Search

Single-purpose greenhouse films such as UV-blocking, NIR-blocking, or ultrathermic films are commonly developed in various climate regions. However, multifunctional films of combined functions are rarely explored, especially in the tropical regions. In this research, a multifunctional film having high UV filtration, high NIR reflection, and good light diffusion was developed for a greenhouse cover application in tropical regions. Effects of type, quantity, and particle size of additives on optical properties (280–2500 nm) and mechanical properties of 3-layer laminated films comprising 90% LLDPE/10% EVA polymer matrix and additives were studied. Results show that properties of those films are adjustable by varying types, particle size, and content of additives. The UV transmission of the film was ranged from 13.7 to 32.7 %T, NIR reflection from 12.1 to 19.8 %R, and %haze diffusion from 39.5 to 72.3 where photosynthetically active radiation (PAR) transmission was in the range of 62.6–78.9 %T. Those films exhibit tensile strength of 18–24 MPa, modulus of elasticity of 200–280 MPa, and elongation at break of 610–810%. A field test of the newly developed films as a cover for a greenhouse of 6 m wide ×24 m long ×4.3 m high with double roof design showed a better quality of plant growth in terms of weight, height, and bush width compared to a 7% UV absorber commercial film.

Multi-branched poly(D-lactide)s (mbPDLAs) with various structures are synthesized via ring-opening polymerization by using polyglycidol (PG) macro-initiators. Their chemical structures and thermal properties are controlled by adjusting feed ratios of D-lactide (DLA) and PG. The materials are blended with commercial linear poly(L-lactide)(l-PLLA) to form a stereocomplex structure. Effects of mbPDLAs structures and l-PLLA/mbPDLA ratios on the blends’ thermal, mechanical, and rheological properties are evaluated. Mechanical properties of the stereocomplex blends, especially elongation at break and toughness, are dependent on the blend compositions, in which a 90:10 ratio exhibits the most desirable properties. The material also exhibits the lowest complex viscosity, which provides easy processing conditions. This is achieved by the incorporation of copolymers with multi-branched structures and an ability to form a much stronger stereocomplex structure.

A composite of 70/30 poly(lactic acid)/hydroxyapatite was systematically prepared using various amounts of glycidyl methacrylate as reactive compatibilizer or Joncryl ADR®-4368 containing nine glycidyl methacrylate functions as a chain extension/branching agent to improve the mechanical and biological properties for suitable usage as internal bone fixation devices. The effect of glycidyl methacrylate/Joncryl on mechanical properties of poly(lactic acid)/hydroxyapatite was investigated through flexural strength. Cell proliferation and differentiation of osteoblast-like MC3T3-E1 cells cultured on the composite samples were determined by Alamar Blue assay and alkaline phosphatase expression, respectively. Result shows that flexural strength tends to decrease, as glycidyl methacrylate content increases except for 1 wt.% glycidyl methacrylate. With an addition of dicumyl peroxide, the flexural strength shows an improvement than that of without dicumyl peroxide probably due to the chemical bonding of the hydroxyapatite and poly(lactic acid) as revealed by FTIR and NMR, whereas the composite with 5 wt.% Joncryl shows the best result, as the flexural strength increases getting close to pure poly(lactic acid). The significant morphology change could be seen in composite with Joncryl where the uniform agglomeration of hydroxyapatite particles oriented in poly(lactic acid) matrix. Addition of the epoxy functional compatibilizers at suitable percentages could also have benefits to cellular attachment, proliferation, differentiation and mineralization. So that, this poly(lactic acid)/hydroxyapatite composite could be a promising material to be used as internal bone fixation devices such as screws, pins and plates.