Search

Recently, it has been reported that tear osmolarity (Tosm) is correlated with plasma osmolarity and will increase during exertion. We aimed to assess whether inhaling oxygen-enriched air between exercises could significantly change the Tosm value. Thirty men aged 24.9 years were included in the study. A cycloergometer was used to perform the exercise protocol. We recorded the participants’ Tosm (mOsm/L), heart rate (HR, beats/minute), oxygen saturation, and blood pressure values. After the first exhaustive exercise (T1), participants inhaled oxygen in the experimental group and a placebo in the control group. After the second exercise (T2), another set of measurements was obtained. The Tosm value before exercise was 297.4 ± 1.21 and 296.53 ± 1.11 mOsm/L (p = 0.61718) and the HR was 72.6 ± 2.59 and 73 ± 2.59 beats/minute (p = 0.39949) in the study and the control group, respectively. At T1, Tosm was 303.67 ± 1.25 and 302.2 ± 1.25 mOsm/L (p = 0.41286) and the HR reached 178.04 ± 2.60 and 176.4 ± 2.60 beats/minute (p = 0.65832), respectively. At T2, Tosm in the study group reached 305.73 ± 0.86 mOsm/L (correlation with the use of oxygen: r = −0.3818), and in the control group, it was 308.4 ± 0.86 mOsm/L (p = 0.0373), while the HR reached 172.20 ± 2.53 beats/minute in the study group and 178.2 ± 2.53 beats/minute in the control group (p = 0.057). It was concluded that inhaling oxygen before and after exercise could increase the rate of recovery after exhaustive exercise.

Objectives Vestibular rehabilitation leads to a gradual diminution of the subjective and objective symptoms that accompany the vestibular disorders. The aim of the study was to compare the impact of 2 different types of vestibular rehabilitation on vestibular compensation in patients with chronic unilateral vestibular dysfunction. Material and Methods The study was conducted on a group of 58 subjects (43 females and 15 males) aged 40–64 years, who presented with chronic unilateral vestibular dysfunction and were hospitalized. The patients were randomly assigned to either of the 2 groups established. The study was conducted in a 6-week period. Group 1 consisted of patients who underwent customized group vestibular rehabilitation in an outpatient setting. The program was performed once a week for 1 h 30 min, under the supervision of a physiotherapist and a physiatrist. Group 2 was instructed to perform Cawthorne–Cooksey exercises and simple balance exercises twice a day for 15 min. Results An improvement in the outcomes of the Dynamic Gait Index as well as the Berg Balance Scale was statistically significant for group 1. The time for fulfilling the task in the Timed Up and Go Test improved in both groups (p < 0.05). The subjective estimation of the symptoms evaluated with the use of the Dizziness Handicap Inventory and the Visual Analogue Scale revealed a statistically significant improvement in both groups, yet it was higher in group 1. Conclusions The compensation achieved after 6 weeks of the customized, supervised outpatient rehabilitation program in group 1 was superior to the results of the home-based unsupervised Cawthorne–Cooksey and balance exercises. Int J Occup Med Environ Health. 2020;33(3):273–82

Physical exertion leads to the rise in tear osmolarity. However, previous studies have been conducted mostly on males and did not consider sex differences and the possible alteration in blinking during physical exercise. Sixteen women and 18 men aged 25.09 ± 1.70 were divided into equal groups with eyes open and shut. Participants performed 8-min medium-intensity exercise and 5-min intense exercise on a cycloergometer. Tear osmolarity (in mOsm/L) was evaluated before ( T0), after medium-intensity (T1) and intense exercise (T2). The blinking rate was assessed in a group with eyes open. Tear brake up time was measured in T0 and T1. With tear osmolarity measuring 305.72 ± 1.22 and 313.56 ± 1.90 for men and women, respectively, we observed significant differences in T1. In T2, tear osmolarity in men was 303.3 ± 1.28 vs. 310.87 ± 1.36 in women. The blinking rate decreased from 14.24 ± 2.54/min in T0 to 9.41 ± 2.83/min in T1. There was a statistically significant change in tear osmolarity in both groups, that is, in the group with eyes shut from 300.53 ± 1.37 in T0 to 308.06 ± 1.55 in T1 to 304.88 ± 1.54 in T2. In the group with eyes open, tear osmolarity increased from 300.29 ± 1.37 in T0 to 310.76 ± 1.55 in T1 and then dropped to 308.88 ± 1.54 in T2. Tear brake up time measured in T0 was 14.7 ± 1.43 vs. 13.53 ±1.48 in the open eyes condition. Due to physical exercise, short-term changes in tear osmolarity are partially caused by altered blinking. Sex differences in tear osmolarity in response to exertion may confirm the relationship between total body water and tear osmolarity.

The aim of the work was to compare the degradation behavior of electrospun nanofibres obtained from pure poly(lactic acid) (PLA) and modified with carbon nanotubes (CNTs) in aqueous environment. The nanofibres in the form of mats were manufactured using the electrospinning technique (ES) with potential biomedical application. To investigate the degradation behavior, one-component and composite (containing CNTs) nanofibres were compared using scanning electron microscopy (SEM), water contact angle measurements, differential scanning calorimetry (DSC), and mechanical testing. The changes in their morphology, structure, and selected physical and mechanical properties during incubation up to 14 days were analysed. Two types of CNTs differing in concentration of surface functional groups were used to modify the PLA nanofibres. PLA and composite nanofibres (PLA + CNT) during incubation underwent swelling and partial degradation due to the penetration of water into polymer matrix. Changes in the mechanical properties of composite mats were higher than those observed for pure PLA mats. After 14-day incubation, samples retained from 47 to 78% of their initial tensile strength, higher for PLA samples. Morphological changes in pure PLA nanofibres were more dynamic than in composite nanofibres. No significant changes in crystallinity, wettability, and porosity of the samples occurred.

The aim of this study was to evaluate a novel composite material for tracheal reconstruction in an ovine model. A polymer containing various forms of carbon fibers (roving, woven, and nonwoven fabric) impregnated with polysulfone (PSU) was used to create cylindrical tracheal implants, 3 cm in length and 2.5 cm in diameter. Each implant, reinforced with five rings made of PSU-impregnated carbon-fiber roving, had three external layers made of carbon-fiber woven fabric and the inner layer formed of carbon-fiber nonwoven fabric. The inner surface of five implants was additionally coated with polyurethane (PU), to promote migration of respiratory epithelium. The implants were used to repair tracheal defects (involving four tracheal rings) in 10 sheep (9-12 months of age; 40-50 kg body weight). Macroscopic and microscopic characteristics of the implants and tracheal anastomoses were examined 4 and 24 weeks after implantation. At the end of the follow-up period, outer surfaces of the implants were covered with the tissue which to various degree resembled histological structure of normal tracheal wall. In turn, inner surfaces of the prostheses were covered only with vascularized connective tissue. Inner polyurethane coating did not improve the outcomes of tracheal reconstruction and promoted excessive granulation, which contributed to moderate to severe stenosis at the tracheal anastomoses. The hereby presented preliminary findings constitute a valuable source of data for future research on a tracheal implant being optimally adjusted for medical needs.

Polymer substrates obtained from poly(lactic acid) (PLA) nanofibres modified with carbon nanotubes (CNTs) and gelatin (GEL) for cartilage tissue engineering are studied. The work presents the results of physical, mechanical, and biological assessment. The hybrid structure of PLA and gelatine nanofibres, carbon nanotubes- (CNTs-) modified PLA nanofibres, and pure PLA-based nanofibres was manufactured in the form of fibrous membranes. The fibrous samples with different microstructures were obtained by electrospinning method. Microstructure, physical and mechanical properties of samples made from pure PLA nanofibres, CNTs-, and gelatin-modified PLA-nanofibres were studied. The scaffolds were also testedin vitroin cell culture of human chondrocytes collected from patients. To assess the influence of the nanofibrous scaffolds upon chondrocytes, tests for cytotoxicity and genotoxicity were performed. The work reveals that the nanofibrous structures studied were neither genotoxic nor cytotoxic, and their microstructure, physical and mechanical properties create promising scaffolds for potential use in cartilage repairing.