It is known that the temperature of crystallization during the synthesis of zeolite is one of the most important process parameters. However, during the research work on the synthesis of zeolite 13X and the introduction of this material into regular industrial production, it was noticed that the heating rate of the starting reaction suspension can have an equally important influence. This influence can be so pronounced that a difference of just a few minutes in reaching the crystallization temperature can make a significant difference in product quality, affect the presence of other phases in the crystal, or even determine the direction of zeolite crystallization. Therefore, the aim of this work was to show the influence of the heating rate on the quality of the obtained 13X zeolite powders. The obtained samples were analysed in terms of crystallinity (by X-ray diffraction), chemical composition, granulometry and specific surface area (by Brunauer-Emmett-Teller analysis), and regarding water and CO2 adsorption capacities. Additionally, scanning electron microscopy analysis of the samples showed the morphological characteristics of different 13X zeolite powders. The analysis results of the obtained powders confirmed the influence of the heating rate and helped to define the optimal synthesis parameters i.e. the initial temperature and heating time, that resulted in stable product quality.

Increasing amounts of residues and waste materials coming from industrial activities in different processes have become an increasingly urgent problem for the future. The paper presents the problem of mine tailings generated in mine “Sase” (Republic of Srpska, Bosnia and Herzegovina) with high metal content (Pb, Cu and Zn). Dumpsite of this tailing represents potential risk for water bodies in the vicinity of this location. Chosen treatment process was stabilization/solidification (S/S). Inorganic agents used in this study were fly ash and red mud that represent secondary industrial waste generated on locations relatively near the mine. Therefore, their application can be used as an example of a sustainable solution of regional environmental problem. Further investigations are related to the impact of various factors on metals leaching from mine tailings solidified/stabilized material using the above mentioned immobilization agents. The performance of the immobilizing procedures was examined using several leaching tests: ANS 16.1, TCLP, DIN, MWLP. The results indicated that all S/S samples can be considered as non-hazardous waste, as all leached metal concentrations met the set criteria. These results will further enable the modelling of metals behaviour during long-term leaching from treated mine tailing. The data are invaluable in terms of economically and environmentally sound management of mine tailing.