Search

In this work, a process chain for the fabrication of dense zirconia parts will be presented covering the individual steps feedstock compounding, 3D printing via Fused Filament Fabrication (FFF) and thermal postprocessing including debinding and sintering. A special focus was set on the comprehensive rheological characterization of the feedstock systems applying high‐pressure capil‐lary and oscillation rheometry. The latter allowed the representation of the flow situation especially in the nozzle of the print head with the occurring low‐shear stress. Oscillation rheometry enabled the clarification of the surfactant’s concentration, here stearic acid, or more general, the feedstocks composition influence on the resulting feedstock flow behavior. Finally, dense ceramic parts (best values around 99 % of theory) were realized with structural details smaller than 100 μm.

In this work, a process for the realization of new polymer matrix composites with nanosized barium ferrite (BaFe12O19) as ferrimagnetic filler, acryl butadiene styrene (ABS) as polymer matrix and an extrusion-based method, namely fused filament fabrication (FFF), as 3D printing method will be described comprehensively. The whole process consists of the individual steps material compounding, rheological testing, filament extrusion, 3D-printing via FFF and finally a widespread specimen characterization regarding to appearance, mechanical properties like tensile and bending behavior as well as the aspired magnetic properties. Increasing ferrite amounts up to 40 vol.% (equal 76 wt.%) cause a reduction of the ultimate stress and an increase of the magnetic polarization as well as of the energy product (BH)max in comparison to the pure polymer matrix. In addition, an extensive discussion of typical printing defects and their consequences on the device properties will be undertaken.

The ceramic injection molding (CIM) process is a cost-effective powder-based near net shape manufacturing process for large-scale production of complex-shaped ceramic functional components. This paper presents the rheological analysis of environmentally friendly CIM feedstock formulations based on the binder components polyvinyl butyral (PVB) and polyethylene gycol (PEG). The prepared PVB/PEG-based alumina molding compounds were investigated with respect to their PVB:PEG ratios as well as to their powder filling degrees in the range between 50 and 64 vol.%. Corresponding viscosities and shear stresses were determined for increasing shear rates to show the effects of increased PEG content and solid loadings on them. Two single reactor components were injection molded and subsequently joined in their green state for fabrication of an alumina microreactor. The intended purpose of the alumina microreactors is their potential application as wear-resistant and hydrothermal stable multifunctional devices (&micro, mixer, &micro, reactor, &micro, analyzer) for continuous hydrothermal synthesis (CHTS) of metal oxide nanoparticles in supercritical water (sc-H2O) as the reaction medium.

With respect to rapid prototyping of ceramic components, there are known only a few processes (stereo lithography, binder jetting). In this work, a new process chain is described in detail, showing that ceramics can be printed in a very cost-efficient way. We developed a ceramic&ndash, polymer composite as filament material that can be printed on a low-cost fused filament fabrication (FFF) desktop printer, even with very small nozzle sizes enabling very small geometric feature sizes. The thermal post-processing, with debinding and sintering, is very close to the ceramic injection molding (CIM) process chain.