Search

Large single crystals of rare-earth calcium oxoborates R Ca 4 O (BO 3) 3 with R = Er , Y, Dy, Gd, Sm, Nd, La (R C O B) were grown by the Czochralski method. Complete sets of dielectric, piezoelectric stress, and elastic stiffness coefficients of the R C O B crystal species were determined at ambient conditions using a combination of resonant ultrasound spectroscopy and the substitution method. The results are inherently consistent and reveal clear crystal chemical trends, with the size of the trivalent cation playing an important role. In particular, the longitudinal and shear aggregate elastic stiffnesses, c 11 iso and c 44 iso , decrease from about 165 to 154 GPa and, respectively, 45 to 41 GPa from the smallest to the largest R 3 + cation of the investigated crystal species, while the dielectric coefficients ϵ 22 and ϵ 33 increase. However, the maximum longitudinal piezoelectric effect peaks with 8.6 pCN − 1 at N d C O B , the species where the radius of R 3 + best matches the one of Ca 2 + . Increasing differences in the size of R 3 + and Ca 2 + lead to anisotropic stresses in the crystal lattice, which are partially relaxed by an increasing degree of cation disorder. [ABSTRACT FROM AUTHOR]

Large single crystals of GdCa4O(BO3)3 (space group Cm) were grown by the Czochralski method. Dielectric, piezoelectric and elastic coefficients at room temperature as well as specific heat capacity, thermal expansion and cation disorder were studied employing a variety of methods including resonant ultrasound spectroscopy, differential scanning calorimetry, dilatometry and X-ray diffraction techniques. The electromechanical parameters (4 dielectric, 10 piezoelectric and 13 elastic stiffness coefficients) obtained on different samples are in excellent agreement indicating high internal consistency of our approach, whereas the values reported in literature differ significantly. The elastic behaviour of GdCa4O(BO3)3 resembles the one of structurally related fluorapatite, i.e. the elastic anisotropy is relatively small and the longitudinal effect of the deviations from Cauchy-relations exhibit a pronounced minimum along the direction of the dominating chains of cation polyhedra. GdCa4O(BO3)3 exhibits a maximum longitudinal piezoelectric effect of 7.67 × 10−12 CN−10, a value in the order of that of langasite-type materials. Significant changes of the calcium/gadolinium distribution on the 3 independent cation sites accompanied by characteristic anomalies of heat capacity and thermal expansion suggest processes of nonconvergent cation ordering above about 900 K in GdCa4O(BO3)3. [ABSTRACT FROM AUTHOR]

Large single crystals of GdCa4O(BO3)3 (space group Cm) were grown by the Czochralski method. Dielectric, piezoelectric and elastic coefficients at room temperature as well as specific heat capacity, thermal expansion and cation disorder were studied employing a variety of methods including resonant ultrasound spectroscopy, differential scanning calorimetry, dilatometry and X-ray diffraction techniques. The electromechanical parameters (4 dielectric, 10 piezoelectric and 13 elastic stiffness coefficients) obtained on different samples are in excellent agreement indicating high internal consistency of our approach, whereas the values reported in literature differ significantly. The elastic behaviour of GdCa4O(BO3)3 resembles the one of structurally related fluorapatite, i.e. the elastic anisotropy is relatively small and the longitudinal effect of the deviations from Cauchy-relations exhibit a pronounced minimum along the direction of the dominating chains of cation polyhedra. GdCa4O(BO3)3 exhibits a maximum longitudinal piezoelectric effect of 7.67 × 10−12 CN−10, a value in the order of that of langasite-type materials. Significant changes of the calcium/gadolinium distribution on the 3 independent cation sites accompanied by characteristic anomalies of heat capacity and thermal expansion suggest processes of nonconvergent cation ordering above about 900 K in GdCa4O(BO3)3. [ABSTRACT FROM AUTHOR]

Large single crystals of GdCa4O(BO3)3 (space group Cm) were grown by the Czochralski method. Dielectric, piezoelectric and elastic coefficients at room temperature as well as specific heat capacity, thermal expansion and cation disorder were studied employing a variety of methods including resonant ultrasound spectroscopy, differential scanning calorimetry, dilatometry and X-ray diffraction techniques. The electromechanical parameters (4 dielectric, 10 piezoelectric and 13 elastic stiffness coefficients) obtained on different samples are in excellent agreement indicating high internal consistency of our approach, whereas the values reported in literature differ significantly. The elastic behaviour of GdCa4O(BO3)3 resembles the one of structurally related fluorapatite, i.e. the elastic anisotropy is relatively small and the longitudinal effect of the deviations from Cauchy-relations exhibit a pronounced minimum along the direction of the dominating chains of cation polyhedra. GdCa4O(BO3)3 exhibits a maximum longitudinal piezoelectric effect of 7.67 × 10−12 CN−10, a value in the order of that of langasite-type materials. Significant changes of the calcium/gadolinium distribution on the 3 independent cation sites accompanied by characteristic anomalies of heat capacity and thermal expansion suggest processes of nonconvergent cation ordering above about 900 K in GdCa4O(BO3)3. [ABSTRACT FROM AUTHOR]

Large single crystals of GdCa4O(BO3)3 (space group Cm) were grown by the Czochralski method. Dielectric, piezoelectric and elastic coefficients at room temperature as well as specific heat capacity, thermal expansion and cation disorder were studied employing a variety of methods including resonant ultrasound spectroscopy, differential scanning calorimetry, dilatometry and X-ray diffraction techniques. The electromechanical parameters (4 dielectric, 10 piezoelectric and 13 elastic stiffness coefficients) obtained on different samples are in excellent agreement indicating high internal consistency of our approach, whereas the values reported in literature differ significantly. The elastic behaviour of GdCa4O(BO3)3 resembles the one of structurally related fluorapatite, i.e. the elastic anisotropy is relatively small and the longitudinal effect of the deviations from Cauchy-relations exhibit a pronounced minimum along the direction of the dominating chains of cation polyhedra. GdCa4O(BO3)3 exhibits a maximum longitudinal piezoelectric effect of 7.67 × 10−12 CN−10, a value in the order of that of langasite-type materials. Significant changes of the calcium/gadolinium distribution on the 3 independent cation sites accompanied by characteristic anomalies of heat capacity and thermal expansion suggest processes of nonconvergent cation ordering above about 900 K in GdCa4O(BO3)3. [ABSTRACT FROM AUTHOR]

The full sets of elastic constants (considering piezoelectric effect, i.e., taking into account piezoelectric coupling effects) and piezoelectric stress constants of five natural tourmaline single crystals of different chemical composition have been determined from room temperature up to ∼900 K employing resonant ultrasound spectroscopy. Further, the coefficients of thermal expansion were studied in a wide temperature range from 100 K to 950 K. Electron microprobe analysis showed that the chemical composition of investigated samples varied over a wide range, which allows to study the compositional dependence of thermal, elastic, and piezoelectric properties of tourmalines. At room temperature, the piezoelectric constants of tourmalines were found at-least 1.5 times higher than that for α-quartz. Importantly, we find that the application of tourmaline at temperatures up to its decomposition temperature is not limited by phase transitionsor any ultrasound dissipation effects. [ABSTRACT FROM AUTHOR]

Coefficients of elastic stiffnesses and thermal expansion of hot isostatically pressed, reaction‐sintered and technical fused‐mullite ceramics were measured between 100 and 1673 K in comparison with single crystal mullite employing resonant ultrasound spectroscopy and dilatometry, respectively. Additionally, chemical and phase compositions and the microstructure of the ceramics were studied using X‐ray diffraction techniques and scanning electron microscopy. Our studies revealed that despite polycrystallinity and slight porosity of up to 1.6%, the elastic behavior of the hot isostatically pressed ceramics is near to ideal aggregate elastic properties of mullite single crystal, for example, their bulk moduli fit within 0.7% to B = 170.0 GPa of single crystal mullite. On the other hand, with B = 155 GPa, the reaction‐sintered mullite behaves significantly softer. The difference can be explained with more tight grain to grain contacts in hot isostatically pressed ceramics as compared to reaction‐sintered materials. The thermal expansion of both types of ceramics almost coincides with the corresponding averaged behavior of single crystal mullite. For example, between 573 and 1273 K, the volume expansion coefficients of all these materials are (18.0 ± 0.3)·10−6 K−1. Obviously, the microstructural features are less important for the macroscopic thermal expansion. Due to heterogeneous microstructure and high α‐alumina and zirconia contents, the corresponding properties of fused‐mullite refractory deviate strongly from those of the other mullite materials. [ABSTRACT FROM AUTHOR]

Our numerical modelling of the Czochralski growth of single crystalline β-Ga2O3 crystals (monoclinic symmetry) starts at the 2D heat transport analysis within the crystal growth furnace, proceeds with the 3D heat transport and fluid flow analysis in the crystal-melt-crucible arrangement and targets the 3D thermal stress analysis within the β-Ga2O3 crystal. In order to perform the stress analysis, we measured the thermal expansion coefficients and the elastic stiffness coefficients in two samples of a β-Ga2O3 crystal grown at IKZ. Additionally, we analyse published data of β-Ga2O3 material properties and use data from literature for comparative calculations. The computations were performed by the software packages CrysMAS, CGsim, Ansys-cfx and comsol Multiphysics. By the hand of two different thermal expansion data sets and two different crystal orientations, we analyse the elastic stresses in terms of the von-Mises stress. [ABSTRACT FROM AUTHOR]