Polycaprolactone scaffolds modified with cross-linked hyaluronic acid were prepared in order to establish whether a more hydrophilic and biomimetic microenvironment benefits the progenitor cells arriving from bone marrow in a cell-free tissue-engineering approach. The polycaprolactone and polycaprolactone/hyaluronic acid scaffolds were characterized in terms of morphology and water absorption capacity. The polycaprolactone and polycaprolactone/hyaluronic acid samples were implanted in a chondral defect in rabbits; bleeding of the subchondral bone was provoked to generate a spontaneous healing response. Repair at 1, 4, 12, and 24 weeks was assessed macroscopically using the International Cartilage Repair Society score and the Oswestry Arthroscopy Score and microscopically using immunohistological staining for collagen type I and type II, and for Ki-67. The presence of hyaluronic acid improves scaffold performance, which supports a good repair response without biomaterial pre-seeding. [ABSTRACT FROM AUTHOR]

Two series of 3D scaffolds based on ε-caprolactone were synthesized. The pore size and architecture (spherical interconnected pores) was the same in all the scaffolds. In one of the series of scaffolds, made of pure ε-polycaprolactone, the volume fraction of pores varied between 60% and 85% with the main consequence of varying the interconnectivity between pores since the pore size was kept constant. The other scaffolds were prepared with copolymers made of a ε-caprolactone-based hydrophobous monomer and hydroxyethyl acrylate, as the hydrophilic component. Thus, the hydrophilicity and, presumably, the adhesion properties varied monotonously in the copolymer series while porosity was kept constant. A suspension of human chondrocytes in culture medium was injected in the 3D scaffolds and cultured in static conditions up to 28 days. SEM and immunofluorescence assays allowed characterizing cells and extracellular matrix inside the scaffolds after different culture times. To do that, cross sections of the scaffolds were observed by SEM and confocal microscopy. The quantity of cells inside the scaffolds decreases with a decrease of the volume fraction of pores, due to the lack of interconnectivity between the cavities. The scaffolds up to a 30% of hydrophilicity behave in a similar way than the hydrophobous; a further increase of the hydrophilicity rapidly decreases cell viability. In all the experiments production of collagen type I, type II, and aggrecan was found, and some cells were Ki-67 positive, showing that some cells are adhered to the pore walls and maintain their dedifferentiated phenotype even when cultured in three-dimensional conditions. [ABSTRACT FROM PUBLISHER]