ± 1,2 a 9,5 ± 2,0nm, respectivamente. Os resultados concordaram com os disponíveis na literatura, confirmando a aplicabilidade da técnica no estudo da dinâmica dos NCC em suspensões aquosas. Não observou-se variação significativa de L com o aumento da força G na faixa estudada. Por outro lado, houve redução de d para valores de força G acima de 7370.