Search

Item does not contain fulltext, Calcium phosphate cements (CPCs) and fibrin glue (FG) are used for surgical applications. Their combination is promising to create bone substitutes able to promote cell attachment and bone remodeling. This study proposes a novel approach to create CPC-FG composites by simultaneous CPC setting and FG fibrinogenesis. CPC-FG composites were obtained by mixing CPC powders, i.e. alpha-tricalcium phosphate, dicalcium phosphate anhydrous and precipitated hydroxyapatite, with FG powder components, i.e. fibrinogen and thrombin, and a 2% Na(2) HPO(4) solution. To study the effect of FG quantity and fibrinogenesis kinetics, long and fast setting FGs were evaluated in amounts of 0.125, 0.250, and 0.500 mL on CPC-FG composites. Physicochemical, interconnectivity, and mechanical properties were measured. Scanning electron microscopy, Micro-computed tomography (mu-CT), X-ray diffraction, and Fourier transform Infrared spectroscopy (FTIR) analyzed morphology, structure, crystallographic, and chemical composition, respectively. FG fibrinogenesis was performed within the CPC. FTIR confirmed this and its interfacial bonding with CPC. mu-CT confirmed a good FG distribution. FG addition affected the CPC when compared with pristine CPC. Adding FG to CPC changed their morphology, density, porosity, setting, cohesion, injectability, interconnectivity, crystallographic and chemical composition and mechanical properties. Moreover, 0.500 mL of long setting FG modified the observed fracture behavior of the CPC-FG.

1 januari 2012, Item does not contain fulltext, Porosity and interconnectivity are important properties of calcium phosphate cements (CPCs) and bone-replacement materials. Porosity of CPCs can be achieved by adding polymeric biodegradable pore-generating particles (porogens), which can add porosity to the CPC and can also be used as a drug-delivery system. Porosity affects the mechanical properties of CPCs, and hence is of relevance for clinical application of these cements. The current study focused on the effect of combinations of polymeric mesoporous porogens on the properties of a CPC, such as specific surface area, porosity and interconnectivity and the development of mechanical properties. CPC powder was mixed with different amounts of PLGA porogens of various molecular weights and porogen sizes. The major factors affecting the properties of the CPC were related to the amount of porogen loaded and the porogen size; the molecular weight did not show a significant effect per se. A minimal porogen size of 40 mum in 30 wt.% seems to produce a CPC with mechanical properties, porosity and interconnectivity suitable for clinical applications. The properties studied here, and induced by the porogen and CPC, can be used as a guide to evoke a specific host-response to maintain CPC integrity and to generate an explicit bone ingrowth.

1 september 2012, Item does not contain fulltext, Calcium phosphate cements (CPCs) use the simultaneous presence of several calcium phosphates phases. This is done to generate specific bulk and in vivo properties. This work has processed and evaluated novel multiphasic CPCs containing dual tricalcium phosphate (TCPs) phases. Dual TCPs containing alpha- and beta-TCP phases were obtained by thermal treatment. Standard CPC (S-CPC) was composed of alpha-TCP, anhydrous dicalcium phosphate and precipitated hydroxyapatite, while modified CPC (DT-CPC) included both alpha- and beta-TCP. Physicochemical characterization of these CPCs was based on scanning electron microscopy, X-ray diffraction, specific surface area (SSA) and particle size (PS) analysis and mechanical properties. This characterization allowed the selection of one DT-CPC for setting time, cohesion and biological assessment compared with S-CPC. Biological assessment was carried out using a tibial intramedullary cavity model and subcutaneous pouches in guinea pigs. Differences in the surface morphology and crystalline phases of the treated TCPs were detected, although PS analysis of the milled CPC powders produced similar results. SSA analysis was significantly higher for DT-CPC with alpha-TCP treated at 1100 degrees C for 5h. Poorer mechanical properties were found for DT-CPC with alpha-TCP treated at 1000 degrees C. Setting time and cohesion, as well as the in vivo performance, were similar in the selected DT-CPC and the S-CPC. Both CPCs created the desired host reactions in vivo.

01 mei 2012, Item does not contain fulltext, Quantification of the amount of newly formed bone is an essential part of bone regeneration studies. Histomorphometry, based on histological sections of plastic-embedded specimens, is the most frequently applied technique in this assessment. Before performing image analysis, a specific region of interest (ROI) has to be determined. Based on the histological procedure, different areas within the ROI can be discriminated and assigned to relevant tissue structures. However, in literature not much attention is paid to the effect of the histological procedures on the final outcome of the histomorphometrical measurements on bone regeneration. In this study, the histomorphometrical bone formation of the intramedullary cavity of the guinea pig tibia, filled with calcium phosphate cement, was quantified in plastic-embedded and paraffin-embedded specimens and in specimens analyzed with scanning electron microscopy in the backscattering mode (SEM-BS). The data showed that the histological procedure significantly affected the measured bone amount. Therefore, it is recommended that scaffold characteristics are carefully considered in selecting a proper technique for the analysis of bone formation in bone tissue engineering studies. The results of this study identified high-resolution SEM-BS and elastic van Gieson staining of decalcified histological sections as recommendable techniques for evaluating bone formation.

Item does not contain fulltext, Bone metastases are usually treated by surgical removal, fixation and chemotherapeutic treatment. Bone cement is used to fill the resection voids. The aim of this study was to develop a local drug delivery system using a calcium phosphate cement (CPC) as carrier for chemotherapeutic agents. CPC consisted of alpha-tricalcium phosphate, calcium phosphate dibasic and precipitated hydroxyapatite powders and a 2% Na(2)HPO(4) hardening solution. Scanning electron microscopy (SEM) was used to observe CPC morphology. X-ray diffraction (XRD) was used to follow CPC transformation. The loading/release capacity of the CPC was studied by a bovine serum albumin-loading model. Release/retention was measured by high performance liquid chromatography and X-ray photoelectron spectrometry. For chemotherapeutic loading, paclitaxel (PX) was loaded onto the CPC discs by absorption. Viability of osteosarcoma U2OS and metastatic breast cancer MDA-MB-231 cells was measured by an AlamarBlue assay. Results of SEM and XRD showed changes in CPC due to its transformation. The loading model indicated a high retention behavior by the CPC composition. Cell viability tests indicated a PX minimal lethal dose of 90 mug/ml. PX released from CPC remained active to influence cell viability. In conclusion, this study demonstrated that CPC is a feasible delivery vector for chemotherapeutic agents.

Item does not contain fulltext, Calcium phosphate cements (CPCs) are significant alternatives to autologous bone grafting. CPCs can be composed of biphasic or multiphase calcium phosphate (CaP) compounds. A common way to process CPCs is by ball milling. Ball milling can be used for grinding or mechanosynthesis. The aim of this study was to determine the effect of well-defined ball milling grinding parameters, applied via different milling pathways, on the properties of CPCs. Starting CaP compounds used included alpha-tricalcium phosphate, dicalcium phosphate anhydrous and precipitated hydroxyapatite. Scanning electron microscopy showed changes in the powder morphology, which were related to the behavior of the starting CaP materials. Specific surface area (SSA) and particle size (PS) measurements exposed the effect of ball milling on the CaP compounds and CPC powders. X-ray diffraction revealed no effect of ball milling pathways or milling time on the composition of CPCs or the starting materials, but affected their crystallographic properties. No contamination of the milling media or transformation into an amorphous calcium phosphate compound was found. The milling pathways affected setting and cohesion. Fourier transform infrared spectroscopy (FTIR) revealed differences on the CPC v-PO(3) bands according to the interaction, created between the CaP compounds by the milling pathways. FTIR confirmed that the milling pathways changed the crystallographic properties. This study demonstrates that the pathways used for milling grinding modify the PS, SSA, and crystallographic properties of the powders, without affecting their composition. These modifications affected the bulk and reactivity properties of the CPCs by creating different setting and cohesion behaviors.