Typically, archers prepare two sets of bows for competitions in case of bow breakage, but if the limbs of the bow break during a match, archers can become psychologically disadvantaged, leading to potentially fatal consequences. Archers are very sensitive to the durability and vibration of their bows. While the vibration-damping properties of Bakelite® stabilizer are excellent, its low density and somewhat lower strength and durability are disadvantages. As a solution, we used carbon fiber-reinforced plastic (CFRP) and glass fiber-reinforced plastic (GFRP) for the archery limb with stabilizer, commonly used for the limbs of the bow, to manufacture the limb. The stabilizer was reverse-engineered from the Bakelite® product and manufactured using glass fiber-reinforced plastic in the same shape as the existing product. Analyzing the vibration-damping effect and researching ways to reduce the vibration that occurs during shooting through 3D modeling and simulation, it was possible to evaluate the characteristics and the effect of reducing the limb’s vibration by manufacturing archery bows and limbs using carbon fiber- and glass fiber-reinforced composites. The objective of this study was to manufacture archery bows using CFRP and GFRP, and to assess their characteristics as well as their effectiveness at reducing limb vibration. Through testing, the limb and stabilizer that were produced were determined to not fall behind the abilities of the bows currently used by athletes, and they also exhibited a noticeable reduction in vibrations.

Novel poly(vinyl alcohol) (PVA)/poly(vinyl butyral–vinyl alcohol) (P(VB-VA)) films with improved hydrophobicity were prepared from poly(vinyl acetate) (PVAc)/poly(vinyl butyral) (PVB) blend films with various mass ratios by saponification in a heterogeneous medium. The successful conversion of PVAc to PVA and PVAc/PVB to PVA/P(VB-VA) films was confirmed by Fourier transform infrared spectrometry, X-ray diffraction, and proton nuclear magnetic resonance analysis. This study also shows that the degree of saponification (DS) depends on the saponification time. The maximum DS of 99.99% was obtained at 96 h of saponification for all films, and the presence of PVB did not affect the DS at saponification times of 48–96 h. The effects of the PVAc/PVB blend ratio before and after saponification were determined by contact angle measurement, and the hydrophobicity was found to increase in both cases with increasing PVB content. Additionally, all the films exhibited improved mechanical properties after saponification, and the treated films possessed an unusual porous and uneven surface, in contrast with the untreated films. The prepared films with improved hydrophobicity can be used for various applications, such as biomaterials, filters, and medical devices.

A novel PVA/clay (MMT) film is prepared for the first time based on the saponification of the PVAc/MMT film in the presence of heterogeneous conditions. With the help of optical microscopy, the characteristics and surface morphology of the saponified PVA/MMT film is confirmed. It is found to contain black MMT nanoparticles in PVAc films as the content of MMT increased. According to atomic force microscopy results, PVAc/MMT films shows unexpected surface roughness owing to the slow progress of the saponification reaction in the presence of MMT contents in the PVAc matrix. The thermal stability of the PVA/MMT film is measured using thermal gravimetric analyses. The results indicate that thermal stability increases significantly when the MMT concentration increases. The entire structure of the PVA/MMT nanocomposite has been elucidated using XRD. To prove the differences between the PVAc/MMT and the PVA/MMT films, XRD measurements and Fourier transform Infrared spectroscopy analyses are utilized.

For the first time, poly(vinyl alcohol) (PVA)/poly(methyl methacrylate–methallyl alcohol) (P(MMA-MAA)) (9:1, 7:3, 5:5) blend films were made simultaneously using the saponification method in a heterogeneous medium from poly(vinyl acetate) (PVAc)/poly(methyl methacrylate) (PMMA) (9:1, 7:3, 5:5) blend films, respectively. The surface morphology and characteristics of the films were investigated using optical microscopy (OM), atomic force microscopy (AFM), X-ray diffractometer (XRD), Fourier transform infrared (FTIR) spectroscopy, thermogravimetric analysis (TGA), and differential scanning calorimetry (DSC). Moreover, the effect of the PVAc content on the degree of saponification (DS) of the PVAc/PMMA films were evaluated and revealed that the obtained DS value increased with the increase in PVAc content in the PVAc/PMMA blend films. According to the OM results, the saponified films demonstrated increased surface roughness compared with the unsaponified films. The AFM images revealed morphological variation among the saponified PVAc/PMMA blend films with different mass ratios of 9:1, 7:3, and 5:5. According to the DSC and TGA results, all blend film types exhibited higher thermal property after the saponification treatment. The XRD and FTIR results confirmed the conversion of the PVAc/PMMA into PVA/P(MMA-MAA) films. Thus, our present work may give a new idea for making blend film as promising medical material with significant surface properties based on hydrophilic/hydrophobic strategy.

Blown films based on low-density polyethylene (LDPE)/linear low-density polyethylene (LLDPE) and silica aerogel (SA; 0, 0.5, 1, and 1.5 wt.%) were obtained at the pilot scale. Good particle dispersion and distribution were achieved without thermo oxidative degradation. The effects of different SA contents (0.5–1.5 wt.%) were studied to prepare transparent-heat-retention LDPE/LLDPE films with improved material properties, while maintaining the optical performance. The optical characteristics of the composite films were analyzed using methods such as ultraviolet–visible spectroscopy and electron microscopy. Their mechanical characteristics were examined along the machine and transverse directions (MD and TD, respectively). The MD film performance was better, and the 0.5% composition exhibited the highest stress at break. The crystallization kinetics of the LDPE/LLDPE blends and their composites containing different SA loadings were investigated using differential scanning calorimetry, which revealed that the crystallinity of LDPE/LLDPE was increased by 0.5 wt.% of well-dispersed SA acting as a nucleating agent and decreased by agglomerated SA (1–1.5 wt.%). The LDPE/LLDPE/SA (0.5–1.5 wt.%) films exhibited improved infrared retention without compromising the visible light transmission, proving the potential of this method for producing next-generation heat retention films. Moreover, these films were biaxially drawn at 13.72 MPa, and the introduction of SA resulted in lower draw ratios in both the MD and TD. Most of the results were explained in terms of changes in the biaxial crystallization caused by the process or the influence of particles on the process after a systematic experimental investigation. The issues were strongly related to the development of blown nanocomposites films as materials for the packaging industry.

Novel poly(vinyl alcohol) (PVA) nanofibers were prepared through the heterogeneous saponification of poly(vinyl acetate) (PVAc) nanofibers for the first time. To prepare the saponified PVA nanofibers, the effects of the alkali solution concentration and temperature were studied. It was found that the degree of saponification depended on the temperature and alkali solution concentration. Field emission scanning electron microscopy was utilized to characterize the morphology and properties of mats of the saponified PVA nanofibers, and unusual wrinkled and wound fibers were found. The conversion of PVAc nanofibers to PVA nanofibers was measured using proton nuclear magnetic resonance spectrometry, X-ray diffraction measurements, and Fourier transform infrared spectroscopy.

Nanocomposite film of pullulan (PULL), tempo cellulose nanofibrils (TOCNs) and, montmorillonite clay (MMT) were prepared using a solution casting method with aqueous solutions. X-ray diffraction data revealed that exfoliated MMT nanoplatelets are distributed within the PULL/TOCNs/MMT film structure. Fourier-transform infrared results revealed that there might be interactions among the TOCNs, MMT and PULL matrix led to improved tensile strength, thermal stability, water barrier properties, and decrease moisture susceptibility while maintained reasonable transparency and biodegradability of the ternary PULL nanocomposites. These excellent properties of the nanocomposites clearly indicate towards a new strategy for developing high-performance PULL-based nanocomposites by using two different types of fillers with various geometric shapes and aspect ratio. This kind of ternary nanocomposite film can be broadly used in food packaging and protection as a green and biodegradable film.

Fall-arrest systems(maximum arrest force and allowable free-fall) have been widely applied to provide a safe stop during fall incidents for various industrial activities. Fabric structure affects on the mechanical properties of shock energy absorber. The object of this study is to perform the basic research for the evaluation of the capacity of fall arrest energy absorber in relation to the different interlace yarn density. In this work, pack style energy absorber was prepared by weaving 10 types(Interlace yarn density used high tenacity PET 1000D : 60, 59, 58, 57, 56, 55, 54, 53, 52, 51). The paper presents the results of theoretical investigations of the performance of adjustable absorber during fall arrest. Dynamic load tests based on the EU fall protection equipment standard(CE : EN355:2002) were conducted. Results showed that the maximum arrest force by dynamic load test of energy absorber was satisfied with global standard(below 6,000N). Also, Maximum allowable free-fall of energy absorber showed below 1.75m.

Poly(vinyl alcohol) (PVA)/pullulan (PULL) blend nanofibres were prepared from their aqueous solutions by electrospinning method. Polymer solutions with different concentrations and blend ratios were used to investigate the effect of polymer concentrations and blend ratios on the morphologies and properties of PVA/PULL nanofibres. At a fixed blend ratio, the total polymer concentrations were also adjusted to find suitable electrospinning condition for preparing uniform and bead-free nanofibres. The as-prepared nanofibres were characterized by scanning electron microscopy (SEM), thermogravimetric analysis (TGA), differential scanning calorimetry (DSC), X-ray diffraction (XRD), and Fourier transform infrared (FTIR) spectroscopy. Their mechanical properties were also studied by measuring their tensile strength. The results showed that polymer concentrations and blend ratios have direct influence on the morphologies and properties of PVA/PULL nanofibres. 12 wt.% total polymer concentration and higher PVA contents have been found to be favourable for obtaining uniform and bead free PVA/PULL blend nanofibres with improved mechanical and thermal properties.

Poly(acrylonitrile) (PAN) nanofibres containing variable amounts of titanium dioxide (TiO2) were successfully electrospun under different conditions to find optimum electrospinning conditions and to investigate the effects of TiO2 content and electrospinning parameters on the morphologies and thermal properties of PAN/TiO2 nanofibres. Various amounts of TiO2 were dispersed separately into PAN solutions. N, N'-dimethyl formamide (DMF) was used as a solvent. Electrospinning parameters such as applied voltage and tip to collector distance (TCD) were varied at a fixed PAN/TiO2 mixing ratio. The PAN/TiO2 nanofibres containing different amounts of TiO2 were characterized by field-emission scanning electron microscopy (FE-SEM), X-ray photoelectron spectroscopy (XPS), and thermogravimetric analysis (TGA). The results showed TiO2 content and electrospinning parameters have direct influence on the morphologies of PAN/TiO2 nanofibres. Moreover, the addition of TiO2 significantly improved the thermal stability of the PAN nanofibres.

Zein produced from maize is a hydrophobic protein, which holds great potential for a number of industrial applications, for example, food packaging, pharmaceutical, cosmetic, and biomedical industry. Sorghum, known as important cereal crop worldwide, is a good source of various phytochemicals such as tannins, phenolic acids, anthocyanins, phytosterols, and policosanols, and these phytochemicals have great impact on human health. Poria cocos, a well‐known traditional East‐Asian medicinal plant, is found around the roots of pine trees in Korea and China. As a rapid and efficient process, electrospinning has drawn huge interest among scientists to produce nanostructured polymer materials with excellent properties. In this work, we studied the influence of co‐solvent ratio and concentration of zein/medicinal plant extract on the morphologies of nanostructured zein/medicinal plant extract nanomaterials prepared by electrospinning technique from ethanol/water solution. The zein/medici‐ nal extract nanofibers were characterized by field‐emission scanning electron micro‐ scopy, transmission electron microscopy, thermogravimetric analysis, and differential scanning calorimetric technique. And we were to incorporate medicinal plant resources into the electro‐spun zein nanofibers by electrospinning technique to investigate the effect of medicinal extract on the morphologies, antibacterial, antioxidant, and other properties. Zein/medicinal plant extract might have a practical use as a new preserva‐ tive for cosmeceutical applications.

Novel poly(vinyl alcohol) (PVA) nanofiber mats were prepared for the first time through heterogeneous saponification of electrospun poly(vinyl acetate) (PVAc) nanofibers. The effect of varying the saponification conditions, including temperature, time, and concentration of the alkaline solution, on the morphology of the saponified PVA fibers were evaluated by field-emission scanning electron microscopy. At 25 degrees C, the saponified PVA fibers exhibited a broad diameter distribution. The average fiber diameter, however, was found to decrease with increasing saponification temperature. When the saponification time was increased from 6 to 30 h, the average fiber diameter decreased gradually from 1540 to 1060 nm. In addition, the fiber diameter and morphology were also affected by the concentration of the alkaline saponification solution. The most optimal conditions for fabrication of thin, uniform, and smooth PVA nanofibers corresponded to an alkaline solution containing 10 g each of NaOH, Na2SO4, and methanol per 100 g of water, a temperature of 25 degrees C, and a saponification time of 24 h.

Pullulan/Chitosan oligosaccharide (COS)/Montmorillonite (MMT) hybrid nanofibers were electrospun from their aqueous solution using different Pullulan/COS mass ratios and variable amounts of MMT. The effects of Pullulan/COS mass ratios and MMT contents on the morphologies and properties of PulluIan/COS/MMT hybrid nanofibers were investigated. The obtained nanofibers were characterized with field emission-scanning electron microscopy (FE-SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD), thermo gravimetric analysis (TGA), and tensile strength measurement. The Pullulan/COS mass ratio and MMT contents significantly influence the morphologies and properties of the Pullulan/COS/MMT hybrid nanofibers. Higher Pullulan contents than COS contents forms uniform and bead free nanofibers. The addition of COS to Pullulan improves the thermal stability of Pullulan/COS blend nanofibers. The incorporation of MMT to the Pullulan/COS/MMT hybrid nanofibers increase their fiber diameter, improves their thermal stability and tensile strength. These morphological changes and property enhancement depend on the amount of MMT added. The XRD and TEM results suggest the coexistence of Pullulan, COS and MMT within polymer matrix through intercalation of polymer chain between silicate layers forming well-ordered multiplayer morphology with alternating polymeric and silicate layers.

The optimum conditions for the fabrication of zein/Ag composite nanoparticles from ethanol/H₂O cosolvents using electrospinning and the properties of the composite were investigated. The zein/Ag nanoparticles were characterized using field-emission scanning electron microscopy, transmission electron microscopy (TEM), X-ray diffraction (XRD), and thermogravimetric analysis. The antibacterial activity of the zein/Ag composite nanoparticles was also investigated. The XRD patterns and TEM images indicate the coexistence of a zein matrix and well-distributed Ag nanoparticles.

Almost general poly(vinyl alcohol) (PVA) films were prepared by the processing of a PVA solution. For the first time, a novel poly(vinyl alcohol) (PVA) film was prepared by the saponification of a poly(vinyl acetate) (PVAc) film in a heterogenous medium. Under the same saponification conditions, the influence of saponification time on the degree of saponification (DS) was studied for the preparation of the saponified PVA film, and it was found that the DS varied with time. Optical microscopy was used to confirm the characteristics and surface morphology of the saponified PVA film, revealing unusual black globules in the film structure. The contact angle of the films was measured to study the surface properties, and the results showed that the saponified PVA film had a higher contact angle than the general PVA film. To confirm the transformation of the PVAc film to the PVA film, 1H nuclear magnetic resonance spectroscopy, X-ray diffraction measurements, differential scanning calorimetry, and Fourier-transform infrared spectroscopy were employed.