Ceramics based on zirconium dioxide are very important compounds for dental, implant, and structural material applications. Despite the fact that tetragonally stabilized YSZ has been well studied, the search for new compositions of zirconia-based ceramics is still in progress. The ZrO2-CeO2 system is one of the alternatives for YSZ materials, but there is conflicting experimental data on its phase composition and mechanical properties depending on the ratio of components. In this study, we investigated the phase composition, and microstructural, mechanical, and physical properties of (1 − x)∙ZrO2-x∙CeO2 (step of x = 0.05) ceramics obtained by the solid-state sintering process from micron-sized powders. For the characterization of samples, XRD, Raman spectroscopy, SEM, the Vickers Microhardness Test, and dielectric spectroscopy were implemented. The results showed that by varying the CeO2 concentration, it is possible to synthesize stable tetragonal ZrO2 at room temperature with a high microhardness HV0.05 value of ~1500, low porosity (~2.5%), and a high dielectric constant of 36. The pronounced combined effect of tetragonal phase formation, densification, and grain size reduction on the mechanical and dielectric properties of the experimental samples was investigated. Refined experimental data make it possible to synthesize high-quality zirconia–ceria ceramics for use as refractories, dispersed nuclear fuel, or solid oxide fuel cells.

In this work, using a mechanochemical solid-phase synthesis method, ZrO2—CeO2 ceramics doped with yttrium were obtained, which have great prospects for use as a basis for dispersed nuclear fuel materials or inert nuclear fuel matrices. The purpose of this work was to study the formation of the ZrO2—CeO2 phase composition, depending on the concentration of yttrium dopant, as well as to study their structural and strength properties. The relevance of this study is in obtaining new data on the properties of composite ceramics based on oxides having a cermet structure, as well as the effect of doping with yttrium on increasing the resistance of ceramics to deformation and thermal properties. During the studies, the dynamics of the phase transformations depending on the concentration of the dopant, as well as changes in the structural characteristics and dislocation density, were established. It was found that at a dopant concentration of 0.25 mol, the main phase in the structure was Ce3ZrO8–triclinic P1 (1), the formation of which led to an increase in the mechanical and strength properties of the ceramics as well as a 1.5-fold increase in the thermal conductivity coefficient.