Cobaltite-like materials having metal-insulator transitions are relevant in the consumer electronics market. In this work, we present the structural, magnetic, and electrical properties of Ba1-xNaxCoO3(with x= 0.25, 0.5, 0.75) cobaltite. All samples were synthesized using a solid-state reaction process. Their crystal structure was determined using X-ray diffraction (XRD) data by the Rietveld method, which showed that all the samples were crystallized in the orthorhombic space group C2221(N.° 20). The microstructure of the sintered samples was characterized by scanning electron microscopy (SEM). The magnetic susceptibility measurements confirmed a paramagnetic behavior for x≥ 0.5in the temperature range that was used. Likewise, a broad peak around 33 Kin the sample x = 0.25,andcharacteristic of antiferromagnetic behaviors wereobserved. Onthe other hand, resistivity contributed to determining the insulating behavior of samples where x = 0.5and x = 0.75. In contrast, at low sodium content (x = 0.25), a metal-insulator transition was observed with transition temperature near 105 K. Los materiales de tipo cobaltita que presentan transición metal-aislante tienen relevancia en el mercado de la electrónica de consumo. En este trabajo presentamos las propiedades estructurales, magnéticas y eléctricas de las cobaltitas Ba1-xNaxCoO3(con x= 0.25, 0.5, 0.75). Todas las muestras se sintetizaron mediante un proceso de reacción en estado sólido y su estructura cristalina se determinó a partir de datos de difracción de rayos X (DRX),mediante el método de Rietveld, el cual indicó que las muestras cristalizan en el grupo espacial ortorrómbico C2221(N.o20). La microestructura de las muestras sinterizadas se caracterizó mediante microscopía electrónica de barrido (MEB). Las medidas de susceptibilidad magnética confirmaron un comportamiento paramagnético para x≥ 0.5en el rango de temperatura estudiado y un pico amplio alrededor de 33 Ken la muestra x= 0.25,lo cual es característico de los comportamientos antiferromagnéticos. Las medidas de resistividad permitieron determinar el comportamiento aislante de muestras con x= 0.5y x= 0.75, mientras que a bajo contenido de sodio (x= 0.25),se observó una transición metal-aislante con temperatura de transición cercana a 105K.

This paper reports the synthesis and characterization of Bi1-xLuxFeO3 (x = 0.00, 0.02, and 0.04) produced by solid-state reaction, in order to evaluate the influence of lutetium on the structural and magnetic properties of bismuth ferrite (BiFeO3). The samples were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX), and magnetic analysis by vibrating sample magnetometer (VSM) in the temperature range from 50 to 320 K. The obtained results allowed confirming the formation of crystalline materials of rhombohedral structure, space-group R3c (161), defined morphology and particle sizes between 2.25 and 4.50 μm. The Lu3+ insertion in the structure caused an increase in magnetization, purity of BiFeO3, and a decrease in the synthesis temperature as compared with the reported in the literature. Resumen Este artículo reporta la síntesis y caracterización de Bi1-xLuxFeO3 (x = 0.00, 0.02 and 0.04) producido por reacción de estado sólido, con el fin de evaluar la influencia del catión lutecio sobre las propiedades estructurales y magnéticas de la ferrita de bismuto (BiFeO3). Las muestras fueron caracterizadas por difracción de rayos X (DRX), microscopia electrónica de barrido (MEB), espectroscopia de energía dispersiva de rayos X (EDX) y análisis magnético por medio de magnetometría de muestra vibrante (VSM) en un rango de temperatura de 50 a 320 K. Los resultados obtenidos permitieron confirman la formación de materiales cristalinos de estructura romboédrica, grupo espacial R3c (161), de morfología definida y tamaños de partícula entre 2.25 y 4.50 μm. La inserción de Lu3+ en la estructura provocó un aumento en la magnetización, la pureza de BiFeO3 y una disminución en la temperatura de síntesis en comparación con lo reportado en la literatura.

We report the synthesis of CaMn0.9Mo0.1O3 manganite by glow discharge (GD) plasma treatment under Argon-Air atmosphere. The morphological, structural and magnetic properties were evaluated by scanning electron microscopy (SEM), X-ray diffraction (XRD) and magnetization measures. The results from these measures reveal that the properties of GD synthesized manganite are similar to that exhibited by CaMn0.9Mo0.1O3 produced by conventional resistive furnace. The Rietveld analysis of XRD patterns performed at room temperature show that the samples crystallize in orthorhombic structure of Pnma (62) space group. The magnetization curves as a function of temperature show two inflection points related to paramagnetic-antiferromagnetic and structural transition. The GD treatment produces a compound with similar properties, reducing the time and energy consumption in comparison with conventional synthesis route by using resistive furnace. Resumen En este trabajo reportamos la síntesis de la manganita CaMn0.9Mo0.1O3 empleando plasma de descarga luminiscente en atmosfera de argón-aire. Se evaluaron las propiedades morfológicas, estructurales y magnéticas a través de microscopía electrónica de barrido (MEB), difracción de rayos X (DRX) y medidas de magnetización. Los resultados de éstas medidas revelan que las propiedades de la manganita CaMn0.9Mo0.1O3 sintetizada por descarga luminiscente son similares a las propiedades de la misma producida en horno resistivo convencional. El análisis Rietveld de los patrones de DRX tomados a temperatura ambiente revelan que la muestra cristaliza en el grupo espacial Pnma (62) ortorrómbica. Las curvas de magnetización en función de la temperatura muestran dos puntos de inflexión que evidencian una transición paramagnética-antiferromagnética y una transición estructural. El tratamiento por descarga luminiscente produce un compuesto con propiedades similares, reduciendo el tiempo y consumo energético en comparación con la producción del mismo material usando horno resistivo.

1 recurso en línea (páginas 33-40)., This document reports the synthesis of the materials Sr2GdSbO6 (SGSO) and GdBa2Cu3O7−δ (GBCO), by the reaction method in solid state and GdBa2Cu3O7−δ /Sr2GdSbO6 (GBCO/SGSO) composites in different volumetric proportions. The structural characterization of the synthesized compounds was carried out by means of X-ray diffraction, using the Rietveld refinement method, performing a quantitative analysis of phases in volume. The results obtained confirm that the two materials (GBCO / SGSO) are chemically stable, coexisting in the same volume at 9000 C. It was also found, by means of magnetization measures, that the GBCO contained in each one of the different composites, It keeps superconducting properties, as the transition to the superconducting state was obtained below a temperature of 900 K. The morphological characterization was performed by scanning electron microscopy (SEM) and elemental analysis by means of dispersive energy spectroscopy (EDX) measurements. The electrical study was performed by means of voltage measurements as a function of the current at room temperature and subsequent calculation of the volumetric resistivity. The study of the percolative effect was carried out by calculating the critical volume and the critical exponents in each one of the insulating and conductive phases, using the Kussy model [1] and the semi-classical non-linear response model Random Resistor cum Tuning Bond Network (RRTN)[2], by contrasting critical exponents with those found in the literature., En este trabajo se reporta la síntesis de los materiales Sr2GdSbO6 (SGSO) y GdBa2Cu3O7−δ (GBCO), por el método de reacción en estado sólido y de compósitos GdBa2Cu3O7−δ /Sr2GdSbO6 (GBCO/SGSO) en diferentes proporciones volumétricas. La caracterización estructural de los compuestos sintetizados se realizó por medio de difracción de rayos X, usando el método de refinamiento Rietveld, realizando un análisis cuantitativo de fases en volumen. Los resultados obtenidos permiten confirmar que los dos materiales (GBCO/SGSO) son estables químicamente, coexistiendo en un mismo volumen a 900 C. También se encontró, mediante medidas de magnetización, que el GBCO contenido en cada uno de los diferentes compósitos, conservó sus propiedades superconductoras, ya que se obtuvo la transición al estado superconductor por debajo de una temperatura de 90 K. La caracterización morfológica se realizó mediante medidas de microscopia electrónica de barrido (SEM) y análisis elemental mediante medidas de espectroscopia de energía dispersiva (EDX). El estudio eléctrico se realizó mediante medidas de voltaje en función de la corriente a temperatura ambiente y posterior cálculo de la resistividad volumétrica. El estudio del efecto percolativo se llevó a cabo mediante el cálculo del volumen crítico y de los exponentes críticos en cada una de las fases aislante y conductora, usando el modelo de Kussy [1] y el modelo de respuesta no lineal semi clásica Random Resitor cum Tunelling bond Network (RRTN) [2] contrastando los exponentes críticos, con los encontrados en la literatura., Bibliografía: página 40.

This article presents the production and structural and magnetic characterization of the Bi1-xYxFeO3 System x = 0 and 0.07, the samples were obtained by solid state reaction method. The samples were characterized by x-ray diffraction (XRD), electron microscopy scanning SEM and Mössbauer Spectroscopy. The analysis by Rietveld refinement, allowed to determine system Bi1-xYxFeO3 crystallizes in the Group R3c (161) rhombohedral. The obtained results allowed to conclude that the replacement of Bi by ions of and influence the appearance of Bi2Fe4O9 impurities, without affecting the structural response of the samples with the increase of doping yttrium.

Resumen La tecnología del plasma es una ciencia que desde sus comienzos se encuentra en una constante evolución, desde aplicaciones para el tratamiento de materiales hasta aplicaciones ambientales. En particular el plasma de la descarga luminiscente ofrece una amplia gama de aplicaciones desde aplicaciones en plasmo-química hasta tratamientos termoquímicos de materiales. En el presente trabajo se busca aprovechar la generación de calor por parte de la descarga luminiscente de baja presión en corriente continua, debido a la transferencia de energía cinética desde el plasma hacia los electrodos. Para ello se diseñó un reactor cilíndrico que genera una descarga luminiscente de baja presión en una atmósfera de argón. El cátodo de la descarga lo constituye el electrodo interno, mientras que el ánodo, y al mismo tiempo la pared de la cámara, lo constituye un cilindro metálico externo, concéntrico al cátodo. Para mantener la descarga se utilizó una fuente de corriente continua pulsada y la descarga se generó a varias corrientes y en diferentes atmósferas gaseosas (N2, H 2 y Ar). Mediante medidas eléctricas de la descarga se determinó la potencia y consumo energético del reactor, comparándolo con los valores obtenidos para un dispositivo calefactor comercial basado en resistencias eléctricas. Abstract Plasma technology is a science that is in a constant evolution from its beginnings, from applications from materials treatment until environmental applications. Particularly the glow discharge plasma offers a wide variety of uses, including plasma-chemical applications and thermo-chemical materials treatment. In the present work seeks to exploit the heat generation by the low pressure glow discharge, which is due to kinetic energy transfer from the plasma toward the electrodes. For this purpose a cylindrical reactor that generates a low-pressure glow discharge in gas argon was designed. The discharge cathode constitutes the internal electrode, while the anode, which also constitutes the chamber wall, is a metallic cylinder concentric to the cathode. To sustain the glow discharge a source of pulsed direct current is used and the discharge was generated at several currents in different gas atmospheres (N2, H2 y Ar). Through electrical measurements of the discharge parameters, power and energy consumption of the reactor is determined. These are compared with the values obtained for a commercial heating device based on electrical resistance.

Resumen En este trabajo se reporta la síntesis del superconductor YBa2Cu3O7-δ mediante el método no convencional de sinterización por plasma en el rango de descarga luminiscente anormal (DLA). Las muestras se sometieron a diferentes temperaturas y tiempos de sinterización. Como referencia se usó una muestra superconductora obtenida por el método convencional (horno resistivo). La caracterización estructural de estas muestras se hizo por difracción de rayos X y refinamiento con el método de Rietveld. El comportamiento superconductor se determinó mediante el análisis de las curvas de magnetización en función de la temperatura según los procedimientos experimentales de enfriado en campo magnético cero (zero field cooling, ZFC) y enfriado con campo magnético aplicado (field cooling, FC). Las muestras sinterizadas por DLA presentaron características estructurales (ortorrómbica Pmmm) y superconductoras con una temperatura crítica de Tc~ 92 K, similares a las obtenidas por el método convencional, pero con una significativa reducción en las temperaturas y tiempos, bajo un ambiente adecuado de presión en el proceso de sinterización. © 2017. Acad. Colomb. Cienc. Ex. Fis. Nat. Abstract In this study we synthesized the YBa2Cu3O7-δ superconductor using the unconventional method of plasma sintering in the range of abnormal glow discharge (AGD). The samples were treated with different sintering temperatures and times. As reference we used a superconductor sample obtained by using the conventional method (resistive furnace). The structural characterization of these samples was performed by X-ray diffraction measurements and Rietveld refinements. Superconductivity behavior was determined by analyzing magnetization curves as a function of the temperature according to zero field cooling (ZFC) and field cooling (FC) experimental procedures. The samples sintered by AGD presented structural characteristics (orthorhombic Pmmm) and superconductivity with a critical temperature of Tc ~ 92 K, which were similar to those obtained by the conventional method, but with a significant reduction of temperature and time under proper pressure environment during the sintering process. © 2017. Acad. Colomb. Cienc. Ex. Fis. Nat.

En este artículo analizamos el sistema La1.5+xBa1.5+x-yCa yCu3Oz, basados en la producción de muestras que se encuentran en el rango de fase única, fase pura, propuesta por West [1]. Reportamos la producción y caracterización de los sistemas La1.1Ba1.4Ca0.5Cu3Oz, La1.1Ba1.5Ca0.4Cu3Oz, La1.1Ba1.6Ca0.3Cu3Oz, La1.2Ba1.3Ca0.5Cu3Oz, La1.2Ba1.4Ca0.4Cu3Oz, La1.3Ba1.2Ca0.5Cu3Oz, en contraste con los reportados en artículos previos [2]. Las muestras fueron producidas por el método de reacción de estados solido (SSR) con una temperatura de sinterizado de 850 ºC. Se presenta la caracterización morfológica referente al comportamiento granular utilizando la técnica de Microscopía electrónica de barrido (SEM); La caracterización estructural, se determinó sometiendo las muestras a la técnica de Difracción de Rayos X (DRX) y los parametros estructurales a partir del metodo de refinamiento Rietveld en el sofware FullProf. Los materiales resultantes tipo perovskita poseen celdas unitarias tetragonal tipo P4/mmm con a 3.89 , b 3.89 y c 11.60 . Los sistemas tienen fase única, fase pura como lo propone West. La temperatura crítica es comparada con los parametros x e y. In this paper we analyzed the La1.5+xBa1.5+x-yCa yCu3Oz system, based on the production of samples that are in the range of single phase, pure phase, proposed by West [1]. We report the production and characterization La1.1Ba1.4Ca0.5Cu3Oz, La1.1Ba1.5Ca0.4Cu3Oz, La1.1Ba1.6Ca0.3Cu3Oz, La1.2Ba1.3Ca0.5Cu3Oz, La1.2Ba1.4Ca0.4Cu3Oz, La1.3Ba1.2Ca0.5Cu3Oz, systems, in contrast to those reported in previous articles [2]. The material was produced by the solid state reaction method (SSR) with a sintered temperature between 820 and 850 ºC. The morphological characterization with respect to the granular behavior using the Scanning Electron Microscopy (SEM) technique is showed; the structural characterization is obtained submitting the specimen to X Rays Diffraction (DRX) and the structural parameters are got implementing the Rietveld refinement method in software FullProf; the material results to possess tetragonal unitary cells type P4/mmm perovskite with a 3.89 , b 3.89 and c 11.60. Systems have a pure phase, single phase as proposed by West. The critical temperature is compared with the parameters x and y.

En este artículo se estudian y analizan las propiedades físicas superficiales en muestras de vidrio plano colombiano, específicamente de vidrio sodo-cálcico, por medio de técnicas experimentales como microscopía electrónica de barrido (SEM), microscopía de fuerza atómica (AFM) y análisis térmico diferencial (DTA). Con SEM se detectaron incrustaciones superficiales de Ti y Co y de infundidos cuyo análisis químico indicó que en más del 92% corresponden a SiO2. La rugosidad microscópica, analizada mediante AFM, se relacionó con el tiempo de envejecimiento de la muestra. Se observó la influencia de cemento diluido sobre las propiedades de la superficie. El análisis termodiferencial (DTA) permitió detectar cambios relacionados con la absorción de agua molecular y, a altas temperaturas, la eliminación de agua ligada In this article we study and analize the surface physical propierties in samples of Colombian flat glass, specifically soda-lime glass, by scanning electronic microscopy (SEM), atomic force microscopy (AFM) and differential thermal analisys (DTA). The SEM results detected surface deposits of Ti and Co and infused whose chemical analisys indicated that over 92% is SiO2. The microscopic roughness, analized by AFM, was associated with the aging time of the sample. It was observed the influence of diluid cement on surface properties. DTA allowed detect changes related to absorption of molecular water and, at high temperatures, the removal of bound water

En este artículo se analiza el sistema La1,5+xBa1,5+x-y +x - y Ca yCu3Oz, con base en la producción de muestras que se encuentran en el rango de fase única, fase pura, propuesta por West [1]. El análisis estructural fue realizado mediante difracción de rayos X (DRX), logrando establecer un primer indicio de la presencia de fase pura en el sistema La1,5+xBa1,5+x-yCa yCu3Oz, el cual fue corroborado a partir del refinamiento Rietveld. Los parámetros estructurales de las muestras producidas se obtuvieron por el método estándar de reacción de estado sólido. Este primer indicio fue confirmado también con medidas de microscopía electrónica de barrido (SEM), y la composición elemental se verificó a través de energía por dispersión de rayos X (EDX). Finalmente, y teniendo en cuenta los análisis efectuados, se puede concluir que la mayoría de las muestras presentan características superconductoras de alta anisotropía planar, y que, aunque el rango total propuesto por West corresponde a sistemas superconductores, no todas las muestras registran fase pura In this paper it is analyzed the system La1,5+xBa1,5+x-yCa yCu3Oz, based on the production of samples that are in the range of single phase, pure phase, proposed by West [1]. The structural analysis was carried out starting from X Rays Diffraction (XRD), being able to establish a first indication of the presence of pure phase in the system La1,5+xBa1,5+x-yCa yCu3Oz, which was corroborated through the refinement Rietveld. Structural parameters of the samples were obtained by the standard method of reaction of solid state. This first indication was also corroborated with measures of Scanning Electronic Microscopy (SEM), and the elementary composition was verifyed through Energy for Dispersion of X Rays (EDX). Finally, and having into account the carried out analysis, it is shown that most of the samples present superconductor characteristics of high planar anisotropy and that although the total range proposed by West corresponds to superconductor systems, not all the samples present pure phase

La aplicación de la descarga luminiscente anormal al proceso de sinterización es una técnica reciente que representa disminución en el tiempo requerido para el proceso de sinterización de muestras, tanto metálicas como cerámicas, y un menor consumo de energía, debido a que el calentamiento se realiza en forma directa por el bombardeo de los iones y átomos neutros sobre la superficie del cátodo donde generalmente se localiza la muestra. En este trabajo se estudia la aplicación de la descarga luminiscente anormal de baja presión como método alternativo para realizar la etapa de sinterización del material cerámico YBa2Cu3O7-δ, se comparan la estructura y la microestructura de muestras sinterizadas en la descarga luminiscente con las de muestras sinterizadas en horno resistivo, el cual es comúnmente utilizado para la producción de este tipo de materiales. Para ello se realiza el análisis estructural y morfológico por DRX y SEM, respectivamente, de las muestras obtenidas por los dos procedimientos. Los resultados experimentales permitieron establecer una estructura similar para ambos casos y una menor porosidad superficial en las muestras sinterizadas por plasma. Además, en el proceso de sinterización por plasma se observa una ligera contaminación de la superficie de las muestras debida a la pulverización catódica, la cual es fácilmente eliminada por métodos mecánicos.

1 recurso en línea (ii, 97 páginas) Ilustraciones, figuras, tablas., Este documento sintetiza las etapas implementadas con el objeto de llevar a óptimo desarrollo el trabajo de tesis titulado “Producción y Caracterización del Sistema CaMn1-xTixO3 (Con x= 0.25, 0.5, 0.75)”; elaborado como requisito fundamental para optar por el grado de Magister en Ciencias-Físicas. El interés por el sistema tipo perovskita CaMn1-xTixO3 nace de las propiedades magnéticas y eléctricas que exhiben los compuestos CaMnO3 y CaTiO3, las cuales pueden modificarse cambiando la estructura y/o estequiometria. Al producir el sistema CaMn1-xTixO3 fundamentado en los compuestos mencionados anteriormente se busca un material que muestre propiedades eléctricas y magnéticas, para obtener un compuesto multiferróico y evaluar sus propiedades magnéticas y eléctricas. Para el desarrollo del trabajo se aprovechó la experiencia del GFM en la producción de materiales tipo perovskita para impulsar y orientar las diferentes etapas del proyecto. Para cumplir los objetivos y alcance del proyecto se realizó la síntesis del sistema tipo perovskita CaMn1-xTixO3 por medio del método de reacción de estado sólido y, la evaluación de las propiedades estructurales, magnéticas y eléctricas mediante refinamiento Rietveld de rayos X, de magnetización en función de la temperatura y del campo aplicado y, medidas de polarización eléctrica., Bibliografía y webgrafía: páginas 93-97., Maestría, Magíster en Ciencias - Física