Search

Improving the stability of electrocatalysts for the oxygen evolution reaction (OER) through materials design has received less attention than improving their catalytic activity. We explored the effect of Mn addition to a cobalt oxide for stabilizing the catalyst by comparing Na-containing CoOx and (Co0.7Mn0.3)Ox films electrodeposited in alkaline solution. The obtained disordered films were classified as layered oxides using X-ray absorption spectroscopy (XAS). The CoOx films showed a constant decrease in the catalytic activity during cycling, confirmed by oxygen detection, while that of (Co0.7Mn0.3)Ox slightly increased as measured by electrochemical metrics. These trends were rationalized based on XAS analysis of the metal oxidation states, which were Co2.8+ and Mn3.7+ near the surface after cycling. Thus, adding Mn to CoOx successfully stabilized the catalyst material and its activity during OER cycling. The development of stabilization approaches is essential to extend the durability of OER catalysts., Comment: arXiv admin note: text overlap with arXiv:2010.06957

This article reports on studies of chlorine-substituted MAPbI3 using combined temperature-dependent XRD synchrotron and Pb-L3 edge EXAFS to analyze the anharmonicity of the lead halide bond. The EXAFS parameters were described in the orthorhombic phase by an Einstein or T2 type behavior, which was then compared with the experimental EXAFS parameters of the tetragonal/cubic phase. In the orthorhombic phase, it was observed that the asymmetry of the pair distribution function (cumulant C3) in MAPbCl3 is much lower than in MAPbI3. Compared with the behavior in the orthorhombic phase, the anharmonicity changed after the phase transition to the room temperature phase, with MAPbCl3 showing an increased anharmonicity and MAPbI3 a decrease. The differences between MAPbI3 and 2% chlorine substitution were small, both in the orthorhombic and tetragonal phases. By determining the structural parameters required to convert the effective force constants k0 and k3 resulting from the EXAFS analysis into the Morse potential parameters {\alpha} and D, we could establish that our results agree with other experimental findings. Moreover, by using XRD we found that the [PbX6] octahedra shrink slightly in the tetragonal phase of MAPbI3 and MAPbI2.94Cl0.06, towards increasing temperatures. This behavior in the tetragonal phase is related to the dominant negative tension effects observed by EXAFS.

The requirements for beneficial materials restructuring into a higher performance OER electrocatalyst are still a largely open question. Here we use Erythrite (Co$_3$(AsO$_4$)$_2\cdot$8H$_2$O) as a Co-based OER electrocatalyst to evaluate its catalytic properties during in-situ restructuring into an amorphous Co-based catalyst in four different electrolytes at pH 7. Using diffraction, microscopy and spectroscopy, we observed a strong effect in the restructuring kinetics depending of the anions in the electrolyte. Only carbonate electrolyte could activate the catalyst electrode, which we relate to its slow restructuring kinetics. While its turnover frequency (TOF) reduced from 2.84 O$_2$ Co$^{-1}$ s$^{-1}$ to a constant value of 0.10 O$_2$ Co$^{-1}$ s$^{-1}$ after 300 cycles, the number of redox active sites continuously increased, which explained the current increase of around 100%. The final activated material owns an adequate local order, a high Co oxidation state and a high number of redox-active Co ions, which we identify as the trinity for enhancing the OER activity. Thus, this work provides new insights into for the rational design of high-performance OER catalysts by electrochemical restructuring.

Manganese oxides have received much attention over the years among the wide range of electrocatalysts for the oxygen evolution reaction (OER) due to their low toxicity, high abundance and rich redox chemistry. While many previous studies focused on the activity of these materials, a better understanding of the material transformations relating to activation or degradation is highly desirable, both from a scientific perspective and for applications. We electrodeposited Na-containing MnOx without long-range order from an alkaline solution to investigate these aspects by cyclic voltammetry, scanning electron microscopy and x-ray absorption spectroscopy at the Mn-K and Mn-L edges. The pristine film was assigned to a layered edge-sharing Mn3+/4+ oxide with Mn-O bond lengths of mainly 1.87 {\AA} and some at 2.30 {\AA} as well as Mn-Mn bond lengths of 2.87 {\AA} based on fits to the extended x-ray fine structure. The decrease of the currents at voltages before the onset of the OER followed power laws with three different exponents depending on the number of cycles and the Tafel slope decreases from 186 \pm 48 to 114 \pm 18 mV dec-1 after 100 cycles, which we interpret in the context of surface coverage with unreacted intermediates. Post-mortem microscopy and bulk spectroscopy at the Mn-K edge showed no change of the microstructure, bulk local structure or bulk Mn valence. Yet, the surface region of MnOx oxidized toward Mn4+, which explains the reduction of the currents in agreement with literature. Surprisingly, we find that MnOx reactivates after 30 min at open-circuit (OC), where the currents and also the Tafel slope increase. Reactivation processes during OC are crucial because OC is unavoidable when coupling the electrocatalysts to intermittent power sources such as solar energy for sustainable energy production., Comment: Author Version

The hybrid halide perovskites MAPbI$_{3}$, MAPbI$_{2.94}$Cl$_{0.06}$, and MAPbCl$_{3}$ (MA - methylammonium) have been investigated using inelastic and quasielastic neutron scattering (QENS) with the aim of elucidating the impact of chloride substitution on the rotational dynamics of MA. In this context, we discuss the influence of the inelastic neutron scattering caused by low-energy phonons on the QENS resulting from the MA rotational dynamics in MAPbI$_{3-x}$Cl$_{x}$. Through a comparative temperature-dependent QENS investigation with different energy resolutions, which allow a wide Fourier time window, we achieved a consistent description of the influence of chlorine substitution in MAPbI$_{3}$ on to the MA dynamics. Our results show that chlorine substitution in the low temperature orthorhombic phase leads to a weakening of the hydrogen bridge bonds since the characteristic relaxation times of C$_{3}$ rotation at 70 K in MAPbCl$_{3}$ (135 ps) and MAPbI$_{2.94}$Cl$_{0.06}$ (485 ps) are much shorter than in MAPbI$_{3}$ (1635 ps). For the orthorhombic phase, we obtained the activation energies from the temperature-dependent characteristic relaxation times ${\tau}$C$_{3}$ by Arrhenius fits indicating lower values of E$_{a}$ for MAPbCl$_{3}$ and MAPbI$_{2.94}$Cl$_{0.06}$ compared to MAPbI$_{3}$. We also performed QENS analyses at 190 K for all three samples. Here we observed that MAPbCl$_{3}$ shows slower MA rotational dynamics than MAPbI$_{3}$ in the disordered structure., Comment: Corrected typos in Title and Abstract (

Single crystals of the methylammonium (MA) lead halides MAPbI3, MAPbBr3, and MAPbCl3 have been investigated using infrared spectroscopy with the aim of analyzing structural and dynamical aspects of processes that enable the ordering of the MA molecule in the orthorhombic crystal structure of these hybrid perovskites. Our temperature-dependent studies were focused on the analysis of the CH/NH rocking, C-N stretching, and CH/NH bending modes of the MA molecule in the 800-1750 cm-1 frequency range. They deliver a direct comparison of the behavior of the three halides on crossing the orthorhombic-tetragonal phase transition in MA lead halide single crystals. Drastic changes of all vibrational modes close to the phase transition were clearly observed. Additional spectral features that were not discussed previously are pointed out. The transformation of the 2-dimensional orthorhombic hydrogen bond layers into a more 3-dimensional arrangement in the tetragonal phase seems to be an important feature providing deeper insight into the mechanisms that lead to a free-rotating MA molecule in the inorganic host structure. The change of the molecules site symmetry in the tetragonal crystal structure seems to be an important feature of the orthorhombic-tetragonal phase transition. For low temperatures it can be stated that the iodide is stronger influenced by hydrogen bonding than the bromide and the chloride.