Search

Electrically conductive composite polypropylene and poly(ethylene terephtalate) fabrics were obtained by coating with organo-silicon sol containing dispersed graphene particles. The graphene-modified coating was deposited on the fabric using the sol-gel method and the padding technique. To improve bonding of the coating to the fiber surfaces, the latter were activated with atmospheric pressure plasma in the form of corona discharge. The activation resulted in chemical and structural changes of the surfaces, roughening, and the formation of oxygen-containing functional groups, as evidenced by SEM with 3D analysis, EDS and XPS, and also measurements of contact angles with liquids. The padding with graphene-containing organo-silicon sol imparted electrical conductivity to the polymer fabrics. It was found that the pre-coating activation improved durability of the coating and stability of the electrical properties due to better bonding between the conducting coating and the fiber surfaces.

Electrical conductivity was imparted to a cotton fabric through thermal reduction of graphene oxide. The reduction was enhanced by commercial antioxidants used in the plastics industry. The cotton fabric was coated with GO by the padding method and dipped in antioxidant solution. After drying, the antioxidant assisted reduction of GO was conducted at 220 °C in air. The electrical properties and hydrophobicity of thus-modified fabric were examined. The structure of materials was analyzed by atomic force microscopy and scanning electron microscopy. Application of the antioxidants permitted to reach lower values of surface electrical resistivity of the fabric. After the reduction all fabric samples became hydrophobic.

Ternary blends of polylactide (PLA, 90 wt.%) and poly(methyl methacrylate) (PMMA, 10 wt.%) with functionalized polysilsesquioxanes (LPSQ-R) were obtained by solution blending. R groups in LPSQ containing hydroxyethyl (LPSQ-OH), methylglycolic (LPSQ-COOMe) and pentafluorophenyl (LPSQ-F5) moieties of different chemical properties were designed to modify PLA blends with PMMA. The effect of the type of LPSQ-R and their content, 1–3 wt.%, on the structure of the blends was studied with scanning electron microscopy (SEM) combined with energy dispersive spectroscopy (SEM-EDS), dynamic mechanical thermal analysis (DMTA) and Raman spectroscopy. Differential scanning calorimetry (DSC) and tensile tests also showed various effects of LPSQ-R on the thermal and mechanical properties of the blends. Depth-sensing indentation was used to resolve spatially the micro- and nano-scale mechanical properties (hardness and elastic behaviour) of the blends. The results showed clearly that LPSQ-R modulate the structure and properties of the blends.

Electrospun nonwovens of poly(L-lactide) (PLLA) modified with multiwall carbon nanotubes (MWCNT) and linear ladder-like poly(silsesquioxane) with methoxycarbonyl side groups (LPSQ-COOMe) were obtained. MWCNT and LPSQ-COOMe were added to the polymer solution before the electrospinning. In addition, nonwovens of PLLA grafted to modified MWCNT were electrospun. All modified nonwovens exhibited higher tensile strength than the neat PLA nonwoven. The addition of 10 wt.% of LPSQ-COOMe and 0.1 wt.% of MWCNT to PLLA increased the tensile strength of the nonwovens 2.4 times, improving also the elongation at the maximum stress.

Microbial infections lead to elevated inflammatory responses, which usually result in prolonged and incomplete wound healing. Therefore, there is an increasing demand for biodegradable fibres that are effective against a different range of microorganisms, especially those with antibiotic resistance. Herein, quercetin-(Q)-loaded polylactide-based fibres were developed using the electrospinning technique. Since Q exhibits low chemical stability, we used star-shaped polylactides (PLAs) with a β-CD core to host Q by inclusion complexation. To enhance the stability of the fibres and additionally entrap the Q between polymeric chains, we adapted supramolecular cross-linking by the stereocomplexation of PLAs with opposite configurations. As a control, we prepared an additional formulation of star-shaped/commercial PLA/Q for the preparation of nonwovens in which the β-CD moiety was not present. All developed fibres were smooth and continuous, with an average diameter of 37 μm. Although nonwovens did not possess diffusible activity, good antibacterial effects against Staphylococcus aureus (S. aureus), Escherichia coli (E.coli) and Klebsiella pneumoniae (K. pneumoniae) were observed. All these features validate the proposed approach, in which different supramolecular interactions were used to modify the properties of PLA-based fibres and, most importantly, show their great potential usefulness against microbial infections.

Pentaerythritol tetrakis(3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate), an antioxidant widely applied in the plastic industry, was used to assist thermal reduction of graphene oxide (GO) on a cotton fabric in air. l-ascorbic acid was also applied for comparison. GO was deposited on the fabric by the padding method. Reduction of GO deposited on fiber surfaces at 180 and 220 °C in air imparted electrical conductivity. For all the materials the conductivity worsened after the reduction during cooling and during the first hours of storage at room conditions. However, the most stable effect of GO reduction was achieved using pentaerythritol tetrakis(3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate), which assisted the reduction of GO at both 180 and 220 °C, and allowed to obtain the cotton fabric with a stable surface resistivity of 6.6 and 3.7 MΩ/sq, respectively. Moreover, superhydrophobicity of the conductive fabric was achieved by modification with methyltrichlorosilane in an anhydrous environment.

Nonwovens of commercially available polylactide (PLA) were produced by electrospinning using laboratory scale equipment. The nonwovens were subsequently coated with an aqueous dispersion of multiwall carbon nanotubes (MWCNT), using the padding technique. MWCNT formed 3D networks on fiber surfaces making the nonwovens electrically conducting, with surface electrical resistivity of 77 Ω/sq – 680 Ω/sq. Modification of the nonwovens with methyltrichlorosilane made them superhydrophobic, what was reflected in the water contact angles of 160 − 175°. In turn, electrochemical deposition of silver particles (Ag°) on the conductive nonwovens imparted antibacterial activity against Staphylococcus aureus (gram-positive) and Escherichia coli (gram-negative).

Electrical conductivity and hydrophobicity was imparted to a cotton fabric through a sol-gel method by coating with an organosilicon sol containing dispersed graphene oxide (GO). The coating was followed by thermal treatment causing GO reduction and completion of cross-linking reactions. To enhance the reduction, a reductive sol was synthesized from alkoxysilanes with active groups obtained in the hydrolysis and condensation reactions. A siloxane oligomer with covalently bonded –SiH groups was used as a reducing component. The reductive sol was analyzed by means of 1H and 29Si NMR spectroscopy and ATR FTIR. Surface electrical resistivity and hydrophobicity/philicity of the modified fabric were determined, whereas the fiber surfaces were analyzed by SEM. The resistivity of 2.7 MΩ/sq and water contact angle of approx. 150° was reached. Electrical resistance of the coated fabric was sensitive to strain but returned to its initial value after the strain release. Moreover, neither the electrical conductivity nor hydrophobicity worsened after intense sonication, unlike in the case of reference fabric sample prepared by coating with GO alone and GO thermal reduction.