Search

Diffusional limitations associated with zeolite microporous systems can be overcome by developing hierarchical zeolites, i.e., materials with a micro- and mesoporous framework. In this work, Y and ZSM-5 zeolites were modified using a surfactant-mediated hydrothermal alkaline method, with NaOH and cetyltrimethylammonium bromide (CTAB). For Y zeolite, after a mild acidic pretreatment, the effect of the NaOH+CTAB treatment time was investigated. For ZSM-5 zeolite, different concentrations of the base and acid solutions were tested in the two-step pretreatment preceding the hydrothermal treatment. The properties of the materials were studied with different physical–chemical techniques. Hierarchical Y zeolites were characterized by 3.3–5 nm pores formed during the alkaline treatment through the structure reconstruction around the surfactant aggregates. The effectiveness of the NaOH+CTAB treatment was highly dependent on the duration. For intermediate treatment times (6–12 h), both smaller and larger mesopores were also obtained. Hierarchical ZSM-5 zeolites showed a disordered mesoporosity, mainly resulting from the pretreatment rather than from the subsequent hydrothermal treatment. High mesoporosity was obtained when the concentration of the pretreating base solution was sufficiently high and that of the acid one was not excessive. Hierarchical materials can be obtained for both zeolite structures, but the pretreatment and treatment conditions must be tailored to the starting zeolite and the desired type of mesoporosity. [ABSTRACT FROM AUTHOR]

Acid mine drainage (AMD) is one of the main environmental problems associated with mining activity, whether the mine is operational or abandoned. In this work, several precipitates from this mine drainage generated by the oxidation of sulfide minerals, when exposed to weathering, were used as adsorbents. Such AMD precipitates from abandoned Portuguese mines (AGO, AGO-1, CF, and V9) were compared with two raw materials from Morocco (ClayMA and pyrophyllite) in terms of their efficiency in wastewater treatment. Different analytical techniques, such as XRD diffraction (XRD), Fourier Transform Infrared spectroscopy (FTIR), N2 adsorption isotherms, and Scanning Electron Microscopy (SEM) with Energy Dispersive X-ray (EDX) were used to characterize these natural materials. The adsorption properties were studied by optimizing different experimental factors, such as type of adsorbent, adsorbent mass, and dye concentration by the Box–Behnken Design model, using methylene blue (MB) and crystal violet (CV) compounds as organic pollutants. The obtained kinetic data were examined using the pseudo-first and pseudo-second order equations, and the equilibrium adsorption data were studied using the Freundlich and Langmuir models. The adsorption behavior of the different adsorbents was perfectly fitted by the pseudo-second order kinetic model and the Langmuir isotherm. The most efficient adsorbent for both dyes was AGO-1 due to the presence of the cellulose molecules, with qm equal to 40.5 and 16.0 mg/g for CV and MB, respectively. This study confirms the possibility of employing AMD precipitates to adsorb organic pollutants in water, providing valuable information for developing future affordable solutions to reduce the wastes associated with mining activity. [ABSTRACT FROM AUTHOR]

A series of multicomponent oxide catalysts (CuO/ZnO/MemOn/ZrO2/SiO2, with Me = Mg, Ce, or La) was synthesized through a one-pot soft-template approach and used for CO2 hydrogenation to methanol. In the case of the La-containing catalysts, additional samples were prepared with CuO contents in the range 40–60 wt%. The influence of the catalyst composition on the physicochemical properties as well as the effect on the catalytic performance were investigated. The fresh catalysts were characterized in terms of composition, structure, textural properties, dispersion of the oxidic phases, and reducibility. On the reduced samples, structural and acid–base properties were also investigated, as well as specific metal surface area and dispersion of Cu0. After in situ H2-treatment at 250 °C, the catalysts activity was tested in a bench scale plant at 250 °C and 3.0 MPa, using a gas hourly space velocity of 24,000 Ncm3 h−1 gcat−1 and a H2/CO2 molar ratio equal to 3. It was found that the production of methanol is particularly favored by the introduction of La2O3, the highest value of methanol space–time yield (413 mg CH 3 OH h - 1 g cat - 1 ) being obtained on the CuO/ZnO/La2O3/ZrO2/SiO2 catalyst containing 50 wt% of copper oxide. [ABSTRACT FROM AUTHOR]

In this work, we propose two bifunctional nanocomposite catalysts based on acidic mesostructured γ-Al2O3 and a Cu/ZnO/ZrO2 redox phase. γ-Al2O3 was synthesized by an Evaporation-Induced Self-Assembly (EISA) method using two different templating agents (block copolymers Pluronic P123 and F127) and subsequently functionalized with the redox phase using an impregnation method modified with a self-combustion reaction. These nanocomposite catalysts and their corresponding mesostructured supports were characterized in terms of structural, textural, and morphological features as well as their acidic properties. The bifunctional catalysts were tested for the CO2-to-DME process, and their performances were compared with a physical mixture consisting of the most promising support as a dehydration catalyst together with the most common Cu-based commercial redox catalyst (CZA). The results highlight that the most appropriate Pluronic for the synthesis of γ-Al2O3 is P123; the use of this templating agent allows us to obtain a mesostructure with a smaller pore size and a higher number of acid sites. Furthermore, the corresponding composite catalyst shows a better dispersion of the redox phase and, consequently, a higher CO2 conversion. However, the incorporation of the redox phase into the porous structure of the acidic support (chemical mixing), favoring an intimate contact between the two phases, has detrimental effects on the dehydration performances due to the coverage of the acid sites with the redox nanophase. On the other hand, the strategy involving the physical mixing of the two phases, distinctly preserving the two catalytic functions, assures better performances. [ABSTRACT FROM AUTHOR]

Zinc oxide/ and iron oxide/SBA-15 composites were synthesized using the innovative Two-Solvents procedure and tested as sorbents for the mid-temperature (300 °C) removal of hydrogen sulphide, and then compared with a commercial unsupported ZnO sorbent. The sulphur retention capacity results showed the superior performance of the iron oxide/SBA-15 composite (401 mg S g−1 Fe2O3) in comparison with the zinc oxide/SBA-15 composite (53 mg S g−1 ZnO), both these sorbents being much more efficient than the commercial sorbent (6 mg S g−1 ZnO). The different sorption behaviour was discussed in terms of the nature of the nanocomposites where: (i) the mesostructure of the support was retained with a high surface area and pore volume; (ii) the zinc oxide phase was incorporated inside the SBA-15 channels as a thin amorphous homogeneous layer while the iron oxide was dispersed in form of small maghemite crystallites; and (iii) significant interactions occurred between the silica matrix and the zinc oxide phase. Remarkable differences in the regeneration behaviour of the exhaust sorbents were revealed by temperature-programmed experiments under an oxidizing atmosphere. After regeneration, the sorption properties of the zinc oxide/SBA-15 composite appeared to be enhanced compared to the commercial sorbent. Incomplete recovery of the sorption activity was observed for the regenerated iron oxide/SBA-15 sorbent, whose performance remained far better than that of the ZnO-based one, either fresh or regenerated. In view of its higher sulphur retention capacity and appropriate regeneration temperature (T≤ 350 °C), the iron oxide/SBA-15 composite is a promising material for the design of advanced sorbents for a thermally efficient H2S removal process from hot gas streams. [ABSTRACT FROM AUTHOR]

In this study, CeO2, La2O3, and CeO2-La2O3 mixed oxide catalysts with different Ce/La molar ratios were prepared by the soft template method and characterized by different techniques, including inductively coupled plasma atomic emission spectrometry, X-ray diffraction, N2 physisorption, thermogravimetric analysis, and Raman and Fourier transform infrared spectroscopies. NH3 and CO2 adsorption microcalorimetry was also used for assessing the acid and base surface properties, respectively. The behavior of the oxides as catalysts for the dimethyl carbonate synthesis by the transesterification of propylene carbonate with methanol, at 160 °C under autogenic pressure, was studied in a stainless-steel batch reactor. The activity of the catalysts was found to increase with an increase in the basic sites density. The formation of dimethyl carbonate was favored on medium-strength and weak basic sites, while it underwent decomposition on the strong ones. Several parasitic reactions occurred during the transformation of propylene carbonate, depending on the basic and acidic features of the catalysts. A reaction pathway has been proposed on the basis of the components identified in the reaction mixture. [ABSTRACT FROM AUTHOR]