Search

Highly crystalline perovskite films with large grains and few grain boundaries are conducive for efficient and stable perovskite solar cells. Current methods for preparing perovskite films are mostly based on a fast crystallization process, with rapid nucleation and insufficient growth. In this study, MAPbI3 perovskite with inhibited nucleation and promoted growth in the TiO2/ZrO2/carbon triple mesoscopic scaffold was crystallized by modulating the precursor and the crystallization process. N-methylformamide showed high solubility for both methylammonium iodide and PbI2 and hampered the formation of large colloids in the MAPbI3 precursor solution. Furthermore, methylammonium chloride was added to reduce large colloids, which are a possible source of nucleation sites. During the crystallization of MAPbI3, the solvent was removed at a slow controlled speed, to avoid rapid nucleation and provide sufficient time for crystal growth. As a result, highly oriented MAPbI3 crystals with suppressed non-radiative recombination and promoted charge transport were obtained in the triple mesoscopic layer with disordered pores. The corresponding hole-conductor-free, printable mesoscopic perovskite solar cells exhibited a highest power conversion efficiency of 18.82%. The device also exhibited promising long-term operational stability of 1000 h under continuous illumination at maximum power point at 55 ± 5 °C and damp-heat stability of 1340 h aging at 85 °C as well as 85% relative humidity.

Abstract: 3D organic–inorganic lead halide perovskites have shown great potential in efficient photovoltaic devices. However, the low stability of the 3D perovskite layer and random arrangement of the perovskite crystals hinder its commercialization road. Herein, a highly oriented 2D@3D ((AVA)2PbI4@MAPbI3) perovskite structure combining the advantages of both 2D and 3D perovskite is fabricated through an in situ route. The highest power conversion efficiency (PCE) of 18.0% is observed from a 2D@3D perovskite solar cell (PSC), and it also shows significantly enhanced device stability under both inert (90% of initial PCE for 32 d) and ambient conditions (72% of initial PCE for 20 d) without encapsulation. The high efficiency of 18.0% and nearly twofold improvement of device stability in ambient compared with pure 3D PSCs confirm that such 2D@3D perovskite structure is an effective strategy for high performance and increasing stability and thus will enable the timely commercialization of PSCs. [ABSTRACT FROM AUTHOR]

Highly crystalline perovskite films with large grains and few grain boundaries are conducive for efficient and stable perovskite solar cells. Current methods for preparing perovskite films are mostly based on a fast crystallization process, with rapid nucleation and insufficient growth. In this study, MAPbI 3 perovskite with inhibited nucleation and promoted growth in the TiO 2 /ZrO 2 /carbon triple mesoscopic scaffold was crystallized by modulating the precursor and the crystallization process. N-methylformamide showed high solubility for both methylammonium iodide and PbI 2 and hampered the formation of large colloids in the MAPbI 3 precursor solution. Furthermore, methylammonium chloride was added to reduce large colloids, which are a possible source of nucleation sites. During the crystallization of MAPbI 3 , the solvent was removed at a slow controlled speed, to avoid rapid nucleation and provide sufficient time for crystal growth. As a result, highly oriented MAPbI 3 crystals with suppressed non-radiative recombination and promoted charge transport were obtained in the triple mesoscopic layer with disordered pores. The corresponding hole-conductor-free, printable mesoscopic perovskite solar cells exhibited a highest power conversion efficiency of 18.82%. The device also exhibited promising long-term operational stability of 1000 h under continuous illumination at maximum power point at 55 ± 5 °C and damp-heat stability of 1340 h aging at 85 °C as well as 85% relative humidity., Competing Interests: The authors declare that they have no conflicts of interest in this work., (© 2021 The Authors. Publishing Services by Elsevier B.V. on behalf of KeAi Communications Co. Ltd.)