Search

Abstract The inhibition efficiency and adsorption affinity were investigated for two novel compounds, namely: 6-methoxy-2-naphthyl-[2, 2’-bithiophene]-5-carboxamidine hydrochloride salt (MA-1440) and 5'-(4-chlorophenyl)-2, 2’-bifuran-5-carboxamidine hydrochloride salt (MA-1456). The inhibition study was conducted on carbon steel surface in 1.0 M HCl with different inhibitor doses and different temperature levels, to investigate the optimum dose and preferable temperature. The performed investigation included chemical, electrochemical, instrumental, and quantum computation techniques. A chemical technique was accomplished by using weight-loss measurements. Different factors were studied using weight-loss measurements in order to reach the maximum inhibition efficiency. The adsorption study revealed that the examined inhibitors obey the Langmuir adsorption isotherm and are chemically adsorbed on the steel surface. The electrochemical measurements were accomplished through the electrochemical impedance (EIS) and potentiodynamic polarization (PDP) techniques. Based on the electrochemical measurements, the examined compounds were categorized as mixed inhibitors. The instrumental examination using different techniques namely: scanning electron microscope (SEM), energy dispersive X-ray (EDX), Fourier-transform infrared spectroscopy (FT-IR), and X-ray photoelectron spectroscopy (XPS) confirmed that the considered inhibitors are excellently adsorbed over the carbon steel surface. The extent of the adsorption affinity of these compounds on the carbon steel surface was studied theoretically using quantum computations and Monte Carlo simulation. The theoretical investigation results of quantum chemistry were validated with those obtained by chemical and electrochemical methodologies. All investigations prove that, the tested compounds were adsorbed chemically on the steel surface and achieved maximum inhibition efficiency of, 94.69% and 90.85% for M-1440 and MA-1456, respectively, at the optimum concentration 30 $$\times$$ × 10–6 mol L−1 and temperature 328 K.

Abstract Aluminum corrosion inhibitors “{[CuI (CN)2(phen) CuII (CN)2(phen)]5H2O},(MOF1) and {[CuI(CN)2(phen)CuII(CN)2(phen)]5H2O}@TiO2 (MOF1@TiO2) were studied in one molar HCl solution”. The ML results for three different temperatures (25–45 °C) were compared with the results of PDP and EIS analyses. The adsorption of inhibitors on Al surfaces has been calculated and discussed by a Langmuir isotherm. The inhibitors that were created showed great effectiveness, with a noticeable increase in their inhibitory efficiency as the dosage was raised and the temperature was lowered. Inhibition efficiency each amounted to 88.6%, 84.5% at 400 ppm and 25 °C for MOF1@TiO2 and MOF1, respectively. Analyzing the polarization curves of synthesized inhibitors revealed that they were mixed-type inhibitors. Al was found to be surface inhibited when coated with a thin film of inhibitors, and “Al's surface morphology was assessed by different techniques such as scanning electron microscopy (SEM), energy dispersive X-ray (EDX) and atomic force microscope (AFM)”. “Theoretical models like quantum chemical and molecular dynamics simulation authenticated the experimental observation”. The MOFs exhibit exceptional corrosion resistance against Al when exposed to acidic environments, according to several tests.

The effect of the SCPs-[CuII(en)2] [CuI (CN)2]2. H2O] (SCP1) and {[H2DAB] [Cu4(CN)6].2H2O} (SCP2) as corrosion inhibitors for carbon steel (CS) was studied in 1.0M HCl solution. As the synthesized inhibitor dose increases, the inhibition productivity (%e) increases reaching to 90.3% and 89.9% at 21x10-6M dose for SCP2 and SCP1, respectively. This result evidenced by mass loss (ML) investigated at three different temperatures 25-35-45oC, while potentiodynamic polarization (PP), electrochemical impedance spectroscopy (EIS), and electrochemical frequency modulation technique (EFM) were tested at 25°C. The synthesized inhibitors adsorbed on the CS surface physically allowing Henry isotherm. The results displayed that the synthesized inhibitors are excellent and their (%e) was significantly increased by raising the dose and decreased by raising the temperature. Polarization curves revealed that the synthesized inhibitors act as mixed type. The thermodynamic parameters were calculated and discussed. The protection was confirmed by the creation of the thin film of inhibitors precipitated on the surface of CS.

Abstract The effects of [Co2 (SCN) 4(hmt)2(H2O)6. H2O] (SC1) and [Co (CN)6 (Me3Sn)3(H2O). (qox)] (SCP2) MOF as corrosion inhibitors on C-steel in 0.5 M sulfuric acid solutions are illustrated utilizing mass reduction (MR), electrochemical [potentiodynamic polarization (PP), and AC electrochemical impedance (EIS)]. The experiments revealed that as the dose of these compounds rose, the inhibition efficacy (IE percent) of C-steel corrosion improved, reaching 80.7–93.1% at dose 25 × 10−6 M for SC1 and SCP2, respectively. IE percent, on the other hand, dropped as the temperature range grew. SC1was adsorbed physically and chemically (mixed adsorption) but SCP2 was adsorbed physically on the surface of C-steel and conformed to the Langmuir adsorption isotherm equation. The PP studies revealed that these compounds act as mixed kind inhibitors. To establish the morphology of the inhibited C-steel surface, scanning electron microscopy (SEM), energy transmitted X-ray (EDX), and atomic force microscopy (AFM) studies were used. All tested experiments were in good agreement.