Search

This paper presents the results of the optimization of electrophoretic deposition parameters for manufacturing of nc-TiO2/chitosan composite coatings on X2CrNiMo17-12-2 steel as well as characterization of their microstructure, electrochemical properties and adhesion to the substrate. The parameters of the deposition, such as composition, pH and zeta potential of suspensions as well as voltage and process time were investigated. The microstructure of the coatings was characterized using scanning and transmission electron microscopy. Obtained coatings were crack-free and uniform. The adhesion strength to the substrate was measured by scratch-test method. The deposited coatings improve corrosion resistance of steel, what was confirmed by the results of the potentiodynamic polarization test in Ringer’s solution.

Porous hydroxyapatite doped SiO2 coatings were electrophoretically deposited (EPD) on commercially pure titanium. The influence of EPD parameters on coatings quality was investigated. Microstructural observation was done using transmission and scanning electron microscopy as well as X-ray diffractometry.

In this study, chitosan coatings were electrophoretically deposited (EPD) on near-β Ti-13Nb-13Zr alloy. The influence of colloidal solution composition and EPD parameters on the quality of chitosan coatings was investigated. It was established that the uniformity of as-deposited chitosan coatings is highly dependent on the chemical composition of the solution used for EPD, the pH, electrophoretic mobility and zeta potential of chitosan colloidal molecules, as well as EPD parameters, such as potential difference value and deposition time. The microstructure of the coatings was investigated using electron microscopy and X-ray diffractometry. The coatings 350 nm thick were homogeneous and exhibited an amorphous structure. The coatings had low hardness and Young’s modulus. The effect of surface of the substrate preparation prior to coating deposition on the adhesion of chitosan coatings to the Ti-13Nb-13Zr alloy was also investigated. The coatings exhibited good adhesion to the non-acid-etched surface of the titanium alloy.

The aim of the work was to obtain thin bismuth oxide films containing, at room temperature, the Bi1,5Er0,5O3 phase. This phase corresponds to the structure of the high-temperature δ-Bi2O3 phase, in pure bismuth oxide, characterized by the highest ionic conductivity of all known solid state ionic conductors. The high-temperature δ-Bi2O3 phase with the face centered cubic structure, in pure bismuth oxide, occurs only at temperature above 730°C. Stabilization of the δ-Bi2O3 phase at room temperature was achieved by an addition of the erbium together with the employment of the Pulsed Laser Deposition (PLD) technique. The influence of an amount of Er alloying and the film thickness on surface morphology, microstructure, phase composition of thin films were investigated. The velocity of deposition of thin layers of bismuth stabilized with erbium in the PLD process using the Nd: YAG laser was about 0.5 nm/s. The investigation results of erbium doped bismuth oxide thin films deposited onto (0001) oriented Al2O3 monocrystalline substrate are presented. Thin films of uniform thickness, without cracks, and porosity were obtained. All deposited thin films (regardless of the film thickness or erbia (Er2O3) content) exhibited a columnar structure. In films stabilized with erbium, up to approx. 250 nm thickness, the columns have a diameter at the base from 25 to 75 nm. The columns densely and tightly fill the entire volume of the films. With increasing of the film thickness increases, porosity also significantly increases. In thin layers containing from 20 to 30 mole % Er2O3 the main identified phase at room temperature is Bi1.5Er0.5O3. It is similar to the defective fluorite-type structure, and belongs to the Fm-3m space group. This phase corresponds to the structure of the high-temperature δ-Bi2O3 phase in pure bismuth oxide. [ABSTRACT FROM AUTHOR]

This paper presents the results of the optimization of electrophoretic deposition parameters for manufacturing of nc-TiO2/ chitosan composite coatings on X2CrNiMo17-12-2 steel as well as characterization of their microstructure, electrochemical properties and adhesion to the substrate. The parameters of the deposition, such as composition, pH and zeta potential of suspensions as well as voltage and process time were investigated. The microstructure of the coatings was characterized using scanning and transmission electron microscopy. Obtained coatings were crack-free and uniform. The adhesion strength to the substrate was measured by scratch-test method. The deposited coatings improve corrosion resistance of steel, what was confirmed by the results of the potentiodynamic polarization test in Ringer's solution. [ABSTRACT FROM AUTHOR]

Porous hydroxyapatite doped SiO2 coatings were electrophoretically deposited (EPD) on commercially pure titanium. The influence of EPD parameters on coatings quality was investigated. Microstructural observation was done using transmission and scanning electron microscopy as well as X-ray diffractometry. The coatings consisted of spherical micro and nanocrystalline hydroxyapatite (HAp) as well as amorphous SiO2 nanoparticles. The coatings exhibited open porosity with pore diameter up to 1 μm and due to presence of nanoparticles high surface development. It was found that application of SiO2/HAp coating increase corrosion resistance of titanium in Ringer's solution. [ABSTRACT FROM AUTHOR]

Abstract: The work is devoted to the investigation of nanohardness and tribological properties in TiB2 coatings deposited on austenitic steel substrates using an unbalanced magnetron sputtering with the focus on the coatings prepared under small negative bias to reduce compressive stresses. The coating prepared under floating potential exhibited nanocomposite microstructure with the size of TiB2 (hcp) nanocrystallites in the range of 2–7nm. It is in contrast with the textured microstructure typically developed under higher negative bias. The reduction of the compressive stresses up to −0.4GPa while keeping the nanohardness >30GPa and the coefficient of friction of 0.77 were obtained in this coating. The highest nanohardness of 48.6±3.1GPa and indentation modulus of 562±18GPa were achieved at −100V bias in the textured coating. The friction mechanisms include mechano-chemical formation of a tribological oxide film between the sliding partners combined with an abrasive wear. [Copyright &y& Elsevier]

Abstract: Nanocrystalline TiO2 powders were electrophoretically deposited on the surface of Ti–6Al–7Nb alloy substrate. Post heat treatment at 850 °C was performed to improve the adhesion strength of the coating. The microstructure of the coating and substrate has been examined by light microscopy, scanning electron microscopy, analytical TEM methods (SAED, EDS) and X-ray diffraction. TEM investigations of cross-section thin foils allowed for detailed analysis of the coating microstructure. The TiO2 film exhibited a nanocrystalline structure. SAED and XRD analyses show that the as-deposited nanocrystalline TiO2 films exhibited anatase and rutile phase. The micromechanical properties (microhardness, Young''s modulus) were measured. The results obtained show that TiO2 films have low hardness and Young''s modulus. During scratch tests any flaking or fracture was observed. [Copyright &y& Elsevier]