Search

Amorphous transparent SiCx:H and SiCxNy:H films are prepared at a temperature of 200 °C and a discharge power of 200 W in an inductively coupled RF plasma reactor using hexamethyldisilane vapors and additional argon and/or nitrogen gases. The influence of N2 flow rate on the morphology, chemical structure, elemental composition, transmittance, refractive index, contact angle, and film deposition rate is studied. Plasma components are determined by optical emission spectroscopy. It is shown by HRTEM and EDS mapping methods that the annealed Cu/SiCx:H/Si(100) sample has distinct substrate/film and film/copper layer interfaces, no Cu diffusion occurs, and that the SiCx:H the film can be considered as a promising diffusion barrier layer. Stability of the films during storage under ambient conditions is studied. The tendency of SiCxNy:H films to oxidize is revealed by EDS, IR spectroscopy, and XPS. [ABSTRACT FROM AUTHOR]

Nowadays, Pt-Os binary systems are mainly considered as catalysts and electrocatalysts, but the role of Os in these processes is still poorly understood. The electronic structure of Pt-Os nanosystems remains a few studied as well. Using bimetallic (NH4)2[Pt0.5Os0.5Cl6] as a single-source precursor for preparing Pt-Os nanoalloy through the thermal decomposition in hydrogen and inert atmospheres, the relation of morphology, atomic ordering, and electronic structure of Pt-Os nanoalloy was examined by in situ Quick XAFS, XPS, PXRD, SEM, and HRTEM techniques. Being the only variable parameter, the decomposition atmosphere was found to govern the morphology of the Pt-Os nanoalloy and change the atomic ordering (alloying extent), which involves a change in the electronic structure. In a hydrogen atmosphere, the nanofibers (NFs) (ø ~ 5–6 nm) with the atomic ordering Oscore&Pt-richshell were observed to form; in a nitrogen atmosphere, thin nanoplates (NPLs) (~ 12 nm) with the atomic architecture Os-richcore&Pt-richshell were found out. The depletion in the Os 5d5/2 and Pt 5d5/2,3/2 states was revealed for Pt-Os nanoalloys. This unusual result disagrees with the known d-band theory and indicates that there is a gain of non-d conduction electron counts at one or both sites. Mixed conductivity may exist in such Pt-Os nanoalloy that may be responsible for a manifestation of new physical properties of this binary system. [ABSTRACT FROM AUTHOR]

MOCVD processes for the fabrication of PtxIr(1–x) films (x < 0.3, thickness 1.5-1.8 µm) on the contacts of diagnostic electrodes and titanium discs are developed using a combination of Pt(II) and Ir(I) acetylacetonate (acac) derivatives (Pt(acac)2, Ir(cod)(acac) (cod = cyclooctadiene-1,5) and oxygen as a gas reagent. It is shown that the ratios of metals in the films prepared on different types of supports are similar within the same experiment. The films contain phases of solid solution PtxIr(1–x) without admixtures of metallic and oxide phases; the ratio of metals in the sample volume corresponds to the one experimentally specified. EDS and XPS methods determine a lower iridium content after the formation of PtxIr(1–x) films in the subsurface layers (10 nm) than the XRD method. The surface of PtxIr(1–x) films consists of agglomerates formed by small particles. When the Pt content decreases from x = 0.3 to x = 0.2, the average size of these particles decreases from 29 nm to 24–25 nm and then remains virtually constant. The capacitance values of contacts with PtxIr(1–x) films vary within 62.6-84.5 mC/cm2. [ABSTRACT FROM AUTHOR]

Nowadays, Pt-Os binary systems are mainly considered as catalysts and electrocatalysts, but the role of Os in these processes is still poorly understood. The electronic structure of Pt-Os nanosystems remains a few studied as well. Using bimetallic (NH4)2[Pt0.5Os0.5Cl6] as a single-source precursor for preparing Pt-Os nanoalloy through the thermal decomposition in hydrogen and inert atmospheres, the relation of morphology, atomic ordering, and electronic structure of Pt-Os nanoalloy was examined by in situ Quick XAFS, XPS, PXRD, SEM, and HRTEM techniques. Being the only variable parameter, the decomposition atmosphere was found to govern the morphology of the Pt-Os nanoalloy and change the atomic ordering (alloying extent), which involves a change in the electronic structure. In a hydrogen atmosphere, the nanofibers (NFs) (ø ~ 5–6 nm) with the atomic ordering Oscore&Pt-richshell were observed to form; in a nitrogen atmosphere, thin nanoplates (NPLs) (~ 12 nm) with the atomic architecture Os-richcore&Pt-richshell were found out. The depletion in the Os 5d5/2 and Pt 5d5/2,3/2 states was revealed for Pt-Os nanoalloys. This unusual result disagrees with the known d-band theory and indicates that there is a gain of non-d conduction electron counts at one or both sites. Mixed conductivity may exist in such Pt-Os nanoalloy that may be responsible for a manifestation of new physical properties of this binary system. [ABSTRACT FROM AUTHOR]

Nowadays, Pt-Os binary systems are mainly considered as catalysts and electrocatalysts, but the role of Os in these processes is still poorly understood. The electronic structure of Pt-Os nanosystems remains a few studied as well. Using bimetallic (NH4)2[Pt0.5Os0.5Cl6] as a single-source precursor for preparing Pt-Os nanoalloy through the thermal decomposition in hydrogen and inert atmospheres, the relation of morphology, atomic ordering, and electronic structure of Pt-Os nanoalloy was examined by in situ Quick XAFS, XPS, PXRD, SEM, and HRTEM techniques. Being the only variable parameter, the decomposition atmosphere was found to govern the morphology of the Pt-Os nanoalloy and change the atomic ordering (alloying extent), which involves a change in the electronic structure. In a hydrogen atmosphere, the nanofibers (NFs) (ø ~ 5–6 nm) with the atomic ordering Oscore&Pt-richshell were observed to form; in a nitrogen atmosphere, thin nanoplates (NPLs) (~ 12 nm) with the atomic architecture Os-richcore&Pt-richshell were found out. The depletion in the Os 5d5/2 and Pt 5d5/2,3/2 states was revealed for Pt-Os nanoalloys. This unusual result disagrees with the known d-band theory and indicates that there is a gain of non-d conduction electron counts at one or both sites. Mixed conductivity may exist in such Pt-Os nanoalloy that may be responsible for a manifestation of new physical properties of this binary system. [ABSTRACT FROM AUTHOR]

Nowadays, Pt-Os binary systems are mainly considered as catalysts and electrocatalysts, but the role of Os in these processes is still poorly understood. The electronic structure of Pt-Os nanosystems remains a few studied as well. Using bimetallic (NH4)2[Pt0.5Os0.5Cl6] as a single-source precursor for preparing Pt-Os nanoalloy through the thermal decomposition in hydrogen and inert atmospheres, the relation of morphology, atomic ordering, and electronic structure of Pt-Os nanoalloy was examined by in situ Quick XAFS, XPS, PXRD, SEM, and HRTEM techniques. Being the only variable parameter, the decomposition atmosphere was found to govern the morphology of the Pt-Os nanoalloy and change the atomic ordering (alloying extent), which involves a change in the electronic structure. In a hydrogen atmosphere, the nanofibers (NFs) (ø ~ 5–6 nm) with the atomic ordering Oscore&Pt-richshell were observed to form; in a nitrogen atmosphere, thin nanoplates (NPLs) (~ 12 nm) with the atomic architecture Os-richcore&Pt-richshell were found out. The depletion in the Os 5d5/2 and Pt 5d5/2,3/2 states was revealed for Pt-Os nanoalloys. This unusual result disagrees with the known d-band theory and indicates that there is a gain of non-d conduction electron counts at one or both sites. Mixed conductivity may exist in such Pt-Os nanoalloy that may be responsible for a manifestation of new physical properties of this binary system. [ABSTRACT FROM AUTHOR]