Search

Objectives: Reinforcement of polymethylmethacrylate (PMMA) denture base resins (DBRs) with inorganic fillers with superior properties and accepted aesthetics are favored and still a big dilemma. This study was undertaken to evaluate the color change, flexural strength, and modulus of elasticity of heat-polymerized DBR material modified with silver nanoparticles (AgNPs) and zirconium dioxide nanoparticles (ZNPs). Methods: Sixty acrylic specimens (30/color test, 30/flexural properties) were fabricated and divided according to nanoparticles type and addition into 3 groups (n = 10). Group-I; unmodified specimens, Group-II; modified specimens with 0.5wt% AgNPs (PMMA/AgNPs), and Group-III; modified specimens with 7.5wt% ZNPs (PMMA/ZNPs). Disc-shape (20 × 3 mm) and bar-shape (65 × 10 × 2.5 mm) specimens were fabricated for color and flexural properties, respectively. The spectrophotometer was used for evaluation of the color change (∆E). The flexural strength and elastic modulus evaluation was carried out using a 3-point bending test (5 mm/min). Tukey’s post hoc and one-way ANOVA were used to analyze the data at a significant level P ≤ 0.05. Results: PMMA/AgNPs group exhibited a significant increase in color change when compared with PMMA/ZNPs. PMMA/ZNPs showed significantly the highest flexural strength value when compared with unmodified and PMMA/AgNPs groups (P < 0.001), however, there was an absence of significant differences in terms of flexural strength values between PMMA/AgNPs and unmodified groups (P > 0.05). PMMA/AgNPs insignificantly increased its modulus of elasticity strength (P = 0.09410) while PMMA/ZNPs significantly increased its modulus of elasticity strength (P = 0.00396). Conclusion: The AgNPs and ZNPs addition to PMMA increased the color change and AgNPs change the color of DBRs. The flexural attributes of DBRs have been increased by ZNPs. [ABSTRACT FROM AUTHOR]

Background: Tumor-promoting factors (TPF) and metabolic reprogramming are hallmarks of cancer cell growth. This study is designed to combine the newly synthesized two nanocomposites DDM (HA-FA-2DG@DCA@MgO) and AF (HA-FA-Amygdaline@Fe2O3) with fractionated doses of radiotherapy (6 Gy-FDR; fractionated dose radiotherapy) to improve the efficiency of chemo-radiotherapy against breast cancer cell lines (BCCs; MCF-7 and MDA-MB-231). The physicochemical properties of each nanocomposite were confirmed using energy dispersive XRD, FTIR, HR-TEM, and SEM. The stability of DDMPlusAF was also examined, as well as its release and selective cellular uptake in response to acidic pH. A multiple-MTT assay was performed to evaluate the radiosensitivity of BCCs to DDMPlusAF at 3 Gy (single dose radiotherapy; SDR) and 6 Gy-FDR after 24, 48, and 72 h. Finally, the anti-cancer activity of DDMPlusAF with 6 Gy-FDR was investigated via assessing the cell cycle distribution and cell apoptosis by flow cytometry, the biochemical mediators (HIF-1α, TNF-α, IL-10, P53, PPAR-α, and PRMT-1), along with glycolytic pathway (glucose, HK, PDH, lactate, and ATP) as well as the signaling effectors (protein expression of AKT, AMPK, SIRT-1, TGF-β, PGC-1α, and gene expression of ERR-α) were determined in this study. Results: The stability of DDMPlusAF was verified over 6 days without nanoparticle aggregation. DDMPlusAF release and selectivity data revealed that their release was amenable to the acidic pH of the cancer environment, and their selectivity was enhanced towards BCCs owing to CD44 and FR-α receptors-mediated uptake. After 24 h, DDMPlusAF boosted the BCC radiosensitivity to 6 Gy-FDR. Cell cycle arrest (G2/M and pre-G1), apoptosis induction, modulation of TPF mediators and signaling effectors, and suppression of aerobic glycolysis, all confirmed DDMPlusAF + 6 Gy's anti-cancer activity. Conclusions: It could be concluded that DDMPlusAF exerted a selective cancer radiosensitizing efficacy with targeted properties for TPF and metabolic reprogramming in BCCs therapy. [ABSTRACT FROM AUTHOR]

BACKGROUND: Demineralization of the enamel surface, which appears as white spot lesions during and after removal of the fixed orthodontic appliance, is the most common disadvantage of the orthodontic treatment course. Using the remineralizing agents during and after orthodontic treatment helps to avoid those enamel defects. OBJECTIVE: The present study aims to assess the remineralizing effect of the chicken eggshell powder on the demineralized enamel surfaces after debonding the orthodontic bracket system. MATERIALS AND METHODS: The current study was performed on 80 prepared premolar crowns embedded into acrylic molds. The samples were prepared to receive routine steps of the bonding process for the bracket system. The paste of the chicken eggshell powder was added to the samples after the debonding process. Scanning electron microscopy (SEM) and energy-dispersive X-ray (EDX) were used to evaluate the remineralization effect of the chicken eggshell powder. Also, the Vickers microhardness tester was used to assess the enamel surface microhardness. RESULTS: It was found that the mean value of the Ca/P ratio for the samples before bonding of the orthodontic bracket system was (4.17 ± 2.2). This value significantly decreased to (2 ± 1.3) after debonding of the orthodontic bracket system and then showed a significant increase to (4.79 ± 2.65) after remineralization. These results were assured by the values of the Vickers microhardness tester. CONCLUSION: The chicken eggshell powder has an excellent remineralization effect for the demineralized enamel surface after debonding the orthodontic enamel surface. [ABSTRACT FROM AUTHOR]

The feasibility of using coconut shell powder (CSP) and dog conch shell powder (DCSP) as carburizing media in the pack carburization of SCM 420 steel was investigated. The carbon content and surface hardness of the carburized specimens prepared with different CSP:DCSP ratios and carburizing durations were examined and compared. A CSP:DCSP ratio of 60%:40% and an extended carburizing time of 12 h were found to increase the carbon content of the carburized specimens to 1.14 ± 0.007 wt%. Furthermore, the surface hardness was significantly improved to 961.3 ± 4.918 HV following water quenching. Finally, the thickness of the carburized layer of the quenched specimens increased by around 2.5 times as the carburizing duration was increased from 3 to 12 h. [ABSTRACT FROM AUTHOR]

Objectives: Reinforcement of polymethylmethacrylate (PMMA) denture base resins (DBRs) with inorganic fillers with superior properties and accepted aesthetics are favored and still a big dilemma. This study was undertaken to evaluate the color change, flexural strength, and modulus of elasticity of heat-polymerized DBR material modified with silver nanoparticles (AgNPs) and zirconium dioxide nanoparticles (ZNPs)., Methods: Sixty acrylic specimens (30/color test, 30/flexural properties) were fabricated and divided according to nanoparticles type and addition into 3 groups ( n = 10). Group-I; unmodified specimens, Group-II; modified specimens with 0.5wt% AgNPs (PMMA/AgNPs), and Group-III; modified specimens with 7.5wt% ZNPs (PMMA/ZNPs). Disc-shape (20 × 3 mm) and bar-shape (65 × 10 × 2.5 mm) specimens were fabricated for color and flexural properties, respectively. The spectrophotometer was used for evaluation of the color change (∆E). The flexural strength and elastic modulus evaluation was carried out using a 3-point bending test (5 mm/min). Tukey's post hoc and one-way ANOVA were used to analyze the data at a significant level P ≤ 0.05., Results: PMMA/AgNPs group exhibited a significant increase in color change when compared with PMMA/ZNPs. PMMA/ZNPs showed significantly the highest flexural strength value when compared with unmodified and PMMA/AgNPs groups ( P < 0.001), however, there was an absence of significant differences in terms of flexural strength values between PMMA/AgNPs and unmodified groups ( P > 0.05). PMMA/AgNPs insignificantly increased its modulus of elasticity strength ( P = 0.09410) while PMMA/ZNPs significantly increased its modulus of elasticity strength ( P = 0.00396)., Conclusion: The AgNPs and ZNPs addition to PMMA increased the color change and AgNPs change the color of DBRs. The flexural attributes of DBRs have been increased by ZNPs., Competing Interests: The authors declare that they have no conflicts of interest., (Copyright: © International Journal of Health Sciences.)