The mechanical properties and microstructural features of 1561 aluminum alloy weldments processed by single-wire MIG welding and CMT TWIN welding are investigated. The microstructure and mechanical properties of welded joints were studied by nondestructive testing, metallurgical test, scanning electron microscopy test, fatigue and tensile test. It is revealed that the welding efficiency of CMT TWIN welding is more than six times as much as single-wire MIG welding. It can be easy to find weld zone (WZ), fusion line (FL), heat affected zone (HAZ) and base metal (BM) with different characteristics in the metallographic specimen. In weld zone, the particle phase sizes are smaller than that of base material, but the densities of particle phase are increased. The sample fatigue strength of CMT TWIN welding is higher than the singe-wire MIG welding. It is suggested that the CMT TWIN welding has several advantages compared with single-wire MIG welding.

Plasma-MIG hybrid welding and MIG welding of 5083 marine aluminum alloy was carried out. The influences of parameters of welding process on the weldments morphology were investigated in order to optimize the welding process parameters. The macrostructure, microstructure, tensile and bending properties of the optimized joint were studied. The results show that Plasma-MIG hybrid welding not only has a synergistic effect of Plasma and MIG welding but also has a high welding efficiency. Welding speed, Plasma current and MIG current have a significant effect on welding penetration and welding morphology. Meanwhile, the ductility and strength property of weld joint was qualified though the bending test and tensile test. The average tensile strength of weld joint is about 285MPa at room temperature, about 86% of the base metal.

In order to improve the quality of laser cutting of stainless steel porous, the investigation on cutting 0.12mm stainless steel plates was carried out by a50W-powerbridgefiber laser cutting machine.The influence of the auxiliary line angle, laser power, and the pulse width and gas pressure on the cutting quality was studied in this paper.The results show that fewer defects was found on the samples when the cutting angle of auxiliary line was 90°and few splash orburrswas found on the samplesby 40 Wlaser power, with 56 μs pulse width and 1.3MPa gas pressure.