Search

In this work, the effect of the modification by laser ablation of hydroxyapatite surfaces synthesized by sol-gel on the capacity of apatite formation by in vitro tests was analyzed. For this, layers of sodium titanate were grown on disks of the Ti6Al4V alloy by immersion in 10 M NaOH at 60 ° C for 24 hours. The hydroxyapatite coatings were then prepared using calcium nitrate tetrahydrate and triethyl phosphite as precursors by the sol-gel method and the dip-coating technique. Finally, patterning was performed by means of an Nd: YAG laser, with working energy of 1.3 mJ. Hydroxyapatite was evaluated and characterized using X-Ray Diffraction, Scanning Electron Microscopy and Dispersive X-ray Energy Spectroscopy techniques. In order to evaluate the reactivity, immersion in simulated body fluid was carried out and calcium atomic absorption analysis was carried out to observe the dissolution and precipitation phenomena of this ion, and it was determined that the samples treated at 600 ° C They induced a better response to the growth of apatites, however, all the coatings have characteristics that would allow these coatings to be used as implants in bone substitutes., En este trabajo se analizó el efecto que tiene la modificación por ablación laser de superficies de hidroxiapatita sintetizados por sol gel en la capacidad de formación de apatitas mediante ensayos in vitro. Para ello se crecieron capas de titanato de sodio sobre discos de la aleación de Ti6Al4V mediante inmersión en NaOH 10 M a 60ºC durante 24 horas. Luego se prepararon los recubrimientos de hidroxiapatita utilizando como precursores el nitrato de calcio tetrahidratado y el trietil fosfito por el método sol-gel y la técnica dip-coating. Finalmente se realizó un patronamiento por medio de un láser Nd: YAG, con una energía de trabajo de 1.3 mJ. La hidroxiapatita se evaluó y caracterizó empleando las técnicas de Difracción de Rayos X, Microscopía Electrónica de Barrido y Espectroscopía de Energía Dispersiva de rayos x. Con el fin de evaluar la reactividad de las superficies se realizó una inmersión en fluido corporal simulado y se llevó a cabo análisis de absorción atómica de calcio, para observar los fenómenos de disolución y precipitación de este ion, y se determinó que las muestras tratadas a 600°C indujeron una mejor respuesta al crecimiento de apatitas, sin embargo, todos los recubrimientos presentan características que permitirían que estos recubrimientos sean usados como implantes en sustitutos óseos.

Corrosion behavior on galvanized steel sheets, immersed in solutions with different concentrations of NaCl and Na2SO4 was studied. The steel sheets were immersed using an elevator, in order to simulate an atmosphere, wherein the sheets were always interacting with corrosive medium. The degradation was evaluated by electrochemical impedance spectroscopy and potentiodynamic curves. The morphology of surface was analyzed by scanning electron microscopy and the composition of the corrosion products was determined by EDX and XRD. The results after 30 days showed that the corrosion potential increased with the time, confirming the formation of passive products on the surface; corrosion rate also increased, causing pitting corrosion. For the first few days of exposure, generalized corrosion was observed as a result of compounds passive, porous nature and white., Se estudió el comportamiento de la corrosión en láminas de acero galvanizado, inmersas en soluciones con diferentes concentraciones de NaCl y Na2SO4. Las láminas de acero se sumergieron empleando un elevador de muestras, con el fin de simular una atmosfera, donde las láminas estuvieran siempre interactuando con el medio corrosivo. El deterioro del galvanizado se evaluó mediante espectroscopia de impedancia electroquímica y curvas potenciodinámicas. La morfología del ataque se analizó por microscopía electrónica de barrido y la composición de los productos de corrosión se determinó por EDX y DRX. Los resultados tras 30 días mostraron que el potencial de corrosión del galvanizado aumentó en el tiempo, lo que corrobora la formación de productos pasivos sobre la superficie; la velocidad de corrosión también aumentó, originando corrosión por picado. Para los primeros días de exposición se obtuvo una corrosión generalizada como consecuencia de productos, de naturaleza pasiva, porosa y de color blanco.