Phase pure WC nanoparticles were synthesized on high surface area carbon black (800 m2 g-1) by a temperature programmed reaction (TPR) method. The particle size of WC can be controlled under 30 nm with a relatively high coverage on the carbon surface. The electrochemical testing results demonstrated that the corrosion resistance of carbon black was improved by 2-fold with a surface modification by phase pure WC particles. However, the WC itself showed some dissolution under potential cycling. Based on the X-ray diffraction (XRD) and inductively coupled plasma (ICP) analysis, most of the WC on the surface was lost or transformed to oxides after 5000 potential cycles in the potential range of 0.65-1.2 V. The Pt catalyst supported on WC/C showed a slightly better ORR activity than that of Pt/C, with the Pt activity loss rate for Pt/WC/C being slightly slower compared to that of Pt/C. The performance and decay rate of Pt/WC/C were also evaluated in a fuel cell. © 2010 Elsevier B.V. All rights reserved.

We determined the size-dependent specific and mass activities of the oxygen reduction in HClO4 solutions on the Pt particles in the range of 1-5 nm. The maximal mass activity at 2.2 nm is well explained based on density functional theory calculations performed on fully relaxed nanoparticles. The presence of the edge sites is the main reason for the low specific activity in nanoparticles due to very strong oxygen binding energies at these sites. Our results clearly demonstrate that the catalytic activity highly depends on the shape and size of the nanoparticles. © 2011 American Chemical Society.

The increase in oxygen binding energy was previously proposed to account for the lower oxygen reduction activity of a Pt monolayer supported on Au(111) single crystal than that on Pd(111) and pure Pt(111) surfaces. This single-crystal based understanding, however, cannot explain the new finding of a 1.6-fold increase of oxygen reduction activity on Pt monolayer-modified 3-nm Au nanoparticles (Pt/Au/C) in comparison with that on Pt/Pd/C with a similar particle size. The Pt/Au/C catalyst also has an activity higher than that of a state-of-the-art 2.8-nm Pt/C catalyst. Our new experimental results and density functional theory calculations demonstrate that a significant compressive strain in the surface of the core nanoparticles plays a role in the observed activity enhancement. © 2010 American Chemical Society.

We demonstrate the synthesis of a core-shell catalyst consisting of a Pt monolayer as the shell and porous/hollow Pd-Cu alloy nanoparticles as the core. The porous/hollow Pd-Cu nanoparticles were fabricated by selectively dissolving a less noble metal, Cu, using an electrochemical dealloying process. The Pt mass activity for the oxygen reduction reaction of a Pt monolayer deposited on such a porous core is 3.5 times higher than that of a Pt monolayer deposited on bulk Pd nanoparticles and 14 timeshigherthanthat of state-of-the-artPt/ Celectrocatalysts. © 2010 American Chemical Society.