Search

This study investigated the impact of temperature, time, and homogenisation on the transient liquid phase bonding of Inconel 617 to stainless steel 310, employing AWS BNI2 foil as an interlayer. Nine test series were conducted at temperatures of 1050 °C and 1100 °C, with bonding durations ranging from 10 to 60 min. The homogenisation process was carried out on specimens that underwent full isothermal solidification at a temperature of 1170 °C for 180 min. The microscopic analysis indicated that extending the time and raising the bonding temperature resulted in the extension of the isothermal solidified zone, accompanied by a reduction in the quantity of eutectic phases. Complete isothermal solidification was seen exclusively in samples bonded at temperatures of 1050 °C for 60 min and 1100 °C for a duration of 50 min. The size of the diffusion-affected zone expanded as the bonding temperature and duration rose, but the presence of brittle intermetallic phases diminished. The microstructure of the homogenised sample indicated that the diffusion-affected zone had been almost completely eliminated. Hardness variations indicated heightened hardness in the diffusion-affected zone (DAZ) and athermal solidified zone (ASZ). Shear strength is maximised in homogenised specimens with minimised ASZ. [ABSTRACT FROM AUTHOR]

Friction stir processing (FSP) offers a unique opportunity to tailor the microstructure and improve the mechanical properties due to the combination of extensive strains, high temperatures, and high-strain rates inherent to the process. Reactive friction stir processing was carried out in order to produce in situ Al/(Al13Fe4 + Al2O3) hybrid nanocomposites on wrought/as-annealed (673 K) AA1050 substrate. The active mixture of pre-ball milled Fe2O3 + Al powder was introduced into the stir zone by pre-placing it on the substrate. Microstructural characterisation showed that the Al13Fe4 and Al2O3 formed as the reaction products in a matrix of the dynamically restored aluminium matrix. The aluminium matrix means grain size was found to decrease markedly to 3.4 and 2 μm from ~55 μm and 40–50 μm after FSP using wrought and as-annealed substrates employing electron backscattered diffraction detectors, respectively. In addition, tensile testing results were indicative that the fabricated surface nanocomposite on the as-annealed substrate offered a greater ultimate tensile strength (~160 MPa) and hardness (73 HV) than those (146 MPa, and 60 HV) of the nanocomposite formed on the wrought substrate. [ABSTRACT FROM AUTHOR]

Epoxy is widely used material, but epoxy has limitations in terms of brittleness in failure, and thus researchers explore toughening and strengthening options such as adding a second phase or using electromagnetic fields to tailor toughness and strength, on demand and nearly instantaneously. Such approach falls into the category of active toughening but has not been extensively investigated. In this research, Si-BaTiO3 nanoparticles were used to modify the electro-mechanical properties of a high-performance aerospace-grade epoxy so as to study its response to electric fields, specifically low field strengths. To promote uniform dispersion and distribution, the Si-BaTiO3 nanoparticles were functionalised with silane coupling agents and mixed in the epoxy Araldite LY1564 at different content loads (1, 5, 10 wt%), which was then associated with its curing agent Aradur 3487. Real-time measurements were conducted using Raman spectroscopy while applying electric fields to the nanocomposite specimens. The Raman data showed a consistent trend of increasing intensity and peak broadening under the increasing electric field strength and Si-BaTiO3 contents. This was attributed to the BaTiO3 particles' dipolar displacement in the high-content nanocomposites (i.e., 5 wt% and 10 wt%). The study offers valuable insights on how electric field stimulation can actively enhance the mechanical properties in epoxy composites, specifically in relatively low fields and thin, high-aspect-ratio composite layers which would require in-situ mechanical testing equipped with electric field application, an ongoing investigation of the current research. [ABSTRACT FROM AUTHOR]

Reactive friction stir processing was used to fabricate in situ hybrid nano-composite. Nano-sized Al2O3 and Al13Fe4 products were formed in the stir zone of rolled AA1050 through the addition of pre-milled Al + Fe3O4 powder mixture. The thermomechanical phenomena associated with the process and addition of active powder mixture provided the occurrence of the aluminothermy reaction. Microstructural investigations showed significant matrix grain refinement; the mean grain size of ~ 3 μm was achieved. The nano-sized reinforcement products prevented grain growth after dynamic recrystallization process by pinning the grain boundaries. The excellent matrix grain refining and formation of in situ hard reinforcements led to the increase of hardness and tensile strength to ~ 56% and 49% over those of the untreated substrate, respectively. [ABSTRACT FROM AUTHOR]