Search

The solidification process from emulsion, which consisted of emulsifier, water and molten drug as oil phase without use of any organic solvent, was firstly employed to prepare ultrafine fenofibrate (FF) powder. The effects of stirring speed and volume ratios of hot emulsion to cold water on the particle size and morphology were discussed as well as the impacts of different emulsifiers on emulsion. The produced ultrafine powder was characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD), Fourier transform infrared (FT-IR) spectroscopy, specific surface area analysis and a dissolution test. XRD patterns and FT-IR spectra showed that the ultrafine FF was crystalline powder with the structure and the components similar to those of bulk drug. The product had a mean particle size of about 3 microm with a narrow distribution from 1 microm to 5 microm. The specific surface area reached up to 6.23 m(2)/g, which was about 25 folds as large as that of bulk FF. In the dissolution tests, about 96.1% of ultrafine FF was dissolved after 120 min, while there was only 38.1% of bulk drug dissolved, proving that the dissolution property of ultrafine FF was significantly improved when compared to commercial drug.

Tensile strength is an important material property and usually can be determined experimentally. The strain rate dependent behavior of T300 carbon/epoxy matrix composite was characterized over a wide strain rate range (10×10-5 s-1to10×104s-1). The low to moderate strain rate experiments were carried out on a MTS machine, while the high strain rate experiment was conducted with a split Hopkinson tensile bar. A rate dependent model was introduced to simulate the material response. Two kinds of stacking sequence of composite specimens [(45/-45)4]s and [(0/45/90/-45)2]s were tested at different strain rates, and the results were used to determine parameters of the model. The predictions of the model showed to agree fairly well with the experimental results. The tensile strength and initial elastic modulus of the composites increase when the strain rate increases.

Ultrafine gemfibrozil (GEM) was prepared by reactive precipitation process in which methyl cellulose (MC) was employed to inhibit the growth and the agglomeration of particles. The impact of NaOH concentrations on bulk GEM consumption was explored. The effects of H2SO4 concentrations and the drying methods on the particle size and morphology were also discussed. The produced ultrafine powders were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD), Fourier transform infrared (FT-IR) spectroscopy, specific surface area analysis and dissolution test. XRD patterns and FT-IR spectra showed that the as-obtained ultrafine GEM was a crystalline powder with the structure and components similar to those of bulk GEM. The ultrafine GEM had a mean particle size of about 1.25 microm with a narrow distribution from 0.6 to 3 microm. The specific surface area reached up to 11.01 m2/g, which was about 6 times as large as that of bulk GEM. In the dissolution tests, about 91.2% of ultrafine GEM was dissolved after 120 min, while there was only 23.6% of bulk GEM dissolved, proving that the dissolution property of ultrafine GEM was significantly enhanced when compared to commercial GEM owing to a decreased particle size and an increased specific surface area.