The current study reports the detailed analysis of an observation of the local pinning of a slowly moving austenite-ferrite interface by a single nanosized oxidic particle. The observations were made during an in situ cyclic partial phase transformation experiment on a Fe-0.1C-1.0Mn alloy close to the inversion stage at which the interface migrates at a rather low velocity. The low velocity allowed capturing the interface pinning effect over a period of no less than 16 seconds. From our observations, it was possible to follow the progression of the pinning effect from the initial stages all the way through to the release of the interface. The pinning force exerted by the individual particle having a diameter of 140 nm on the austenite-ferrite interface was estimated as 175 nJ m−1, while the maximum pinning length was approximately 750 nm to either side of the particle, leading to an interface line tension of 170 nJ m−1. The observed pinning behavior is compared with the most relevant models in the literature., Novel Aerospace Materials

Hydrogen embrittlement is shown to proceed through a previously unidentified mechanism. Upon ingress to the microstructure, hydrogen promotes the formation of low-energy dislocation nanostructures. These are characterized by cell patterns whose misorientation increases with strain, which concomitantly attracts further hydrogen up to a critical amount inducing failure. The appearance of the failure zone resembles the "fish eye"associated to inclusions as stress concentrators, a commonly accepted cause for failure. It is shown that the actual crack initiation is the dislocation nanostructure and its associated strain partitioning.

The kinetic behaviour of austenite/ferrite interfaces in a low carbon – 0.5 mass% Mn containing steel during Cyclic Partial Phase Transformation (CPPT) experiments has been investigated using hot stage Transmission Electron Microscopy (TEM). Individual interfaces were observed to display behaviour typical of CPPT experiments as recorded in macroscopic dilatometry experiments and demonstrated i) the “normal”, ii) inverse transformations and iii) a stagnant stage in which the interface migrates at a very low velocity as a result of the interface passing through a Mn enriched zone due to the preceding transformation. The length of the stagnant stage determined from the TEM observations shows excellent agreement with that measured from dilatometry and kinetic modelling, whilst the distance migrated from the interface shows some disparities which are primarily attributed to differences in assumptions about grain geometry and nucleation. No special interface features were observed when the interface changed direction and passed through the previously Mn-enriched zones. General observations on the interaction of the transformation interface with microstructural features are also reported., Green Open Access added to TU Delft Institutional Repository ‘You share, we take care!’ – Taverne project https://www.openaccess.nl/en/you-share-we-take-care Otherwise as indicated in the copyright section: the publisher is the copyright holder of this work and the author uses the Dutch legislation to make this work public., Novel Aerospace Materials