The use of rubber crumbs provides a viable solution for alleviating the disposal problem of waste tires. In this study, rubberized sulfur concrete (RSC) was researched to investigate the optimal mixture proportion and to improve the mixing process in terms of compressive strength and durability performance. For the mixture of the RSC, sand, rubber particles, and micro-filler were adopted as aggregates and sulfur was used for the binding material. Moreover, two mixing processes were applied: the dry mixing process and the wet mixing process. Based on the test results, the increment of rubber particles in the mixture led to a decrease in the compressive strength for both the dry and wet mixing processes. To minimize the voids between the sand and rubber particles, the micro-filler was used at 5% of the total volume. The amount of sulfur varied slightly depending on the mixing process: 30% sulfur for the dry mixing process and 34% sulfur for the wet mixing process, respectively. Consequently, compared to the dry mixing process, the wet mixing process increased the bonding force between sulfur and rubber powder due to the simultaneous heating and combining. In toughness, the wet mixing process demonstrates a 40% higher energy absorption capability compared to the dry mixing process. For the durability performance of the RSC, the mixture with 20% rubber particles produced using the wet mixing process exhibited better corrosion and freeze–thaw resistance. [ABSTRACT FROM AUTHOR]

The purpose of this study is to optimize the composition of CSA (calcium sulfoaluminate) cement with sodium silicate (Na2SiO3) and gypsum for binder jetting 3D printing. The preliminary test was carried out with an applicator to decide the proper thickness of one layer before using the 3D printer. A liquid binder was then selected to maintain the shape of the particles. Based on the results, the optimal mixture of dry materials and a liquid activator was derived through various parametric studies. For dry materials, the optimum composition of CSA cement, gypsum, and sand was suggested, and the liquid activator made with sodium silicate solution and VMA (viscosity modified agent) were selected. The setting time with gypsum and sodium silicate was controlled within 30 s. In case of the delayed setting time and the rapid setting mixture, the jetting line was printed thicker or thinner and the accuracy of the printout was degraded. In order to adjust the viscosity of the liquid activator, 10% of the VMA was used in 35% of sodium silicate solution and the viscosity of 200–400 cP was suitable to be sprayed from the nozzle. With this optimal mixture, a prototype of atypical decorative wall was printed, and the compressive strength was measured at about 7 MPa. [ABSTRACT FROM AUTHOR]