In this study, two different sample preparation methods to synthesize activated carbon from pine wood were compared. The pine wood activated carbon was prepared by mixing ZnCl2 by physical mixing, i.e., "dry mixing" and impregnation, i.e., "wet mixing" before high temperature carbonization. The influence of these methods on the physicochemical properties of activated carbons was examined. The activated carbon was analyzed using nitrogen sorption (surface area, pore volume and pore size distribution), XPS, density, Raman spectroscopy, and electrochemistry. Physical mixing led to a slightly higher density carbon (1.83 g/cm3) than wet impregnation (1.78 g/cm3). Raman spectroscopy analysis also showed that impregnation led to activated carbon with a much higher degree of defects than physical mixing, i.e., ID/IG = 0.86 and 0.89, respectively. The wet impregnated samples also had better overall textural properties. For example, for samples activated with 1:1 ratio, the total pore volume was 0.664 vs. 0.637 cm3/g and the surface area was 1191 vs. 1263 m2/g for dry and wet mixed samples, respectively. In the electrochemical application, specifically in supercapacitors, impregnated samples showed a much better capacitance at low current densities, i.e., 247 vs. 146 F/g at the current density of 0.1 A/g. However, the physically mixed samples were more stable after 5000 cycles: 97.8% versus 94.4% capacitance retention for the wet impregnated samples. [ABSTRACT FROM AUTHOR]

Herein, an innovative method to improve the dewatering of micro- and nanofibrillated cellulose (MNFC) containing furnishes is proposed. This method is based on fiber flotation in which cationic bubbles are injected into the furnish to separate fibers from liquid medium and accumulate them on the surface of the furnish. These cationic bubbles are generated by pressurizing a solution of Hexadecyltrimethylammonium chloride in deionized water in a dissolved air flotation (DAF) tank. The drainage properties of the furnishes with MNFC content from 0% to 25% were studied. With the help of the cationic bubbles, drainage rate of 0% and 15% MNFC furnish increased from 183 ml/s to 210 ml/s and 38 ml/s to 113 ml/s, respectively. The final couch solids content of these furnishes also increased from 16 wt% to 23 wt% and from 21 wt% to 24 wt%, respectively. Cationic bubbles flocculate MNFC fibers and increase retention. Sheets characteristics including morphology, permeability, mass distribution and surface profilometry were investigated. Cationic bubbles help structure fiber elements and improve the sheet formation. [ABSTRACT FROM AUTHOR]