Here, piezoelectric transducers consisting of a P(VDF-TrFE) layer with either silver or PEDOT:PSS screen-printed electrodes are studied. The influence of electrodes on the dielectric and electroacoustic properties are studied in dielectric-spectroscopy and ferroelectric-hysteresis measurements. Only when both the bottom and the top electrodes are made of silver, the typical dielectric relaxation of the P(VDF-TrFE) layer is clearly observed. When one or two of the electrodes are of PEDOT:PSS, a Debye-like relaxation is present. Compared with silver electrodes, PEDOT:PSS electrodes allow for moderate self-healing. Consequently, samples with bottom and top PEDOT:PSS electrodes can be poled to saturation, while samples with silver electrodes can hardly be poled to saturation due to destructive electric breakdown. Acoustic transducer measurements show that silver electrodes facilitate higher and broader frequency operation, while PEDOT:PSS electrodes bring slightly lower total harmonic distortion. Overall, the acoustic performance shows no significant deviations between differently electroded samples so that silver electrodes do not offer any advantages for the transducers studied here due to their much higher tendency for destructive electric breakdown.

The semiconducting properties of a bithiophene-naphthalene diimide copolymer (PNDIT2) prepared by Ni-catalyzed chain-growth polycondensation (P1) and commercially available N2200 synthesized by Pd-catalyzed step-growth polycondensation were compared. Both polymers show similar electron mobility of [similar]0.2 cm2 V−1 s−1, as measured in top-gate OFETs with Au source/drain electrodes. It is noteworthy that the new synthesis has several technological advantages compared to traditional Stille polycondensation, as it proceeds rapidly at room temperature and does not involve toxic tin-based monomers. Furthermore, a step forward to fully printed polymeric devices was achieved. To this end, transistors with PEDOT:PSS source/drain electrodes were fabricated on plastic foils by means of mass printing technologies in a roll-to-roll printing press. Surface treatment of the printed electrodes with PEIE, which reduces the work function of PEDOT:PSS, was essential to lower the threshold voltage and achieve high electron mobility. Fully polymeric P1 and N2200-based OFETs achieved average linear and saturation FET mobilities of >0.08 cm2 V−1 s−1. Hence, the performance of n-type, plastic OFET devices prepared in ambient laboratory conditions approaches those achieved by more sophisticated and expensive technologies, utilizing gold electrodes and time/energy consuming thermal annealing and lithographic steps. Dieser Beitrag ist aufgrund einer (DFG-geförderten) Allianz- bzw. Nationallizenz frei zugänglich.