Search

WOS: 000453906100006, Conductive poly(o-toluidine)/kaolinite composite was synthesized via chemical polymerization of o-toluidine in the availability of kaolinite using ammonium persulfate as oxidizing agent. To investigate the use of the prepared conductive composite as humidity and temperature sensor, the effect of polymerization conditions such as HCl, o-toluidine and oxidant concentrations on the amount of conductive POT contained in the composite and the conductivity values of composites were investigated. It was found that the composites with the highest poly(o-toluidine) content (29.4%) and conductivity (8.3x10(-4) Scm(-1)) were obtained by 0.2 M ammonium persulfate, 0.4 M o-toluidine and 1 M hydrochloric acid for 2 hours of continuous polymerization at 20 degrees C. The resistivity values of pure poly(o-toluidine) and poly (o-toluidine)/kaolinite composite were monitored during heatingcooling cycles in the range of 0-100 degrees C. Changes in resistivity for pure poly(o-toluidine) and poly(o-toluidine)/kaolinite composite with humidity 30-90% were examined and humidity sensor behavior was determined. Characterization of the prepared composite was performed by Fourier transform infrared spectroscopy (FT-IR), X-ray diffraction (XRD), thermogravimetric analysis (TGA) and scanning electron microscopy techniques (SEM)., Turkish Scientific and Technical Research Organization (TUBITAK) [107M542], This work was supported by Turkish Scientific and Technical Research Organization (TUBITAK) project numbered as 107M542.

İletken poli(o-toluidin)/kaolinit kompoziti,kaolinit varlığında yükseltgen olarak amonyum persülfat kullanılarako-toluidinin kimyasal polimerizasyonu ile hazırlandı. Hazırlanan iletkenkompozitin nem ve sıcaklık algılayıcısı olarak kullanımını araştırabilmek içinkompozitin içerdiği iletken POT miktarı ve kompozitin iletkenlik değerlerinepolimerizasyon koşullarından HCl, o-toluidin ve yükseltgen madde derişimlerininetkisi incelendi. En yüksek poli(o-toluidin) miktarı (%29.4) ve iletkenliğesahip (8.3×10-4 Scm-1) kompozitin 0.2 M amonyumpersülfat, 0.4 M o-toluidin ve 1.0 M hidroklorik asit kullanılarak 20 °Csıcaklıkta ve 2 sa. sürdürülen polimerizasyon ile elde edildiği bulundu. Safpoli(o-toluidin) ve poli(o-toluidin)/kaolinit kompozitinin direnç değerleri0-100 °C sıcaklık aralığında tekrar edilen ısıtma-soğutma işlemleri sırasındaizlenerek sıcaklığa karşı duyarlılığı incelendi. Bağıl nem oranı %30-90arasında değiştirilen ortamlarda saf poli(o-toluidin) ve kompozitin dirençdeğerleri ölçülerek nem sensör davranışı belirlendi. Hazırlanan kompozitinkarakterizasyonu Fourier dönüşümlü kızılötesi spektroskopisi (FT-IR), X-Işınları kırınımı (XRD), termogravimetrik analiz (TGA) ve taramalıelektron mikroskobu (SEM) teknikleri ile yapıldı., Conductivepoly(o-toluidine)/kaolinite composite was synthesized via chemicalpolymerization of o-toluidine in the availability of kaolinite using ammoniumpersulfate as oxidizing agent. To investigate the use of the preparedconductive composite as humidity and temperature sensor, the effect ofpolymerization conditions such as HCl, o-toluidine and oxidant concentrationson the amount of conductive POT contained in the composite and the conductivityvalues of composites were investigated. It was found that the composites withthe highest poly (o-toluidine) content (29.4%) and conductivity (8.3×10-4 Scm-1)were obtained by 0.2 M ammonium persulfate, 0.4 M o-toluidine and 1 Mhydrochloric acid for 2 hours of continuous polymerization at 20 °C. Theresistivity values of pure poly(o-toluidine) and poly (o-toluidine)/kaolinite composite were monitored during heating-cooling cyclesin the range of 0-100 °C. Changes in resistivity for pure poly(o-toluidine) andpoly(o-toluidine)/kaolinite composite with humidity 30-90% were examined andhumidity sensor behavior was determined. Characterization of the preparedcomposite was performed by Fourier transform ınfrared spectroscopy (FT-IR),X-ray diffraction (XRD), thermogravimetric analysis (TGA) and scanning electronmicroscopy techniques (SEM).

research Bu çalışmada iletken POT/Sodyum Feldispat kompoziti in-situ kimyasal polimerizasyon yöntemi ile hazırlandı. Sodyum Feldispat partikülleri varlığında asidik sulu ortamda hazırlanan kompozitin iletkenliği ve %POT verimi üzerine sodyum feldispatın tanecik boyutunun ve polimerizasyon koşullarının etkisi araştırıldı. En yüksek elektriksel iletkenlik ve verim için en uygun reaksiyon koşulları 45µm altı partikül boyutundaki Na-Feldispat, 1 M HCl, 0.3 M o-toluidin, 0.0375 M K2Cr2O7 ve 0°C sıcaklık olarak belirlendi. En yüksek POT verimi ve elektriksel iletkenlik değerleri sırasıyla %24.51 ve 22×10-5 Scm-1 bulundu. Hazırlanan kompozitin karakterizasyonu, kompozitin bileşenlerinin saf halleri ile karşılaştırılmalı olarak Fourier dönüşümlü kızılötesi spektroskopisi (FTIR), X-ışınları kırınımı (XRD), termal gravimetrik analiz (TGA) ve taramalı elektron mikroskop (SEM) teknikleri kullanılarak yapıldı. Recently, conductive polymeric materials have attracted a lot of interest in scientific and technological fields. Among all conducting polymers, polyaniline are of great interest due to easy synthesis, good environmental stability and its high conductivity. However, the main problem is the weak mechanical properties and workability of PANı based on insoluble in common organic solvents. This problem is resolved to some extent through the use of derivatives such as N-methyl or N-ethyl aniline, toluidine and anisidine instead of aniline. In these days, organic-inorganic nanohybrid materials known as polymer nanocomposites have become an effective alternative for many applications. Inorganic materials are used for imparting new and superior properties to composites.