Search

Low-temperature synthesis routes are necessary for selectively synthesizing many metastable solid-state materials. Here, we identify a cooperative effect that starting materials have in lowering temperatures in solid-state metathesis reactions by studying the formation of yttrium manganese oxide. Previous studies have shown that YMnO3 can be synthesized by ternary metathesis with an alkali halide being produced as a secondary product. In this contribution, we show that by using alkaline earth metals instead of alkali metals, the polymorph selectivity of the reaction is changed, as orthorhombic YMnO3 forms at lower temperatures than the hexagonal polymorph. Reactions were studied using ex post facto synchrotron X-ray diffraction. These experiments reveal that reactions using alkaline earth manganese oxides as a starting material require high temperatures to progress. Reaction temperatures can be lowered from 700 to 550 °C while maintaining phase selectivity by reacting both MgMn2O4 and CaMn2O4 with YOCl in a cooperative "cometathesis"reaction. The nascent halide salts appear to improve the reaction kinetics. Since the onset temperature for YMnO3 formation falls 50 °C below the MgCl2-CaCl2 liquidus, the enhanced reactivity is consistent with the surface melting of a nasscent salt byproduct at the interfaces. Cometathesis routes have similar phase selectivity and temperature reduction in reactions that form TbMnO3, ErMnO3, and DyMnO3. Cometathesis lowers reaction temperatures while preserving the reaction selectivity of the end members, making it a valuable approach for synthesizing metastable targets.

In the synthesis of complex oxides, solid-state metathesis provides low-temperature reactions where product selectivity can be achieved through simple changes in precursor composition. The influence of precursor structure, however, is less understood in solid-state synthesis. Here we present the ternary metathesis reaction (LiMnO2 + YOCl → YMnO3 + LiCl) to target two yttrium manganese oxide products, hexagonal and orthorhombic YMnO3, when starting from three different LiMnO2 precursors. Using temperature-dependent synchrotron X-ray and neutron diffraction, we identify the relevant intermediates and temperature regimes of reactions along the pathway to YMnO3. Manganese-containing intermediates undergo a charge disproportionation into a reduced Mn(II,III) tetragonal spinel and oxidized Mn(III,IV) cubic spinel, which lead to hexagonal and orthorhombic YMnO3, respectively. Density functional theory calculations confirm that the presence of Mn(IV) caused by a small concentration of cation vacancies (∼2.2%) in YMnO3 stabilizes the orthorhombic polymorph over the hexagonal. Reactions over the course of 2 weeks yield o-YMnO3 as the majority product at temperatures below 600 °C, which supports an equilibration of cation defects over time. Controlling the composition and structure of these defect-accommodating intermediates provides new strategies for selective synthesis of complex oxides at low temperatures.

Complex polymorphic relationships in the LnSiP3 (Ln = La and Ce) family of compounds are reported. An innovative synthetic method was developed to overcome differences in the reactivities of the rare-earth metal and refractory silicon with phosphorus. Reactions of atomically mixed Ln + Si with P allowed for selective control over the reaction outcomes resulting in targeted isolation of three new polymorphs of LaSiP3 and two polymorphs of CeSiP3. In situ X-ray diffraction studies revealed that the developed method bypasses formation of the thermodynamic dead-end, the binary SiP. Careful re-determination of the crystal structure ruled out the previously reported ordered centrosymmetric structure of CeSiP3 and showed that the main LnSiP3 polymorphs crystallize in the non-centrosymmetric Pna21 and Aea2 space groups featuring distinct distortions of the regular P square net to yield either cis–trans 1D phosphorus chains (Pna21) or disordered-2D phosphorus layers (Aea2). The disordered 2D nature of the P layers in the Aea2 LaSiP3 polymorph was confirmed by Raman spectroscopy. A unique centrosymmetric P21/c polymorph was observed for LaSiP3 and has a completely different crystal structure lacking P layers. Consecutive polymorphic transformations at increasing temperatures for LaSiP3(Pna21 → P21/c → Aea2) were derived from optimized synthetic profiles and confirmed by a combination of phonon computations and experimental in situ and ex situ annealings. Crystal structures of the LaSiP3 polymorphs were verified via advanced solid state NMR analysis using 31P MAS and 31P{139La} double resonance techniques. A combination of phonon and electronic structure calculations, NMR T1 relaxation times, UV/Vis/NIR spectroscopy, and resistivity measurements revealed that all the reported polymorphs are semiconductors with resistivities and thermal conductivities strongly dependent on the degree of distortion of P square layers in the crystal structure. Reported here, non-centrosymmetric LnSiP3 polymorphs with tunable resistivity and thermal conductivity provide a platform for the development of novel functional materials with a wide range of applications. [ABSTRACT FROM AUTHOR]

The synthesis of complex oxides at low temperatures brings forward aspects of chemistry not typically considered. This study focuses on perovskite LaMnO 3 , which is of interest for its correlated electronic behavior tied to the oxidation state and thus the spin configuration of manganese. Traditional equilibrium synthesis of these materials typically requires synthesis reaction temperatures in excess of 1000 °C, followed by subsequent annealing steps at lower temperatures and different p (O 2 ) conditions to manipulate the oxygen content postsynthesis (e.g., LaMnO 3+ x ). Double-ion exchange (metathesis) reactions have recently been shown to react at much lower temperatures (500-800 °C), highlighting a fundamental knowledge gap for how solids react at lower temperatures. Here, we revisit the metathesis reaction, LiMnO 2 + LaOX, where X is a halide or mixture of halides, using in situ synchrotron X-ray diffraction. These experiments reveal low reaction onset temperatures (ca. 450-480 °C). The lowest reaction temperatures are achieved by a mixture of lanthanum oxyhalide precursors: 2 LiMnO 2 + LaOCl + LaOBr. In all cases, the resulting products are the expected alkali halide salt and defective La 1-ϵ Mn 1-ϵ O 3 , where ϵ = x /(3 + x ). We observe a systematic variation in defect concentration, consistent with a rapid stoichiometric local equilibration of the precursors and the subsequent global thermodynamic equilibration with O 2 (g), as revealed by computational thermodynamics. Together, these results reveal how the inclusion of additional elements (e.g., Li and a halide) leads to the local equilibrium, particularly at low reaction temperatures for solid-state chemistry.

Recent computational studies have predicted many new ternary nitrides, revealing synthetic opportunities in this underexplored phase space. However, synthesizing new ternary nitrides is difficult, in part because intermediate and product phases often have high cohesive energies that inhibit diffusion. Here, we report the synthesis of two new phases, calcium zirconium nitride (CaZrN 2 ) and calcium hafnium nitride (CaHfN 2 ), by solid state metathesis reactions between Ca 3 N 2 and M Cl 4 ( M = Zr, Hf). Although the reaction nominally proceeds to the target phases in a 1:1 ratio of the precursors via Ca 3 N 2 + M Cl 4 → Ca M N 2 + 2 CaCl 2 , reactions prepared this way result in Ca-poor materials (Ca x M 2- x N 2 , x < 1). A small excess of Ca 3 N 2 (ca. 20 mol %) is needed to yield stoichiometric Ca M N 2 , as confirmed by high-resolution synchrotron powder X-ray diffraction. In situ synchrotron X-ray diffraction studies reveal that nominally stoichiometric reactions produce Zr 3+ intermediates early in the reaction pathway, and the excess Ca 3 N 2 is needed to reoxidize Zr 3+ intermediates back to the Zr 4+ oxidation state of CaZrN 2 . Analysis of computationally derived chemical potential diagrams rationalizes this synthetic approach and its contrast from the synthesis of MgZrN 2 . These findings additionally highlight the utility of in situ diffraction studies and computational thermochemistry to provide mechanistic guidance for synthesis.

A cloud-hosted web-based software application, nmfMapping, for carrying out a non-negative matrix factorization of a set of powder diffraction or atomic pair distribution function datasets is described. This application allows structure scientists to find trends rapidly in sets of related data such as from in situ and operando diffraction experiments. The application is easy to use and does not require any programming expertise. It is available at https://pdfitc.org/.

Complex polymorphic relationships in the LnSiP3 (Ln = La and Ce) family of compounds are reported. An innovative synthetic method was developed to overcome differences in the reactivities of the rare-earth metal and refractory silicon with phosphorus. Reactions of atomically mixed Ln + Si with P allowed for selective control over the reaction outcomes resulting in targeted isolation of three new polymorphs of LaSiP3 and two polymorphs of CeSiP3. In situ X-ray diffraction studies revealed that the developed method bypasses formation of the thermodynamic dead-end, the binary SiP. Careful re-determination of the crystal structure ruled out the previously reported ordered centrosymmetric structure of CeSiP3 and showed that the main LnSiP3 polymorphs crystallize in the non-centrosymmetric Pna21 and Aea2 space groups featuring distinct distortions of the regular P square net to yield either cis-trans 1D phosphorus chains (Pna21) or disordered-2D phosphorus layers (Aea2). The disordered 2D nature of the P layers in the Aea2 LaSiP3 polymorph was confirmed by Raman spectroscopy. A unique centrosymmetric P21/c polymorph was observed for LaSiP3 and has a completely different crystal structure lacking P layers. Consecutive polymorphic transformations at increasing temperatures for LaSiP3(Pna21 → P21/c → Aea2) were derived from optimized synthetic profiles and confirmed by a combination of phonon computations and experimental in situ and ex situ annealings. Crystal structures of the LaSiP3 polymorphs were verified via advanced solid state NMR analysis using 31P MAS and 31P{139La} double resonance techniques. A combination of phonon and electronic structure calculations, NMR T1 relaxation times, UV/Vis/NIR spectroscopy, and resistivity measurements revealed that all the reported polymorphs are semiconductors with resistivities and thermal conductivities strongly dependent on the degree of distortion of P square layers in the crystal structure. Reported here, non-centrosymmetric LnSiP3 polymorphs with tunable resistivity and thermal conductivity provide a platform for the development of novel functional materials with a wide range of applications.

In the synthesis of complex oxides, solid-state metathesis provides low-temperature reactions where product selectivity can be achieved through simple changes in precursor composition. The influence of precursor structure, however, is less understood in solid-state synthesis. Here we present the ternary metathesis reaction (LiMnO 2 + YOCl → YMnO 3 + LiCl) to target two yttrium manganese oxide products, hexagonal and orthorhombic YMnO 3 , when starting from three different LiMnO 2 precursors. Using temperature-dependent synchrotron X-ray and neutron diffraction, we identify the relevant intermediates and temperature regimes of reactions along the pathway to YMnO 3 . Manganese-containing intermediates undergo a charge disproportionation into a reduced Mn(II,III) tetragonal spinel and oxidized Mn(III,IV) cubic spinel, which lead to hexagonal and orthorhombic YMnO 3 , respectively. Density functional theory calculations confirm that the presence of Mn(IV) caused by a small concentration of cation vacancies (∼2.2%) in YMnO 3 stabilizes the orthorhombic polymorph over the hexagonal. Reactions over the course of 2 weeks yield o-YMnO 3 as the majority product at temperatures below 600 °C, which supports an equilibration of cation defects over time. Controlling the composition and structure of these defect-accommodating intermediates provides new strategies for selective synthesis of complex oxides at low temperatures.