Samples of dolomite ore washed with 8% HCl and unwashed, were mixed with reagent grade titanium oxide (TiO2, 99.78%) in stoichiometric amounts and were put to react in an oven at a temperature of 1150 °C with residence times of 8, 12 and 24 hours. The chemical analysis of dolomite was carried out with an x-ray fluorescence equipment. A thermodynamic study was carried out to evaluate the feasibility of obtaining calcium titanate and magnesium titanate. The powders obtained from the calcination reaction were characterized using X-ray diffraction (XRD). The calcium titanate compound was formed with the washed dolomite from 8 hours of treatment, it presents an orthorhombic structure. The magnesium titanate is the predominant phase in the samples of the unwashed dolomite with a treatment of 12 hours of permanence., Muestras de mineral de dolomita lavada con HCl al 8% y sin lavar, se mezclaron con óxido de titanio grado reactivo (TiO2, 99.78%) en cantidades estequiométricas y fueron puestas a reaccionar en un horno a una temperatura de 1150 °C con tiempos de permanencia de 8, 12 y 24 horas. El análisis químico de la dolomita se realizó con un equipo de fluorescencia de rayos x. Se hizo un estudio termodinámico para evaluar la factibilidad de obtener titanato de calcio y titanato magnesio. Los polvos obtenidos de la reacción de calcinación se caracterizaron empleando difracción de rayos x (DRX). El compuesto de titanato de calcio se formó con la dolomita lavada desde 8 horas de tratamiento, este presenta una estructura ortorrómbica El titanato de magnesio es la fase predominante en las muestras de la dolomita sin lavar con un tratamiento de 12 horas de permanencia.