Search

The CO2 methanation mechanism over the highly active (TOF=75.1 h−1), selective (>92%) and stable 10% LaNiO3/CeO2-derived catalyst is still unresolved. The surface of the catalyst is monitored under hydrogenation (H2), oxidizing (CO2) and CO2 methanation (H2 +CO2) conditions by near ambient pressure X-ray photoelectron spectroscopy (NAP-XPS) using synchrotron radiation. Meanwhile, the main reaction intermediates are identified by in situ FTIR analysis. NAP-XPS experiments confirm that LaNiO3 perovskite reduction leads to the ex-solution of Ni0 nanoparticles and Ni2+single bondCeO2−x and Ni2+single bondLa2O3 interfaces conformation, favouring the CO2 adsorption and the H2 dissociation/transfer. In situ FTIR experiments combined with the C1s spectra (NAP-XPS) suggest that the CO2 activation occurs on CeO2−x (oxygen vacancies and OH–) at low temperatures, in the form of bicarbonates; whereas, mono-/bidentate carbonates are formed on different strength La2O3 sites at increasing temperatures. These species are consecutively reduced to formates, as the main reaction intermediate, and methane by the H spilled from Ni0 nanoparticles near to NiOsingle bondCeO2−x and NiOsingle bondLa2O3 interfaces.

Ni/CeO2 catalysts are very active and selective for total hydrogenation of CO2 to methane, but the nature of the active sites is still unclear. The surface of a Ni/CeO2 catalyst has been monitored under CO2 methanation conditions by Near Ambient Pressure-XPS (NAP-XPS) using synchrotron radiation, and has been concluded that the species involved in the redox processes taking place during the CO2 methanation mechanism are the Ni2+-CeO2/Ni0 and Ce4+/Ce3+ pairs. In addition, a small fraction of nickel is present on the catalyst surface forming NiO and Ni2+-carbonates/hydroxyls (around 20% of the total surface nickel), but these species do not participate in the redox processes of the methanation mechanism. Under CO2 methanation conditions the H2 reduction rate of the Ni2+-CeO2/Ni0 and Ce4+/Ce3+ couples is much faster than their CO2 reoxidation rate (2 times faster, at least, at 300ºC), but a certain proportion of nickel always remains oxidized under reaction conditions. The high activity of Ni/CeO2 catalysts for CO2 methanation is tentatively attributed to the simultaneous presence of Ni2+-CeO2 and Ni0 active sites where CO2 and H2 are expected to be efficiently dissociated, respectively.

Intense research efforts are directed toward Cu and Cu2O based catalysts as they are viewed as potential replacements for noble metal catalysts. However, applications are hampered by deactivation, e.g., through facile complete oxidation to CuO. Despite the importance of the redox processes for Cu2O catalysts, a molecular level understanding of the deactivation process is still lacking. Here we study the initial stages of oxidization of well-defined Cu2O bulk single crystals of (100) and (111) termination by means of synchrotron radiation X-ray photoemission spectroscopy (XPS) and scanning tunneling microscopy (STM). Exposure of the (100) surface to 1 mbar O-2 at 25 degrees C results in the formation of a 1.0 monolayer (ML) CuO surface oxide. The surface is covered by 0.7 ML OH groups from trace moisture in the reaction gas. In contrast, neither hydroxylation nor oxidation was observed on the (111) surface under similar mild exposure conditions. On Cu2O(111) the initial formation of CuO requires annealing to similar to 400 degrees C in 1 mbar 02, highlighting the markedly different reactivity of the two Cu2O surfaces. Annealing of the (100) surface, under ultrahigh vacuum conditions, to temperatures up to similar to 225 degrees C resulted in removal of the OH groups (0.46 ML decrease) at a rate similar to a detected increase in CuO coverage (0.45 ML increase), suggesting the reaction path 2OH(adsorbed) + CU2Osolid -> H2Ogas + 2CuO(solid). STM was used to correlate the observed changes in surface chemistry with surface morphology, confirming the surface hydroxylation and CuO formation. The STM analysis showed dramatic changes in surface morphology demonstrating a high mobility of the active species under reaction conditions., QC 20190123

[EN] Sunlight plays a critical role in the development of emerging sustainable energy conversion and storage technologies. Light-induced CO2 reduction by artificial photosynthesis is one of the cornerstones to produce renewable fuels and environmentally friendly chemicals. Interface interactions between plasmonic metal nanoparticles and semiconductors exhibit improved photoactivities under a wide range of the solar spectrum. However, the photoinduced charge transfer processes and their influence on photocatalysis with these materials are still under debate, mainly due to the complexity of the involved routes occurring at different timescales. Here, we use a combination of advanced in situ and time-resolved spectroscopies covering different timescales, combined with theoretical calculations, to unravel the overall mechanism of photocatalytic CO2 reduction by Ag/TiO2 catalysts. Our findings provide evidence of the key factors determining the enhancement of photoactivity under ultraviolet and visible irradiation, which have important implications for the design of solar energy conversion materials.