Search

Submitted by Boris Flegr (boris@uerj.br) on 2021-01-06T19:00:33Z No. of bitstreams: 1 Deborah Reboucas da Cunha.pdf: 4032862 bytes, checksum: df2ee8e18ddd68a752f937c934ee6f90 (MD5) Made available in DSpace on 2021-01-06T19:00:33Z (GMT). No. of bitstreams: 1 Deborah Reboucas da Cunha.pdf: 4032862 bytes, checksum: df2ee8e18ddd68a752f937c934ee6f90 (MD5) Previous issue date: 2019-08-30 Coordenação de Aperfeiçoamento de Pessoal de Nível Superior New material that have been studied in construction engineering to replace the steel include non-metallic bars. Some advantages in its use can be cited as the possibility of lower cover thickness, high tensile strength, low specific weight and no electrical, thermal and magnetic conductivity. This work experimentally analyzes the bond between GFRP bars and concrete through pull-out tests, adapted from Canadian and American standards, CSA S806-12 and ACI 440.3R-04. The parameters considered were the bonded length and the bar diameter. The experimental results were compared with normative formulations and results from previous studies available in literature. In the experimental models it was possible to analyze the influence of the mechanical properties of the bars, as well as the bond stresses, the influence of the bars diameter, the failures modes and the surface conformation coefficient. Five different diameters and three bonded lengths were tested, totalizing fifty-seven models in this study. Dentre os novos materiais para a construção civil que vêm sendo estudados em substituição ao aço, estão as barras não-metálicas. Algumas vantagens no seu uso podem ser citadas como: possibilidade de menor espessura de cobrimento, alta resistência à tração, baixo peso específico e não condutividades elétrica, térmica e magnética. Este trabalho analisa experimentalmente a aderência entre barras de GFRP e concreto por meio de ensaios de arrancamento (Pull Out), adaptados das normas canadense e americana, CSA S806-12 e ACI 440.3R-04, respectivamente. Foram considerados como parâmetros o comprimento de aderência e o diâmetro da barra. Os resultados experimentais foram comparados com formulações normativas propostas e resultados de pesquisas anteriores da literatura técnica. Nos modelos experimentais foi possível analisar a influência das propriedades mecânicas das barras, assim como as tensões de aderência, a influência do diâmetro das barras, modos de ruptura dos ensaios e o coeficiente de conformação superficial. Foram ensaiadas barras com cinco diâmetros diferentes, e três comprimentos de aderência, totalizando cinquenta e sete modelos neste estudo.

Submitted by Boris Flegr (boris@uerj.br) on 2021-01-05T18:29:40Z No. of bitstreams: 4 Dissertacao_RaquelMuylaertCamargoDaSilva_(p 1-39).pdf: 5200441 bytes, checksum: 5397b8079d361bcd470713e2d4c40234 (MD5) Dissertacao_RaquelMuylaertCamargoDaSilva_(p 40-54).pdf: 9294474 bytes, checksum: a5f1f56457e446453fe498a3df15406f (MD5) Dissertacao_RaquelMuylaertCamargoDaSilva_(p 55-62).pdf: 14336435 bytes, checksum: 4caebd7c3c62a552c7fd298a24a28c7c (MD5) Dissertacao_RaquelMuylaertCamargoDaSilva_(p 63-104).pdf: 4920742 bytes, checksum: d983558bd0c6bbc6da083199cf4b3714 (MD5) Made available in DSpace on 2021-01-05T18:29:40Z (GMT). No. of bitstreams: 4 Dissertacao_RaquelMuylaertCamargoDaSilva_(p 1-39).pdf: 5200441 bytes, checksum: 5397b8079d361bcd470713e2d4c40234 (MD5) Dissertacao_RaquelMuylaertCamargoDaSilva_(p 40-54).pdf: 9294474 bytes, checksum: a5f1f56457e446453fe498a3df15406f (MD5) Dissertacao_RaquelMuylaertCamargoDaSilva_(p 55-62).pdf: 14336435 bytes, checksum: 4caebd7c3c62a552c7fd298a24a28c7c (MD5) Dissertacao_RaquelMuylaertCamargoDaSilva_(p 63-104).pdf: 4920742 bytes, checksum: d983558bd0c6bbc6da083199cf4b3714 (MD5) Previous issue date: 2018-08-24 Coordenação de Aperfeiçoamento de Pessoal de Nível Superior In this work, composite materials made from polypropylene (PP) and alumina (Al2O3), as well as from polypropylene and glass fiber (GF) were developed, aiming to improve the polymer thermal and mechanical properties. The effect of each reinforcement element, as well as of the hybrid reinforcement, on the polymer properties was evaluated. The influence of some process variables such as: the surface treatment of alumina with vinyltrietoxisilane, the addition of a coupling agent, polypropylene grafted with maleic anhydride (PP-g-MA), the surface treatment of glass fiber with γ-aminopropyltriethoxy- silane and with an alkaline NaOH solution, on the properties of the composites, PP/Al2O3 and PP/Fiber Glass, respectively, were also investigated. The tensile, flexural and impact properties of the obtained materials were determined. The thermal properties were evaluated through differential scanning calorimetry (DSC), thermogravimetric analysis (TGA) and thermal conductivity measurements. The morphology of the samples was examined by using scanning electron microscopy (SEM). The results obtained showed that the alumina and glass fibers surface treatments exerted no effect on the interfacial adhesion between the matrix and the reinforcements. The composite prepared with 5 wt.% Al2O3 , 20 wt.% of glass fiber in nature and 2 wt.% of PP-g-MA was the material that presented the better combination of mechanical. Due to the poor adhesion properties, the composites processed with the reinforcement elements without any superficial treatment even presented superior mechanical properties. The addition of PP-g-MA to the composites, however, promoted better adhesion between the polypropylene and the reinforcements leading to obtaining better mechanical properties, showing the higher values of impact resistance, Young Modulus, tensile resistance, flexural modulus and resistance. This material presented impact resistance higher than the impact resistance of polypropylene. The thermal conductivity of polypropylene was not improved with the development of the composites. However, the thermal stability was higher than that of polypropylene. The results obtained shows that this material may be used in engineering applications where strong and hard PP based materials with good impact properties and satisfactory thermal stability are necessary. Neste trabalho, o efeito da incorporação de alumina (Al2O3) e de fibra de vidro (FV), assim como de ambas as cargas (reforço híbrido) ao polipropileno (PP) foi investigado. Os efeitos do tratamento superficial da alumina com vinil-trietóxi-silano , do uso do polipropileno graftizado com anidrido maleico (PP-g-MA) como agente de acoplamento, assim como do tratamento superficial da fibra de vidro com γ-aminopropil-trietóxi-silano e com solução alcalina de NaOH, sobre as propriedades mecânicas, térmicas e morfológicas dos compósitos produzidos, PP/Al2O3 e PP/Fibra de Vidro, respectivamente, também foram investigados. O comportamento mecânico dos materiais obtidos foi avaliado em tração, flexão e sob carga de impacto. As propriedades térmicas foram determinadas através de calorimetria exploratória diferencial (DSC), análise termogravimétrica (TGA) e ensaios de condutividade térmica. A morfologia foi analisada através de microscopia eletrônica de varredura (MEV). Os resultados obtidos demonstraram que os tratamentos superficiais efetuados na alumina, assim como na fibra de vidro, não promoveram uma melhor adesão interfacial entre as cargas e a matriz polimérica. Devido a essas propriedades de adesão insatisfatórias foi observado que, de forma geral, os compósitos carregados com alumina tratada e com fibra de vidro tratada apresentaram propriedades mecânicas inferiores às dos compósitos carregados com alumina e fibra de vidro não tratadas, respectivamente. O uso do PP-g-MA como agente de acoplamento, entretanto, promoveu melhor adesão interfacial tanto entre a alumina e o PP, quanto entre a fibra de vidro e o PP, resultando na obtenção de propriedades mecânicas superiores. Entre todos os compósitos estudados, o compósito processado com 5% Al2O3 sem tratamento e 20% de fibra de vidro sem tratamento (FVnt), na presença de 2% de PP-g-MA, foi o que apresentou melhor combinação de propriedades mecânicas, apresentando os maiores valores de resistência ao impacto, de módulo de elasticidade, de resistência à tração, de módulo de flexão e de resistência à flexão. Esse compósito apresentou valor de resistência ao impacto médio superior até mesmo ao do polipropileno puro. A condutividade térmica do polipropileno não foi melhorada com o desenvolvimento dos compósitos, mas a estabilidade térmica dos compósitos foi superior à do polipropileno. Os resultados obtidos indicam a possibilidade da utilização desse material em aplicações de engenharia onde materiais à base de PP rígidos e resistentes tanto em flexão quanto em tração e com boa resistência ao impacto e estabilidade térmica satisfatória sejam necessários.

Tese (doutorado) - Universidade Federal de Santa Catarina, Centro Tecnológico. Programa de Pós-Graduação em Engenharia Civil. Hoje em dia muitas estruturas encontram-se estruturalmente comprometidas

Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico. Programa de Pós-Graduação em Engenharia Civil.

Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnologico Este trabalho de pesquisa procura desenvolver uma avaliação do setor de Plástico Reforçado com Fibra de Vidro no Estado de Santa Catarina. O objetivo principal é o conhecimento da estrutura industrial do setor e a análise dos seus principais problemas, definidos a partir da constatação dos seus pontos fortes e fracos. Utilizou-se a metodologia de Porter como um instrumento analítico. O modelo apresenta um sistema geral para a análise da estrutura de um setor e dos concorrentes que dele participam. As informações da estrutura da indústria do setor de PRFV descrevem os principais ítens que colaboram para a maior intensidade das forças atuantes sobre as empresas deste setor, e permitem a análise do tipo de meio industrial no qual estas empresas estão inseridas. A divisão do setor em grupos estratégicos através do método de Clustering, possibilta às empresas a ele pertencentes uma análise do seu posicionamento em relação aos seus concorrentes. Permitindo assim, através destes conhecimentos a formulação de ações estratégicas específicas de acordo com a problemática de cada grupo estratégico.