Search

In this study, cement minerals, aluminates, and alkali-free accelerators incorporated with steel fiber were used to scrutinize the influence of accelerating agents on the long-term performance of tunneling shotcrete. Performance tests were identified based on the core compressive strength of mix shotcrete specimens with different types of accelerating agents throughout timeframes of 1, 3, 6, and 12 months. Here, 37 kg of steel fiber was incorporated into the cement mineral and aluminate mixes, and 40 kg of steel fiber was incorporated in an alkali-free mix for the shotcrete mix design. The KSF 2784 and ASTM 214 standards were followed for specimen fabrication and core cutting. For all specimens, shotcrete test panels of 250 × 600 × 500 mm were manufactured for core compressive strength tests conducted using 100, 75 and 55 mm diameter cylindrical molds and a length-to-diameter ratio of 2. The 1-month compressive strength of all test variables satisfied the Korea Expressway Co. standard of 21 MPa. The core compressive strength of the shotcrete specimens showed a tendency to increase with age, but a strength reduction occurred in 6 months and increased again at 12 months. Moreover, the impact of the diameter changes in the shotcrete core specimens was analyzed based on the mixing. For 12 months, a large increase in the core compressive strength occurred, particularly in the alkali-free specimens. The comparison also focused on the relative strength compared with a cast concrete mold and shotcrete core specimens. It is necessary to use alkali-free accelerators considering the long-term performance of tunnels and worker safety.

Shotcrete is widely used in underground and tunneling applications due to their superior flexural properties and impact resistance. There is a higher need in improving these properties by adding various admixtures and fiber reinforcements to achieve superior performance to accomplish faster turnout in tunneling constructions. In this study, the effect of three accelerators on the long-term flexural performance of steel-fiber reinforced shotcrete were investigated. The types of accelerators used were aluminate, cement mineral, and alkali-free accelerators, whose effects on the flextural properties were investigated over the periods of 1, 3, 6, 12, and 24 months. The flexural toughness was first estimated in accordance with JSCE SF-04, where up to span/150 deflection area under the load-deflection curve was used for calculating the flexural toughness. Whereas ASTM C1018–97 was used to evaluate the first-crack and post-peak load toughness behavior with three specified points for better understanding the flexural behavior of all mixtures. Moreover, it is important to use alkali-free accelerators in terms of both the long-term performance of the tunnels and the safety of the workers. The long-term performances of the specimens showed by the compressive strength and flexural strength were comparable. Finally, according to the long-term effectiveness and performance, the best mix design for the tunnel construction sites is also proposed.

" # $ % & ' jklmn opq+ ] c rstU( ) *uvw xy*Oz{| Oz}[~{_++,? e€r‚`ynƒ„qY€'-./# 0./ f*1,.2+1#.030 ) 4*1,.2+1#3-3+ 5# * 6 †h‡731./ˆ3‰/‡ hK‡731./ˆ3‰0‡Š‹‡731./ˆ3‰..‡ e€r‚`ynƒ„qY€'5 # * 206 e€r‚`ynƒ„qY€'5 # * 21/-6 e€r‚`ynƒ„qY€'

PURPOSES: The purpose of this study is to compare the alkali-silica reactivity for mortar bar and concrete prism specimens using crushed aggregates of 5 types in Korea. And the alkali-silica reactivity for those aggregates are measured by chemical test method. METHODS: The alkali-silica reactivity for those aggregates was measured by chemical test method of KS F 2545, mortar-bar test of KS F 2546, accelerated mortar-bar test method of ASTM C 1260 and concrete prism test method of ASTM C 1293, relatively. RESULTS: The alkali-silica reactivity for those aggregates was verified by chemical test of KS F 2546 and accelerated mortar-bar test of ASTM C 1260. However, it was not by mortar-bar test of KS F 2546 and concrete prism test of ASTM C 1293. CONCLUSIONS: The above results showed that relationship among the four test methods were very low. The results from 3 types of test methods using cement-aggregate combinations appeared to be different. Because the environmental conditions of test methods for measuring the alkali-silica reactivity such as equivalent alkali content(external source), humidity, temperature, and times were different though the aggregates were same. Moreover, alkali-silica reactivity showed the biggest impact when alkalis were supplied form outside and exposed to environmental conditions. The accelerated mortar-bar test method seems to be most appropriate test method for concrete structures exposed to alkali environment.

The purpose of this study was to review application of ASTM C 1260 for cement matrix with flyash and lithium nitrate using reactive aggregate. The experimental program included the accelerated mortar bar test (AMBT: ASTM C 1260) for the slate which was evaluated as reactive aggregate by ASTM C 1260 at the previous study. The cement, which was substituted by 10, 20, 30% flyash containing less than 10% CaO, could control ASR expansion. From the experiment applying lithium nitrate to control ASR, the mortar bar containing lithium nitrate showed more than 0.1% expansion at 14 days. This is probably due to dissolution of lithium nitrate in NaOH solution during test periods. Thus, it is necessary to adopt another test method to verify the control effect of lithium nitrate against alkali-silica reaction.

The possibility of ASR(alkali-silica reaction) for coarse aggregates had known to be low up to recently in Korea. But the distress of ASR was identified and reported by ASTM C 1260 test. The purpose of this paper was to identify the effect of environmental conditions on length expansion of mortar-bar by alkali-silica reaction with KS F 2546 and ASTM C 1260 test. The results of this study were as following; The result of KS F 2546 test for five kinds of aggregates shows that all of them are non-reactive. But that of ASTM C 1260 test shows that all of aggregates except Andesite-2 are over possible reactive because of environmental condition such as external alkali ion by 1N NaOH, high temperature and humidity. The result of variety of NaOH concentration on ASTM C 1260 using Siltstone indicates that length expansion rate increases highly as NaOH concentration increases. And, comparison results of KS F 2546 for Siltstone with that of 0.00N NaOH experiment indicates that length expansion rate increases as temperature and humidity increases.

The corrosions resulting from defects in painting layers frequently occur in Al alloys, so the application of corrosion preventing systems is also very important. Optimum conditions in terms of electrochemistry in relation to solution treatment, quenching and artificial aging treatment were established in order to optimize precipitation strengthening conditions intended to enhance the strength of Al alloys. Slow strain rate tests (SSRT) at various applied potentials were conducted in potential range from −1.8 to −0.5 V. The results show that the maximum tensile strengths, elongations and time-to-fracture are shown to be high values. After precipitation strengthening heat treatment, a tendency appear that time-to-fracture increases as elongation increases. In the potential range from −1.3 V to −0.7 V, the specimens show excellent mechanical properties, and thus this range is considered to be a corrosion prevention range.

The distresses of alkali-silica reaction (ASR) was recently reported at highway cement concrete pavement in Korea, which showed typical cracking and spalling patterns of ARS. Korea is was no longer safe zone against ASR, needding to find a control methodology against ASR. The purpose of this research was to provide a control methodology against ASR using mineral admixtures through a series of laboratory test program. Laboratory works included the accelerated mortar bar test (AMBT) by ASTM C 1260 regulation with five types of aggregate and three types of mineral admixtures (fly ash, ground granulated blast-furnace slag and silica fume). The result of ASTM C 1260 test for five types of aggregates without mineral admixtures showed that Siltstone and Mudstone were found to be "reactive." Tuff and Andesite-1 were found to be "possiblely reactive." In case of concrete mixed with 10, 20, and 30% fly ash, all specimens except Mudstone mixed with 10% FA were found to be "non-reactive". In cases of concrete mixed with 30, 40, and 50% ground granulated blast-furnace slag and 5, 7.5, and 10% silica fume, all specimens were found to be "non-reactive." These results could be selectively applied in constructions in Korea.

The purpose of this study was to evaluate the alkali-silica reactivity for aggregates in Korea according to test methods: accelerated mortar bar test (AMBT) by ASTM C 1260; chemical test by KS F 2545 (ASTM C 289). The results are as follows: The AMBT (ASTM C 1260) results showed that two (2) igneous rocks (two mica granite and felsite), three (3) sedimentary rocks (arkose, red sandstone and shale), two (2) metamorphic rock (slate and vitric tuff), one (1) mineral (quartz) showed more expansion than 0.1% at 14 days. But, some sedimentary rocks and metamorphic rocks expanded more than 0.1% at 28 days even though they were less than 0.1% at 14 days. Therefore, it is necessary to extend the experimental dates more than 14 days to evaluate the possibility of alkali-aggregate reactivity. The chemical test (KS F 2545) results showed that five (5) igneous rocks (andesite, diabase, granite porphyry, muscovite granite and diorite) were indicative of potentially deleterious expansion, while two (2) igneous rocks (diorite porphyry and quartz porphyry) were possible indicative of expansion, and three (3) igneous rocks (biotite granite, two mica granite and felsite) were indicative of innocuous reactivity. The above results showed that the results from chemical method (KS F 2545) and AMBT (ASTM C 1260) had little relationship.

OBJECTIVE: The purpose of our study was to describe radiologic manifestations of pulmonary tuberculosis in patients with systemic lupus erythematosus. CONCLUSION: The prevalence of pulmonary tuberculosis was high in patients with systemic lupus erythematosus. Imaging of these patients showed miliary dissemination and patchy consolidation. However, cavitation was rare. These findings may reflect impaired immune response against tuberculous bacilli.