Search

Investigation of materials was initiated in 1990. The first theme was on the durability of materials in the space environment. In 1997 the following subjects were studied. (1) All domestic consumer polyurethane-base adhesives were assessed for use in space, and some products were found to be suitable if performance in outgassing and heat resistance was improved. (2) Influence of temperature on radiation-induced degradation was examined, and heat-control films, flexible reflector and OSR (Optical Solar Reflector) were tested in vacuum under irradiation by electron beams. Temperature difference between 70 C and 140 C had less influence than the difference in the dose rate. (3) For contamination by outgassing, sufficient data were collected. (4) Test data was added to the material database, whose service was to be available within NASDA. (5) Shapes of the collision marks left on MLI (Multi-Layer Insulator) and radiator were studied to evaluate the degradation by exposure to the space environment, and the atomic compositions of space debris were identified to be silicon, carbon, aluminum, calcium and phosphorus., 宇宙環境での材料の耐久性というテーマに始まる材料研究が1990年に始まった。1997年に研究したテーマは次の通りである。(1)日本国内で生産されるポリウレタン接着剤の製品をすべて調べ、ガス漏れや熱耐性が改善されれば宇宙で使用できるものがいくつかあることがわかった。(2)宇宙環境での耐久性について、放射線変性の温度の影響を調べた。電子線の放射光により熱調整フィルムやOSR(光学太陽光反射鏡)が試験され、70度Cと140度Cの温度の差は放射線量の差ほど影響はないことがわかった。(3)ガス漏れによる不純物について、ウレタン塗料でのデータを収集した。(4)材料データベースに新たな試験データが加わった。このデータベースはNASDAから利用・登録が可能である。(5)宇宙環境に露出されることによる変性について、MLI(多層断熱材)やラジエータに残った衝突痕の形状を詳細に調べた。MLIに痕を残した破片の組成は、珪素、炭素、アルミニウム、カルシウム、およびリンと同定された。