Search

The objective of this research was to evaluate the best type and adequate content of adhesive in low density particleboards produced with corn cob, in addition to the chemical analysis of the particles. The adhesives used were urea-formaldehyde (UF) and phenol-formaldehyde (PF) distributed in three levels (6, 9 and 12%) on the dry mass of the particles and the nominal density was 0.60 g.cm-3. Regarding the water absorption and swelling properties, no significant differences were found between treatments. The mean value calculated for the IE 24 h was 37.07%, being above the minimum limit stipulated by the standard. The modulus of rupture (MOR) and modulus of elasticity (MOE), were influenced by the tested factors. All particleboards met the requirements of the standard norm. For internal adhesion there was a significant effect only for the type of adhesive factor, with the particleboards produced with PF showing the highest means. For the compression property there was no effect of the factors tested. In general, the dimensional stability of the particleboards was below the minimum required by the standard, but the mechanical properties met all requirements. El objetivo de esta investigación fue evaluar el mejor tipo y contenido adecuado de adhesivo en tableros de particulas de baja densidad producidos con mazorca de maíz, además del análisis químico de las partículas. Los adhesivos utilizados fueron urea-formaldehído (UF) y fenol-formaldehído (FF) distribuidos en tres niveles (6, 9 y 12%) sobre la masa seca de las partículas y la densidad nominal fue de 0,60 g.cm-3. En cuanto a las propiedades de absorción e hinchamiento de agua, no se encontraron diferencias significativas entre tratamientos. El valor medio calculado para IE 24 h fue del 37,07%, por encima del límite mínimo estipulado por la norma. El módulo de ruptura (MOR) y el módulo de elasticidad (MOE) fueron influenciados por los factores probados. Todos los paneles de aglomerado cumplieron los requisitos de la norma estándar. Para la adherencia interna hubo un efecto significativo solo por el tipo de factor adhesivo, y los paneles producidos con FF mostraron los promedios más altos. Para la propiedad de compresión no hubo efecto de los factores probados. En general, la estabilidad dimensional de los paneles estuvo por debajo del mínimo requerido por la norma, pero las propiedades mecánicas cumplieron con todos los requisitos. O objetivo desta pesquisa foi avaliar o melhor tipo e teor adequado de adesivo em painéis aglomerados de baixa densidade produzidos com sabugo de milho, além da análise química das partículas. Os adesivos utilizados foram uréia-formaldeído (UF) e fenol-formaldeído (FF) distribuídos em três teores (6, 9 e 12%) sobre a massa seca das partículas e a densidade nominal foi 0,60 g.cm-3. Em relação às propriedades de absorção de água e inchamento, não foram constatadas diferenças significativas entre os tratamentos. O valor médio calculado para o IE 24 h foi 37,07%, acima do limite mínimo estipulado pela norma. O módulo de ruptura (MOR) e o módulo de elasticidade (MOE), foram influenciados pelos fatores testados. Todos os painéis aglomerados atenderam aos requisitos da norma padrão. Para a adesão interna houve efeito significativo apenas para o fator tipo de adesivo, sendo que os painéis produzidos com FF evidenciaram as maiores médias. Para a propriedade de compressão não houve efeito dos fatores testados. De forma geral, a estabilidade dimensional dos painéis ficou abaixo do mínimo requerido pela norma, mas as propriedades mecânicas atenderam a todos os requisitos.

Este trabalho teve como objetivo produzir e caracterizar compositos a base de gesso reforcados com particulas de residuo de cacau como forma de agregar valor a esse subproduto agricola e criar um material inovador. Para a producao dos compositos foram utilizados gesso fino para fundicao e particulas de residuo de cacau. As proporcoes de reforco inseridas foram de 0,0%; 2,5%; 5,0%; 7,5% e 10,0% em substituicao a massa de gesso. Para a producao dos compositos foram utilizadas formas de madeira com dimensoes de 40 x 40 x 160 mm. Foi realizada analise da composicao quimica do residuo de cacau para determinacao dos teores de extrativos totais, cinzas, lignina e holocelulose. Os compositos foram avaliados nos ensaios fisicos, mecânicos, termico e acustico. Constatou-se que, houve melhorias nas propriedades fisicas com o acrescimo de reforco tornando o material mais leve, visto a reducao da densidade (1190,69 a 1138,92 kg/m³), e proporcionando a diminuicao da higroscopicidade, com teores de umidade decrescendo de 7,74 a 4,01% e de absorcao de agua decrescendo de 18,37 para 5,28%. Da mesma forma, a resistencia termica aumentou gradativamente ao longo dos tratamentos com valores de 1,90 a 2,41 K.m/W e o isolamento acustico foi maior nos compositos em comparacao com o gesso puro, embora nao tenha havido linearidade entre os tratamentos. Ja para as propriedades mecânicas, houve diminuicao de resistencias tanto a flexao (3,60 a 0,84 MPa) quanto a compressao (4,43 a 1,73 MPa). Foi concluido que o residuo de cacau apresenta potencialidade para ser utilizado no composito tendo em vista que a inclusao de ate 8,15% do mesmo atendeu a normatizacao em todos os ensaios realizados. Isso fomenta a ideia de que os residuos lignocelulosicos sao alternativas promissoras para criacao de materiais de alto valor agregado. Palavras-chave: Residuo lignocelulosico, absorcao de agua, resistencia termica, materiais compositos.

This research proposed to investigate a possible destination for the cocoa waste as component in the core layer of Medium Density Particleboards (MDPs) and to evaluate the effect of the waste insertion on the physical-mechanical properties of the panel. The core layers of the MDPs were composed by different percentages of cocoa wastes (0, 25, 50, 75 and 100%) in combination with pine wood. The targeted density of the panels was pre-established in 0.7 g cm−3, bonded with urea-formaldehyde. The cocoa waste showed higher extractives content (34.8%) when compared with the pine wood (4.0%). The inclusion of the waste did not cause a significant difference in the moisture and bulk density of the panels; however, there was an increase in water absorption 24 h (71–105%) and thickness swelling 24 h (13–35%). Despite the values of the mechanical properties decreased in general, in low percentages, the cocoa waste does not prevent the use of the MDPs as furniture for internal environments. The results show that the cocoa waste has potential for being applied as raw material in the core layer of the MDP, in percentages up to 21%. The lignocellulosic wastes are promising alternatives for the achievement of the required current context of the sustainability and should be highlighted with research focused on their management for the development of added value materials.

RESUMO As embalagens multicamadas são utilizadas por um período de tempo bastante curto gerando um volume de descarte elevado. Por serem formadas por diferentes materiais devido suas diversas camadas, sua reciclagem é dificultada. Sendo assim, são importantes novas aplicações para essas embalagens pós-consumo, como por exemplo o seu reaproveitamento em compósitos. Neste contexto, o objetivo deste trabalho foi desenvolver e caracterizar compósitos à base de gesso reforçados com embalagens multicamadas trituradas. As proporções utilizadas para a incorporação dos reforços foram de 0%, 7,5%, 15%, 22,5% e 30% em substituição ao gesso. Foram produzidos corpos de prova (três repetições por tratamento) para avaliação das propriedades de absorção de água, umidade, massa específica aparente, compressão e flexão estática, os quais foram confeccionados com dimensões de 40 x 40 x 160 mm. Para o ensaio térmico, as dimensões foram de 200 x 200 x 20 mm. Os reforços adicionados levaram a um aumento em umidade e absorção de água, enquanto que, para massa específica aparente, condutividade térmica, resistência à flexão, resistência à compressão e rigidez na compressão houve decréscimo. A incorporação de embalagens multicamadas em compósitos de gesso mostrou ser uma alternativa viável, visto que, além de aplicar a logística reversa reutilizando estas embalagens que muitas vezes são descartadas no meio ambiente de maneira inadequada, gerando diversos impactos, ainda melhorou a propriedade térmica dos compósitos e diminuiu a densidade destes. Ademais, todas as porcentagens atenderam a normatização para resistência à flexão, e para a resistência à compressão, apenas a substituição de 30% não atendeu a normativa. ABSTRACT The multilayer packages are used for a very short time generating a high discard volume. Because they are formed by different materials due to their several layers, their recycling is difficult. Therefore, new applications for these post-consumer packages are important, such as their reuse in composites. In this context, the objective of this work was to develop and characterize plaster based composites reinforced with crushed multilayer packages. The proportions used to incorporate reinforcements were 0%, 7.5%, 15%, 22.5% and 30%, replacing gypsum. Test specimens (three replicates per treatment) were produced to evaluate the properties of water absorption, moisture, apparent specific mass, compression and static bending, which were made with dimensions of 40 x 40 x 160 mm. For the thermal test, the dimensions were 200 x 200 x 20 mm. The added reinforcements led to an increase in moisture and water absorption, whereas, for apparent specific mass, flexural strength, compressive strength and stiffness in compression there was decrease. The incorporation of multilayer packages into plaster composites proved to be a viable alternative, since in addition to applying reverse logistics reusing these packages that are often discarded in the environment in an inadequate manner, generating several impacts, it also improved the thermal properties of the composites , their density decreased, all percentages complied with normalization for flexural strength, and for compression strength, only the 30% insertion did not meet the standards.