Electrodes containing 60 wt% micron-sized silicon were investigated with electrolytes containing carbonate solvents and either LiPF6 or lithium bis(fluorosulfonyl)imide (LiFSI) salt. The electrodes showed improved performance, with respect to capacity, cycling stability, rate performance, electrode resistance and cycle life with the LiFSI salt, attributed to differences in the solid electrolyte interphase (SEI). Through impedance spectroscopy, cross sectional analysis using transmission electron microscopy (TEM) and focused ion beam (FIB) in combination with scanning electron microscopy (SEM), and electrode surface characterization by X-ray photoelectron spectroscopy (XPS), differences in electrode morphological changes, SEI composition and local distribution of SEI components were investigated. The SEI formed with LiFSI has a thin, inner, primarily inorganic layer, and an outer layer dominated by organic components. This SEI appeared more homogeneous and stable, more flexible and with a lower resistivity than the SEI formed in LiPF6 electrolyte. The SEI formed in the LiPF6 electrolyte appears to be less passivating and less flexible, with a higher resistance, and with higher capacitance values, indicative of a higher interfacial surface area. Cycling in LiPF6 electrolyte also resulted in incomplete lithiation of silicon particles, attributed to the inhomogeneous SEI formed. In contrast to LiFSI, where LiF was present in small grains in-between the silicon particles, clusters of LiF were observed around the carbon black for the LiPF6 electrolyte.

International audience; The photoluminescence of two series of A- and B-site Eu3+ substituted (SrxBa1-x)(2)CaWyMo1-yO6 double perovskite phosphor materials, (SrxBa1-x)(1.96)Eu0.02K0.02CaWyMo1-yO6 and (SrxBa1-x)(2)Ca0.96Eu0.02Li0.02WyMo1-yO6 (x and y=0, 0.25, 0.50, 0.75, and 1), were studied systematically as a function of stoichiometry and crystal structure. The Eu3+ lattice sites controlled by co-doping with either K or Li were confirmed by Raman spectroscopy. The variation in integrated emission intensity and emission colour over the experimental matrix was examined using statistical tools, and the observed trends were rationalized based on the physical and electronic structure of the phosphors. Phosphors with Eu on B-site with maximum Sr content had remarkably higher emission intensities than all other materials, but the emission was more orange than red due to domination of the D-5(0) - F-7(1) (595 nm) transition of Eu3+. The relative intensities of the D-5(0) - F-7(2) (615 nm) and D-3(0) - F-7(1) transitions of Eu3+, and thus the red-shift of the emission, decreased linearly with increasing Sr content in the A-site Eu-substituted phosphors, and reached a maximum for Sr1.96Eu0.02K0.02CaW0.25Mo0.75O6. A maximum external quantum efficiency of 17% was obtained for the phosphor Sr2Ca0.7Eu0.15Li0.15W0.5Mo0.5O6 with Eu on B-site. (C) 2016 Elsevier Inc. All rights reserved.