LHPG method is used to grow high optical quality single crystal fibers. For LHPG, polycrystalline ceramics can play important roles as feedstocks and cladding on the single crystal fibers.

Polycrystalline yttrium–aluminum garnet (YAG) fibers are attractive for high-power lasers and for high-temperature structural materials. Processing methods for

The superior thermal and optical properties of transparent polycrystalline ceramics make them attractive alternatives to glass-based materials for laser gain media. Fibers have other advantages of compactness, vibration-resistance, and reduced cooling requirements. Recently it was found that surface roughness caused by grain boundary grooving dominated optical scattering even though there were other scattering sources in the fiber. Therefore, a lot of effort went to fabrication of fibers with smooth surfaces. A mechanical polishing method for polycrystalline YAG fibers was developed. The fiber surface roughness was reduced, while maintaining a circular cross-section. Surface-polished 1.5% Ho-doped polycrystalline YAG fiber, 62 mm long with 31 μm diameter, was fabricated, and lasing was demonstrated from this fiber. Effects of surface-polishing on the surface roughness and scattering coefficient are presented, and lasing characteristics are discussed.

A polycrystalline 1.5% Ho: YAG fiber with a diameter of 31 µm was prepared. Surface roughness from grain boundary grooving was reduced by polishing, which decreased the fiber scattering coefficient from 76 msup-1/supto 35 msup-1/sup. Lasing tests were done on this fiber with a SF57 Schott glass cladding. Lasing was confirmed by spectrum narrowing with threshold pump power lower than 500 mW and a slope efficiency of 7%. To our knowledge, this is the first lasing demonstration from a small diameter polycrystalline ceramic fiber.