Purpose: To examine the long-term performance of bonded all-ceramic restorations, specifically veneers, in patients with amelogenesis imperfecta (AI). There are few studies of long-term outcomes using a minimally invasive procedure in these patients. This aspect is essential when treating young patients. All-ceramic restorations, especially veneers, offer a more tissue-preserving treatment but rely on successful bonding. However, due to the defect enamel in AI patients, the bond strength is lower. Materials and Methods: A retrospective evaluation of 40 subjects with AI (26 women, 14 men) was provided with a total of 360 bonded restorations (282 veneers, 78 crowns). The restorations were evaluated according to complications, survival, and success rate. Results: The patients were observed up to 25.3 years (mean 15.4 ± 4.3 years). The mean age when receiving the restorations was 18.5 ± 4.2 years. In total, 59 (16.4%) restorations with prosthetic complications were made, 29 of which (8.1%) were remade (6 due to esthetic reasons, all in one patient) and 30 (8.3%) were recemented (60% caused by trauma). We found 11 teeth with caries and 3 with endodontic complications. The overall survival rate was 91.9%, and the overall success rate was 83.6%. Conclusions: Bonded all-ceramic restorations with no active retention in AI patients have excellent performance. The most common complications were debonding and fractures. The treatment should be based on individual indications and be preceded by a multidisciplinary approach. [ABSTRACT FROM AUTHOR]

Resin-bonded prostheses were clinically evaluated following a mean period of 41 months. The abutment teeth were minimally prepared, and one groove was placed on the surface approximating the edentulous space. Retainers were treated using the Silicoater technique. Thirty-four prostheses were made for 32 patients. Four patients were lost from the study and 30 units were re-examined. Two prostheses had debonded. The results suggest that resin-bonded prostheses can be successful if meticulous attention is given to the procedures outlined. [ABSTRACT FROM AUTHOR]

In a randomized prospective study, two implant systems were compared in forty consecutive patients treated for mandibular edentulism. The patients were randomly allotted for treatment by the Brånemark[sup ®] two-stage (submerged) system (BRS), or the ITI[sup ®] one-stage (non-submerged) system. In all, 102 Brånemark selftapping implants and 106 ITI hollow screw implants were installed and all patients were treated with full bridges. Biological and prosthodontic parameters, complications, success rates, clinical efficacy, patient satisfaction and resource requirements were evaluated. No differences were found in plaque accumulation, bleeding or complications during the follow-up period. The BRS group showed deeper periimplant sulcus, less attached mucosa, larger bridge-mucosa distance and higher Periotest values. Prosthetic complications were not related to the configuration of the implant systems. After 3 years, the cumulative success rates were 97.9% and 96.8% for the Brånemark and ITI systems, respectively (difference not statistically significant). One implant in the BRS group had failed to osseointegrate at the time of abutment connection, and another was lost after 2 years due to progressive breakdown of bone. In the ITI group, three implants showed progressive bone loss after 1–3 years associated with periimplant infection. All 40 bridges were intact and remained stable throughout the study. There was general patient satisfaction, but about half the Brånemark patients reported difficulty in coping with the surgical procedures. Treatment time was similar for the two systems. It is concluded that both systems meet the current requirements for dental implant systems in the treatment of mandibular edentulism. [ABSTRACT FROM AUTHOR]

Three different methods of increasing the bond strength of resin to metal were tested: the original Silicoater technique, the Silicoater MD technique, and the Rocatec system. Metals used for the resin-bonded prostheses were gold, a cobalt-chromium (Co-Cr) alloy, and titanium. Silicoating increased the bond strength to sandblasted specimens. The original Silicoater technique produced the highest bond strengths, especially when used with the Co-Cr alloy and titanium. The Silicoater MD technique showed the lowest bond strengths for all of the test metals. Storage for 7 days with protective film on the silicoated surface did not affect the bond strength, as compared with specimens bonded immediately. The retention of the resin to the gold specimens (Rocatec system) decreased after thermocycling, but retention to the Co-Cr alloy and titanium was not affected. Various resin cements were tested and showed the same retention with the exception of Microfill Pontic, which gave a weaker bond. Scanning electron microscope (SEM) and energy-dispersive X-ray analysis (EDAX) of the specimens before and after the measurements gave no clear explanation of the differences in bond strengths between the test metals. However, it was concluded that silicoating of the metal surfaces contributed to the retention of the resin by chemical action, as no differences in adaptation of the resin to the metal were seen between specimens pretreated by sandblasting and those which were also silicoated. [ABSTRACT FROM AUTHOR]

The effect of phosphate concentration on corrosion was compared for two types of amalgam: a conventional alloy (ANA 68) and a high-Cu admixed alloy (Dispersalloy). The test specimens were stored for 4 months in electrolytes containing 85 mM NaCl and 85 mM NaCl with 2.5, 10, or 100 mM phosphate buffer respectively. The solutions were renewed each month and analyzed for Cu, Zn, Sn, Hg, and Ag in an atomic absorption spectrophotometer. The surfaces and cross-sections of the specimens were studied in a scanning electron microscope (SEM) with an energy dispersive detector (EDAX). The corrosion products, mainly Sn-compounds, at the surface of the amalgams were less in the solutions containing high concentrations of phosphate. In cross-section subsurface corrosion of the high-Cu amalgam was observed especially in specimens immersed in the NaCl solution without phosphate. The conventional amalgam showed surface corrosion only. The decrease in release of elements with time from the conventional amalgam in all the experimental solutions might indicate passivation. For the high-Cu amalgam the release of elements increased with time, except for Cu and Sn in the solution with 100 mM phosphate, indicating that phosphate inhibits corrosion of the Cu-Sn-phases. Release of corrosion products from the high-Cu amalgam was more dependent on the presence of phosphate than the conventional amalgam. [ABSTRACT FROM AUTHOR]

The effect of area ratio, chloride concentration and brushing on amalgam in contact with gold was studied by measuring the amounts of elements released in the electrolyte. A type III gold alloy was stored for 4 months in contact with a conventional amalgam, area relations &frac61; and &frac63;, in an electrolyte containing 85 mM NaCl with 10 mM phosphate buffer. A specimen with area relation &frac61; was also stored in a 10 mM NaCl solution with 10 mM phosphate buffer. The solutions were renewed each month and analyzed for Cu, Zn, Sn, Hg, and Ag in an atomic absorption spectrophotometer. Cross-sections of the amalgams were studied in a scanning electron microscope. The tendency for Sn and Cu to be released from the amalgam was greater than for the other elements. The Sn-release probably mainly originated from surface corrosion and Cu- release from subsurface corrosion. A stronger galvanic influence enhanced only the release of Cu, and to a less extent Zn. The subsurface corrosion of the amalgam and increasing release of Cu was, in contrast to the other elements, largely dependent on a high chloride concentration in the electrolyte. Light brushing of the specimens had no effect on the amounts of elements released. [ABSTRACT FROM AUTHOR]

One conventional and two high-Cu amalgams were tested for marginal microhardness after 2 months' corrosion in an 85 mM NaCl solution. Amalgams immersed in 200 mM phosphate buffer solution were used as controls. The microhardness tests were conducted on cross-sections of the amalgams 50 μm from the surface edges. The microstructure of the amalgams was studied in SEM and the amounts o(Sn, Cu, Zn, Ag, and Hg dissolved in the solutions were analyzed with an atomic absorption spectrophotometer. For the amalgams immersed in the NaCl solution the depth of corrosion after 2 months was between 50 and 400 μm. The specimens immersed in the phosphate solution showed no signs of subsurface corrosion. The marginal microhardness of all the amalgams was reduced after corrosion in the NaCl solution. The greatest microhardness in both the uncorroded and corroded states was shown in the two high-Cu amalgams. The reduction in marginal microhardness after corrosion can probably be attributed mainly to degradation of the gamma-2 phase for the conventional amalgam and to degradation of the η' phase for the two high-Cu amalgams. [ABSTRACT FROM AUTHOR]

Amalgam specimens were immersed for 30 days in 1) water, 2) 0.9% NaCl in water, 3) 0.9% NaCl and 10 mM phosphate buffer in water, and 4) 0.9% NaCl, 7.7 mM phosphate, and. 6.1 mM citric acid in water. The solutions were stored in stoppered glass tubes., Hg-drops were immersed in solutions 1, 2, and 3. The concentration of mercury vapor in the air above the solutions was measured once a day. After 30 days the amounts of Cu, Zn, Hg, and Ag in the solutions were analyzed by atomic absorption spectrophotornetry. The results showed that 0.9% NaCl alone or in combination with the additives increased the amounts of elements released into the solutions. The concentration of Hg0 in the glass tubes increased with the amount of Hg in the solutions, with the exception of solution No. 3, from which significantly less Hg&0 evaporated. The results indicate that the composition of the saliva, oral hygiene and dietary factors may be determinants of Hg0 emission-from amalgams-in the oral cavity. [ABSTRACT FROM AUTHOR]

The marginal microhardness of three different types of amalgam was tested alter 2 months' immersion in an aqueous solution of NaCl (85 mM) and phosphates (Na2HPO4 100 mM and NaH2PO4 100 mM). Amalgams immersed in distilled water were used as controls. The microhardness tests were conducted at a distance of 50 μm from the margins and at the bulk of each specimen. The solutions were analyzed for Sn, Cu, Zn, Ag, and Hg by means of atomic absorption spectrophotometry (AAS). A statistically significant reduction in the marginal micro-hardness after immersion in the test solution was found for the conventional and the high-Cu single composition amalgam but not for the high-Cu blended amalgam. SEM-examination of cross-sections of the amalgams revealed small areas of subsurface grain boundary corrosion, no deeper than 10 μm for all the amalgams. The SEM-examination of the specimens and AAS analysis of the solution indicated that the reduction in marginal microhardness was attributed mainly to corrosion of the Cu-rich phases for the high-Cu single composition amalgam and to corrosion of the γ2 phase for the conventional amalgam. The phosphates reduced the corrosion of the amalgams in the presence of NaCl. It is concluded that the marginal strength of dental amalgams in a corrosive environment is largely dependent upon their corrosion resistance. [ABSTRACT FROM AUTHOR]

Three types of amalgam, one conventional, ANA 68, and two with high copper content, Dispersalloy (dispersed type) and ANA 2000 (single composition type), were investigated. The amalgams were immersed for periods of 7 wk at a time, up to 35 wk, in 23 ml (37°C) of 0.9% NaCl aqueous solutions and in 0.9% NaCl solution buffered with NaH2PO4. (8.8 mM) and Na2HPO4 (1.2 mM). The amalgam specimens were embedded in epoxy resin. The surface area of amalgam exposed to the solutions was 0.2 cm² for each specimen. Every 7 wk the corrosion potential was measured, the amalgam specimens lightly brushed with a soft toothbrush, and the solutions renewed. After 14-21 wk and 35 wk the currents during anodic polarization sweeps over the amalgams were recorded. The corrosion potential for the high-Cu amalgams was somewhat more positive (noble) in the phosphate buffered solution than in the non-buffered solution during the 35 wk of corrosion. The phosphate buffer reduced the reactivity of the amalgams during anodic polarization. Corrosion made the amalgams more passive during the anodic polarization. However, all the elements leached from the amalgams into the solutions throughout the entire experiment. [ABSTRACT FROM AUTHOR]

An abstract is presented for the article "Brånemark system and ITI dental implant system for treatment of mandibular edentulism. A comparative randomized study: 3-year follow-up."

The aim of this study was to compare the quality of fixed partial dentures (FPDs) made in a Chinese dental laboratory with corresponding FPDs made in Swedish dental laboratories. Twenty-one patients were fitted with FPDs between March 2007 and December 2008. Single crowns and prostheses of up to seven units were made. All dentures, gold and CoCr alloys covered with ceramic, were produced in duplicate: one by a dental technician in China and the other by a dental technician in Sweden. The dentures were blind-tested with regard to marginal integrity, anatomic form and color, approximal and occlusal contacts, and time taken for adjustments. The composition of dentures was analyzed, and the material used, framework weight, compliance of the laboratories, and costs (material and labour) were recorded. There was no difference in the quality of marginal integrity, anatomic form, color, approximal and occlusal contacts, or in the time taken for adjustments. The bridge frameworks made in China were thinner and lighter (p<0.01) than those made in Sweden. Three FPDs from China showed elastic deformation when tested clinically and were considered too thin for clinical use. In 11 out of 14 orders from the Chinese laboratory, the gold alloy specified was not delivered and the cobalt-chromium alloy contained small amounts (0.19%) of nickel.The prostheses with gold-alloy frameworks from China cost 47% of those from Sweden (p<0.01) and those with cobalt/chromium frameworks 44% (p<0.01). In conclusion, the quality of the FPDs made in Sweden and China was comparable, with the exception of the dimension of the Chinese bridges, which in some cases was considered too weak. The gold alloy ordered from the Chinese laboratory was often not the alloy delivered and the CoCr alloy contained small amounts of nickel. FPDs from China cost less than half the price of those from Sweden.