Search

Gum rosin (GR) was used as a natural additive to improve the compatibility between polylactic acid, PLA, and poly(butylene adipate-co-terephthalate, PBAT, blended with 20 wt.% of PBAT (PLA/PBAT). The PBAT was used as a soft component to increase the ductility of PLA and its fracture toughness. The coalescence of the PBAT domains was possible due to the plasticization effect of the GR component. These domains contributed to increasing the toughness of the final material due to the variation and control of the PBAT domains’ size and consequently, reducing the stress concentration points. The GR was used in contents of 5, 10, 15, and 20 phr. Consequently, the flexural properties were improved and the impact resistance increased up to 80% in PLA/PBAT_15GR with respect to the PLA/PBAT formulation. Field emission scanning electron microscope (FESEM) images allowed observing that the size of PBAT domains of 2–3 µm was optimal to reduce the impact stress. Differential scanning calorimetry (DSC) analysis showed a reduction of up to 8C on the PLA melting temperature and up to 5.3C of the PLA glass transition temperature in the PLA/PBAT_20GR formulation, which indicates an improvement in the processability of PLA. Finally, transparent films with improved oxygen barrier performance and increased hydrophobicity were obtained suggesting the potential interest of these blends for the food packaging industry.

[EN] The objective of this study was to investigate the thermal expansivities and degradation properties for several in vitro conditioned biodegradable poly(lactic acid)/hydroxyapatite (PLA/HA) and poly(lactic acid)/b-tricalcium phosphate (PLA/ bTCP) composites with different mass% of the particle reinforcements (i.e. 10, 20 and 30). The samples were prepared by extrusion followed by injection moulding and incubated in a customized simulated body fluid at 37 C over 60, 90, 120, 150 and 180 days, respectively. Thermal expansion and degradation properties of in vitro conditioned samples, along with dynamic mechanical properties of unconditioned ones, were systematically investigated through coefficients of linear thermal expansion and thermal strain changes, decomposition temperatures, mass changes and per cent residues. The results indicated that PLA/bTCP composites performed better than PLA/HA composites, irrespective of their filler mass%, revealing high values of glass transition temperatures, around a mean value of 65 C, both on dynamic mechanical analysis and on dilatation measurements but lower values on their degradation temperatures, such as 360 C. The results suggest the feasibility of tailoring high-loaded osteoconductive fillers-reinforced PLA composites for various medical and engineering applications.

[EN] Insights within thermal expansion, conductivity, and decomposition dependencies with temperature on symmetrical and unsymmetrical layered carbon (CF) or basalt (BF) fabrics in combination with flax fibers (FF) were approached. Driven by commercial application and environmental concerns, the paper draws attention on a modified formula of cyanate ester with a common epoxy resin under an optimized ratio of 70:30 (vol%) as well as on the hybrid reinforcements stacking sequences. Synergetic effects were debated in terms of the CF and BF stacking sequences and corresponding volume fraction followed by comparisons with values predicted by the deployment of hybrid mixtures rules (RoHM/iRoHM). CF hybrid architectures revealed enhanced effective thermophysical properties over their BF counterparts and both over the FF-reinforced polymer composite considered as a reference. Thermal conductivities spread between 0.116 and 0.299 W m-1 K-1 from room temperature up to 250 C on all hybrid specimens, giving rise to an insulator character. Concerning the coefficient of thermal expansion, CF hybrid architectures disclosed values of 1.236 10-6 K-1 and 3.102 10-6 K-1 compared with BF affine exhibiting 4.794 10-6 K-1 and 6.245 10-6 K-1, respectively, with an increase in their volume fraction.