Search

In present work the properties of iron-doped indium tin oxide (ITO) films with reduced to 50 mass% indium oxide content prepared by co-sputtering of ITO and Fe2O3 targets and ITO and Fe3O4 targets in mixed argon–oxygen atmosphere were studied by various methods. The influence of different working gas flow rates, RF power of iron oxide targets, type of doping oxide and heat treatment temperatures on the electrical, optical, structural, and morphological properties of the films was characterized by means of four-point probe method, ultraviolet–visible (UV–Vis) spectroscopy, X-ray diffraction and atomic force microscopy. [ABSTRACT FROM AUTHOR]

Silicon nano- and microparticles obtained using electric-spark dispersion of silicon electrodes and granules in 40 wt% solution of methyl alcohol in water were investigated by ultrasoft X-ray emission spectroscopy, X-ray photoelectron spectroscopy, X-ray diffraction, scanning and transmission electron microscopies. In addition, the SiLα spectra of obtained silicon particles were modeled by superimposing the spectra of pure silicon and silicon oxide taken in certain weight ratios. It was found that the surfaces of Si nano- and microparticles obtained in 40 wt% solution of methyl alcohol in water are covered with silicon oxide and chemisorbents, while the core consists of crystalline silicon with a cubic face-centered lattice. The silicon nano- and microparticles show potential as an anode material to replace commonly used graphite electrodes. The charge capacity of the electrode based on mixture of Si nano- and microparticles with graphite powder was about 1272 mAh/g after ten cycles. [ABSTRACT FROM AUTHOR]

Multilayer iron-doped indium-saving indiumtin oxide (ML ITO50:Fe2O3) thin films with high conductivity and high transmittance in the visible spectrum have been fabricated by sputtering method. Structures consisting of very thin layer of conventional indium tin oxide (90 mass% In2O310 mass% SnO2) and iron-doped indium-saving indiumtin oxide layer with reduced content of In2O3 (ITO50:Fe2O3) to 50 mass% are discussed. By optimizing oxygen flow rate in iron-doped indium-saving indiumtin oxide layer, the lowest volume resistivity of 3.78 × 10-4·cm, mobility of 29.8cm2/(V·s), carrier concentration of 4.60 × 1020 cm-3 and transmittance larger than 90% in the visible range have been achieved. ML ITO50:Fe2O3 thin films deposited under optimal conditions demonstrated lower volume resistivity and higher transmittance than undoped multilayer indium-saving ITO thin films and iron-doped single-layer thin films obtained under the same oxygen flow rate Q(O2) = 0.1 sccm. ML ITO50:Fe2O3 thin films demonstrated optimal parameters at the lower oxygen flow rate (Q(O2) = 0.1 sccm) than undoped ML ITO50 thin films. ML ITO50:Fe2O3 thin films are crystallized and show In4Sn3O12 structure. [ABSTRACT FROM AUTHOR]

Hollow graphitic carbon nanoparticles (HGCNs) obtained by catalytic graphitization of acetylene carbon black (ACB) were investigated using ultra-soft X-ray emission spectroscopy. The electronic structures of the ACB HGCNs were compared with those of HGCNs obtained from iron carbide-filled carbon nanocapsules (Fe3C@CNCs) and Q-graphenes. The occupation of the π sub-band decreased in the following sequence: Fe3C@CNC HGCNs > ACB HGCNs > Q-graphenes. This sequence can be explained by changes in the occupations of the C2p states due to the formation of bonds between carbon and residual metal atoms within the HGCNs. It was also found that the contribution of the overlapping ofppπ+ppσ-states in the ACB HGCN walls toward the spectra of the HGNCs was greater in comparison with the reference Q-graphenes. It was established that ACB was not fully transformed into the HGCNs. Scanning and transmission electron microscopy methods were used to study the spatial structures and morphologies of the fabricated HGCNs. [ABSTRACT FROM PUBLISHER]

Investigations of the electronic structure of graphene nanosheets synthesized by the reduction of oxidized graphene nanosheets were carried out using ultra-soft X-ray emission spectroscopy (USXES). Oxidized graphene nanosheets were produced from carbon nanofiber starting material using a modified Hummers method. X-ray diffraction, and scanning and transmission electron microscopy investigations were used in addition to USXES to study the electronic structure evolution from carbon nanofibers to graphene nanosheets. The effect of the degree of corrugation of the graphene nanosheets on the fine structure of the CK(alpha)-emission bands was revealed by USXES. It was found that corrugation of the graphene nanosheets is caused by overlapping of the pi-orbitals and formation of mixed (sigma + pi)-states.